Abstract

The present invention relates to a process for coating paper, wherein the coating material used is a biodegradable, aliphatic-aromatic polyester having a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 3 to 50 cm 3 /10 min.

First claim

We claim:

1. A process comprising:
applying with an extrusion method a coating material to paper to form a coated paper, said coating material comprising an aliphatic-aromatic polyester comprising:
i) from 40 to 70 mol %, based on the total of components i to ii, of a sebacic acid derivative or sebacic acid;
ii) from 60 to 30 mol %, based on the total of components i to ii, of a terephthalic acid derivative;
iii) from 98 to 102 mol %, based on the total of components i ii, of a C 2 -C 8 -alkylenediol or C 2 -C 6 -oxyalkylenediol;
iv) from 0.01 to 2% by weight, based on the total weight of components i to iii, of a chain extender and/or crosslinking agent selected from the group consisting of: a di-functional isocyanate, polyfunctional isocyanate, isocyanurate, oxazoline, epoxide, carboxylic anhydride, an at least trifunctional alcohol, and an at least trifunctional carboxylic acid;
v) from 0 to 50% by weight, based on the total weight of the components i to iv, of an organic filler selected from the group consisting of: native starch, plasticized starch, natural fiber, wood meal, and an inorganic filler, wherein said inorganic filler is selected from the group consisting of: chalk, precipitated calcium carbonate, graphite, gypsum, conductive carbon black, iron oxide, calcium chloride, dolomite, kaolin, silicon dioxide, sodium carbonate, titanium dioxide, silicate, wollastonite, mica, montmorillonite, talc, glass fibers and mineral fibers and
vi) from 0 to 2% by weight, based on the total weight of the components i to iv, of at least one stabilizer, nucleating agent, lubricant and release agent, surfactant, wax, antistatic agent, antifogging agent, dye, pigment, UV absorber, UV stabilizer or other plastics additive;
wherein the aliphatic-aromatic polyester has a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 5 to 25 cm 3 /10 min, and the coating material is a polymer mixture comprising;
from 5 to 95% by weight of the aliphatic-aromatic polyester and,
from 95 to 5% by weight of one or more polymers selected from the group consisting of polylactic acid, polycaprolactone, polyhydroxyalkanoate, chitosan, gluten, polybutylene succinate, polybutylene succinate adipate, polybutylene succinate sebacate, and polybutylene terephthalate-co-adipate,
wherein the polymer mixture has a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 10 to 30 cm 3 /10 min.

2. The process according to claim 1 , wherein the components i) and ii) of the aliphatic-aromatic polyester are as follows:
i) from 52 to 65 mol %, based on the total of components i to ii, of a sebacic acid derivative or sebacic acid;
ii) from 48 to 35 mol %, based on the total of components i to ii, of a terephthalic acid derivative.

3. The process according to claim 1 , wherein the polymer mixture comprises
from 20 to 90% by weight of the aliphatic-aromatic polyester,
from 80 to 10% by weight of polylactic acid, and
from 0 to 2% by weight of an epoxide-containing poly(meth)acrylate.

4. The process according to claim 3 , the polylactic acid having a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 9 to 70 cm 3 /10 min.

5. The process of claim 4 , wherein the coating of the coated paper comprises:
i) an outer layer of the polymer mixture having from 40 to 60% by weight of the aliphatic-aromatic polyester and from 60 to 40% by weight of the polylactic acid and from 0 to 10% by weight of a wax formulation comprising wax, dispersant and antiblocking agents;
ii) optionally a middle layer comprising from 50 to 100% by weight of a polylactic acid and from 0 to 50% by weight of the aliphatic-aromatic polyester; and
iii) an inner layer in contact with the cardboard, comprising from 50 to 100% of the aliphatic-aromatic polyester.

6. The process according to claim 3 , wherein the polylactic acid forms a continuous phase in the polymer mixture.

7. The process according to claim 3 , wherein the coating material comprises 70% to 50% by weight of the polylactic acid.

