Resin-coated metal sheet for containers

Patent metadata

Field	Value
Publication number	US-9751283-B2
Application number	US-201214346194-A
Country	US
Kind code	B2
Filing date	Sep 27, 2012
Priority date	Sep 28, 2011
Publication date	Sep 5, 2017
Grant date	Sep 5, 2017

Abstract

The resin-coated metal sheet for containers includes a resin coating layer (A) having a multilayered structure mainly composed of a polyester resin on at least one surface thereof. The resin coating layer (A) includes a resin layer (a 1 ). The resin layer (a 1 ) adheres to the metal sheet, contains (i) a polyester resin, (ii) a phenolic resin, (iii) a metal alkoxide compound and/or a metal chelate compound, (iv) an epoxy resin, and (v) at least one selected from the group consisting of polyamine resins, polyamidoamine resins, and polyamide resins, and is mainly composed of the polyester resin. Preferably, a polyester film (a 2 ) is disposed on the resin layer (a 1 ).

First claim

The invention claimed is:

1. A resin-coated metal sheet for containers, comprising a metal sheet having on at least one surface thereof a resin layer (a 1 ) in contact with and adhering to the metal sheet, wherein resin layer (a 1 ) contains the following components (i) to (v):
(i) a polyester resin constituting at least 50 mass % of layer (a 1 ), wherein the polyester resin has a number-average molecular weight in the range of 3000 to 100000 and is at least one of the following (i-1) to (i-3):
(i-1) a polyester resin having a glass transition temperature of 0° C. or more and less than 35° C.,
(i-2) a polyester resin having a glass transition temperature of 35° C. or more and less than 65° C., and
(i-3) a polyester resin having a glass transition temperature of 65° C. or more and less than 100° C.,

(ii) a phenolic resin,
(iii) a metal alkoxide compound and/or a chelated metal compound,
(iv) an epoxy resin, and
(v) at least one compound selected from the group consisting of polyamines, polyamidoamine resins, and polyamide resins.

2. The resin-coated metal sheet for containers according to claim 1 , wherein the (iv) epoxy resin does not comprise units of bisphenol A.

3. The resin-coated metal sheet for containers according to claim 1 , further comprising a polyester film (a 2 ) disposed on the resin layer (a 1 ).

4. The resin-coated metal sheet for containers according to claim 1 , wherein the resin component ratio of the resin layer (a 1 ) is as follows:
(i) the polyester resin: 50 to 89 mass %,
(ii) the phenolic resin: 10 to 45 mass %,
(iii) the metal alkoxide compound and/or the chelated metal compound: 0.01 to 10 mass %,
(iv) the epoxy resin: 0.5 to 20 mass %, and
(v) the at least one compound selected from the group consisting of polyamines, polyamidoamine resins, and polyamide resins: 0.1 to 10 mass %.

5. The resin-coated metal sheet for containers according to claim 1 , wherein the polyester resin ratio of the (i) polyester resin is as follows:
the polyester resin having a glass transition temperature of 0° C. or more and less than 35° C.: 30 to 70 mass %,
the polyester resin having a glass transition temperature of 35° C. or more and less than 65° C.: 10 to 35 mass %, and
the polyester resin having a glass transition temperature of 65° C. or more and less than 100° C.: 10 to 35 mass %.

6. The resin-coated metal sheet for containers according to claim 1 , wherein the (i) polyester resin is a polyester resin having diphenolic acid repeating units.

7. The resin-coated metal sheet for containers according to claim 1 , wherein the (iii) metal alkoxide compound and/or chelated metal compound is a titanium alkoxide compound and/or a chelated titanium compound.

8. The resin-coated metal sheet for containers according to claim 3 , wherein the polyester film (a 2 ) is a biaxially stretched polyester film in which 85 mass % or more of the constitutional units of the polyester resin is an ethylene terephthalate unit and/or an ethylene naphthalate unit, and the biaxially stretched polyester film contains inorganic particles and/or organic particles.

Assignees

• Jfe Steel Corp

Inventors

• Yamanaka Yoichiro
• Sasaki Koichi
• Nakagawa Yusuke
• Kitagawa Junichi
• Tobiyama Yoichi

Classifications

• C08J7/0427

  with only one layer of a composition containing a polymer binder (with more layers C08J7/042) · CPC title

• C09D161/16

  of ketones with phenols · CPC title

• C09D167/03

  the dicarboxylic acids and dihydroxy compounds having the carboxyl - and the hydroxy groups directly linked to aromatic rings · CPC title

• B32B2270/00

  Resin or rubber layer containing a blend of at least two different polymers · CPC title

• B32B27/36

  comprising polyesters · CPC title