Lifetime extending and performance improvements of optical fibers via loading

Patent metadata

Field	Value
Publication number	US-9746749-B2
Application number	US-200913003510-A
Country	US
Kind code	B2
Filing date	Jul 3, 2009
Priority date	Jul 11, 2008
Publication date	Aug 29, 2017
Grant date	Aug 29, 2017

Abstract

An optical fiber includes a core and a cladding. The optical fiber includes a core material and a cladding material, respectively, wherein the fiber is a non-linear microstructured optical fiber, the microstructured optical fiber being obtainable by a method including loading with hydrogen and/or deuterium and optionally annealing and/or irradiation whereby the lifetime of the fiber may be extended in high power applications.

First claim

The invention claimed is:

1. A microstructured optical fiber, comprising:
a core comprising a core material comprising hydrogen and/or deuterium bound to said core material; and
a cladding comprising a cladding material;
where at least a part of the core being of silica or doped silica and said core having a Germanium content of less than 0.001 at %;
said microstructured optical fiber being a nonlinear fiber in that said microstructured fiber can guide light for at least a range of wavelengths λ min to λ max and for a mode field diameter (MFD) of the fundamental mode over at least a part of said range the fraction (MFD)/λ is less than or equal to 5; and
said optical fiber being obtained by a method comprising loading said core material with hydrogen or deuterium under loading conditions suitable to allow the hydrogen or the deuterium to become bound to said core material,
where the loading temperature T is equal to or more than 120° C. and wherein said fiber has been subjected to an anneal under conditions corresponding to a temperature T anneal of more than 80° C.

2. The fiber of claim 1 , wherein said optical fiber being obtained by a method comprising loading said core material with hydrogen and deuterium under loading conditions suitable to allow the hydrogen and the deuterium to become bound to said core material.

3. The fiber of claim 1 , wherein said optical fiber being obtained by a method comprising loading said core material and said cladding material, with hydrogen or deuterium under loading conditions suitable to allow the hydrogen or the deuterium to become bound to said materials.

4. The fiber of claim 3 , wherein said optical fiber being obtained by a method comprising loading said core material and said cladding material, with hydrogen and deuterium under loading conditions suitable to allow the hydrogen and the deuterium to become bound to said materials.

5. The fiber of claim 1 , wherein said loading conditions comprise an increased pressure and (a) irradiation and/or (b) subsequent irradiation.

6. The fiber of claim 5 , wherein said fiber has been stored at a reduced temperature for a period in the time from production to said subsequent irradiation of the fiber.

7. The fiber of claim 5 , wherein said subsequent irradiation refers to a maximum accumulated time, not counting time wherein said fiber has been stored at reduced temperature, between loading and subsequent irradiation being less than 7 days.

8. The fiber of claim 5 , wherein said subsequent irradiation comprises pumping said fiber with light having a peak power density within said fiber equal to or higher than 100 W/μm 2 .

9. The fiber of claim 5 , wherein said subsequent irradiation comprises pumping said fiber with radiation having an average power of 1 W or more.

10. The fiber of claim 5 , wherein said subsequent irradiation has a duration of more than 12 hours.

11. The fiber of claim 5 , wherein the pressure is more than or equal to 120 bar.

12. The fiber of claim 1 , wherein said anneal is performed for more than 1 hour.

13. The fiber of claim 1 , wherein said anneal is performed in an atmosphere of gases that is essentially free of free radicals.

14. The fiber of claim 1 , wherein said core consists of un-doped silica.

15. The fiber of claim 1 , wherein at least part of said fiber is arranged to strip higher order modes and/or suppress coupling of light from the fundamental mode to higher order modes.

16. The fiber of claim 1 , wherein the core material comprises more than 0.1 atom percent (at %) bound hydrogen and/or deuterium.

17. The fiber of claim 1 , wherein the core material comprises more than 1 atom percent (at %) bound hydrogen and/or deuterium.

18. An optical fiber, comprising:
a core comprising a core material comprising hydrogen and/or deuterium bound to said core material; and
a cladding comprising a cladding material;
where at least a part of the core being of silica or doped silica and said core having a Germanium content of less than 0.001 atom percent (at %); and
where the optical fiber is a microstructured, non-linear optical fiber in that said microstructured fiber can guide light for at least a range of wavelengths λ min to λ max and for a mode field diameter (MFD) of the fundamental mode over at least a part of said range the fraction (MFD)/λ is less than or equal to 5.

19. A supercontinuum light source comprising a fiber according to claim 18 and a pump light source, said fiber being coupled to said pump light source.

20. The supercontinuum light source of claim 19 , wherein at least part of said fiber is coiled with a minimum diameter being less than 20 mm.

21. The supercontinuum light source of claim 20 , wherein said fiber has an input end coupled to said pump source and an output end, wherein said coiling is performed less than 50 cm from the input end.

22. The supercontinuum light source of claim 19 , wherein said optical output comprises a wavelength of less than 500 nm.

23. The supercontinuum light source of claim 19 , wherein said pump light source and the fiber are adapted to provide an optical output spanning over at least one octave with at least 10 μW/nm.

24. A method of producing a microstructured optical fiber comprising a core and a cladding comprising a core material and a cladding material, respectively; where at least a part of the core being of silica or doped silica and wherein said core having a Germanium content of less than 0.001 at %, said method comprising:
loading said core material, and optionally said cladding material, with hydrogen and/or deuterium under loading conditions suitably to allow hydrogen and/or deuterium to become bound to said material(s), where the loading temperature T is equal to or more than 120° C. and subjecting said fiber to an annealing at a temperature T anneal of more than 80° C.,
wherein the fiber is subjected to a subsequent irradiation comprising pumping the fiber with light having peak power density within said fiber equal to or higher than 10 W/μm 2 for a duration of more than 1 hour, wherein a maximum time between loading and irradiation is 7 days excluding time where the fiber has been stored at a reduced temperature of less than −30° C.

Assignees

• Thomsen Carsten L
• Andersen Thomas Vestergaard
• Nkt Photonics As

Inventors

• Thomsen Carsten L
• Andersen Thomas Vestergaard

Classifications

• G02B6/0006

  Coupling light into the fibre (in general G02B6/4298) · CPC title

• G02B6/02342

  characterised by cladding features, i.e. light confining region · CPC title

• G02B6/02333

  Core having higher refractive index than cladding, e.g. solid core, effective index guiding · CPC title

• G02B6/4296

  coupling with sources of high radiant energy, e.g. high power lasers, high temperature light sources · CPC title

• H01S3/302

  in an optical fibre · CPC title