8. The process according to claim 7 , wherein the coextrusion coating to the paper includes an average grammage of 15 to 30 g/m 2 .

9. The process according to claim 1 , wherein the polymer mixture further comprises from 0.1 to 1% by weight of nucleating agent(s).

10. The process of claim 1 wherein the method of coating is by the coextrusion method.

11. The process of claim 1 wherein the applying the coating is used in the production of paper bags for dry foods, liquids, tube laminates, paper carrier bags, paper laminates and coextrudates, paper adhesive tape, cardboard cups, yoghurt pots, meal trays, wound cardboard containers, wet-strength cartons for outer packagings, fruit boxes of coated cardboard, fast food plates, clamp shells, beverage cartons, cartons for liquids, frozen food cartons, ice packaging, paper labels, flower pots and plant pots.

12. The process of claim 1 wherein said inorganic filler is silicon dioxide.

13. A process comprising:
coating paper with a coating material by coextrusion, the coating material comprising a biodegradable, aliphatic-aromatic polyester comprising:
i) from 40 to 70 mol %, based on the total of components i to ii, of one or more dicarboxylic acids selected from the group consisting of succinic acid, adipic acid, sebacic acid, azelaic acid, brassylic acid, derivative of succinic acid, derivative of adipic acid, derivative of sebacic acid, derivative of azelaic acid, and derivative of brassylic acid;
ii) from 60 to 30 mol %, based on the total of components i to ii, of a terephthalic acid derivative;
iii) from 98 to 102 mol %, based on the total of components i to ii, of a C 2 -C 8 -alkylenediol or C 2 -C 6 -oxyalkylenediol;
iv) from 0.01 to 2% by weight, based on the total weight of components i to iii, of a chain extender and/or crosslinking agent selected from the group consisting of: a di-functional isocyanate, polyfunctional isocyanate, isocyanurate, oxazoline, epoxide, carboxylic anhydride, an at least trifunctional alcohol, and an at least trifunctional carboxylic acid;
wherein the biodegradable, aliphatic-aromatic polyester hats a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 5 to 12 cm 3 /10 min.

14. The process according to claim 13 , wherein the coating material comprises from 5 to 95% by weight of the biodegradable, aliphatic-aromatic polyester, and from 95 to 5% by weight of one or more polymers selected from the group consisting of: polylactic acid, polycaprolactone, polyhydroxyalkanoate, chitosan, gluten, polybutylene succinate, polybutylene succinate adipate, polybutylene succinate sebacate, and polybutylene terephthalate-co-adipate.

15. The process according to claim 14 , wherein the polymer mixture has a melt volume rate (MVR) according to EN ISO 1133 (190° C., 2.16 kg weight) of from 10 to 30 cm 3 /10 min.

16. The process according to claim 13 , wherein the coating material comprises from 20 to 90% by weight of the biodegradable, aliphatic-aromatic polyester, and from 80 to 10% by weight of polylactic acid.

17. A process comprising coating a paper by coextrusion with a coating material, the coating material comprising
20 to 90% by weight of an aliphatic-aromatic polyester that is prepared from:
i) 40 to 70 mol %, based on the total of components i to ii, of one or more dicarboxylic acids selected from the group consisting of succinic acid, adipic acid, sebacic acid, azelaic acid, brassylic acid, derivative of succinic acid, derivative of adipic acid, derivative of s

Assignees

• Skupin Gabriel
• Loos Robert
• Füβl Andreas
• Nevalainen Kimmo
• Basf Se

Inventors

• Skupin Gabriel
• Loos Robert
• Füβl Andreas
• Nevalainen Kimmo

Classifications

• B05D1/265 Primary

  Extrusion coatings · CPC title

• B05D2252/00

  Sheets · CPC title

• C08L67/04

  Polyesters derived from hydroxycarboxylic acids, e.g. lactones (C08L67/06 takes precedence) · CPC title

• C08L2666/02

  Organic macromolecular compounds, natural resins, waxes or and bituminous materials · CPC title

• C08L67/02 Primary

  Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence) · CPC title