Method for manufacturing MgB2 superconductor, and MgB2 superconductor

Patent metadata

Field	Value
Publication number	US-9741472-B2
Application number	US-201415105114-A
Country	US
Kind code	B2
Filing date	Dec 16, 2014
Priority date	Dec 17, 2013
Publication date	Aug 22, 2017
Grant date	Aug 22, 2017

Abstract

Provided are a method for manufacturing MgB 2 superconductor by pressure molding a mixture of Mg powder or MgH 2 powder and B powder and heat-treating the mixture, the method including (I) a step of adding a polycyclic aromatic hydrocarbon to the B powder, while heating the mixture to a temperature higher to or equal to the melting point of the polycyclic aromatic hydrocarbon at the time of this addition, and thereby covering the surface of the B powder with the polycyclic aromatic hydrocarbon; and (II) a step of mixing the B powder having the surface covered with the polycyclic aromatic hydrocarbon, with the Mg powder or the MgH 2 powder, or a step of combining the B powder having the surface covered with the polycyclic aromatic hydrocarbon, with an Mg rod; and an MgB 2 superconducting wire which has high critical current density (Jc) characteristics and less fluctuation in the critical current density (Jc).

First claim

The invention claimed is:

1. A method for manufacturing an MgB 2 superconductor comprising:
(I) adding a polycyclic aromatic hydrocarbon to a B powder, while heating to a temperature higher than or equal to the melting point of the polycyclic aromatic hydrocarbon at the time of this addition, and thereby covering a surface of the B powder with the polycyclic aromatic hydrocarbon;
(IIa) mixing the B powder having the surface covered with the polycyclic aromatic hydrocarbon, with an Mg powder or an MgH 2 powder, and then packing a metal tube with the resulting mixture; or
(IIb) packing a metal tube with the B powder covered with the polycyclic aromatic hydrocarbon and an Mg rod; and
(III) pressure molding and heat-treating the packed metal tube, thereby producing the MgB 2 superconductor.

2. The method for manufacturing an MgB 2 superconductor according to claim 1 , wherein the polycyclic aromatic hydrocarbon is at least one selected from the group consisting of coronene, anthanthrene, benzo(ghi)perylene, circulenes, corannulene, dicoronylene, diindenoperylene, helicene, heptacene, hexacene, kekulene, ovalene, zethrene, benzo[a]pyrene, benzo[e]pyrene, benzo[a]fluoranthene, benzo[b]fluoranthene, benzo[j]fluoranthene, benzo[k]fluoranthene, dibenz[a,h]anthracene, dibenz[a,j]anthracene, olympicene, pentacene, perylene, picene, tetraphenylene, benz[a]anthracene, benzo[a]fluorene, benzo[c]phenanthrene, chrysene, fluoranthene, pyrene, tetracene, triphenylene, anthracene, fluorene, phenalene, and phenanthrene.

3. The method for manufacturing an MgB 2 superconductor according to claim 1 , wherein the polycyclic aromatic hydrocarbon is solid at room temperature and atmospheric pressure and has a melting point that is lower than the decomposition temperature, and a ratio between the number of carbon atoms and the number of hydrogen atoms in the polycyclic aromatic hydrocarbon is such that the ratio C:H is in the range of 1:0.5 to 1:0.8.

4. The method for manufacturing an MgB 2 superconductor according to claim 1 , wherein an amount of addition of the polycyclic aromatic hydrocarbon is in the range of 0.05 mol % to 40 mol % relative to a theoretical amount or an amount of experimental production of MgB 2 .

5. The method for manufacturing an MgB 2 superconductor according to claim 1 , comprising steps (I), (IIa) and (III).

6. The method for manufacturing an MgB 2 superconductor according to claim 1 , comprising steps (I), (IIb) and (III).

Assignees

• Nat Inst For Materials Science

Inventors

• Kumakura Hiroaki
• Matsumoto Akiyoshi
• Ye Shujun

Classifications

• H01B13/0036

  Details · CPC title

• H01B12/06 Primary

  Films or wires on bases or cores · CPC title

• H01B13/0016

  for heat treatment · CPC title

• H01F6/06

  Coils, e.g. winding, insulating, terminating or casing arrangements therefor · CPC title

• H01L39/2487

  Electricity · mapped topic