Polarizer and fabrication method thereof

Patent metadata

Field	Value
Publication number	US-9739919-B2
Application number	US-201615006091-A
Country	US
Kind code	B2
Filing date	Jan 25, 2016
Priority date	Feb 13, 2015
Publication date	Aug 22, 2017
Grant date	Aug 22, 2017

Abstract

The present disclosure provides a polarizer and fabrication method thereof. The polarizer includes a substrate made of transparent material and a first polarizing layer formed on the substrate having an optical alignment direction after being exposed to a polarized ultraviolet light. The substrate is the only substrate in the polarizer, and no additional substrate is configured on the polarizing layer.

First claim

What is claimed is:

1. A polarizer, comprising:
a substrate made of a transparent material; and
a first polarizing layer formed on the substrate having an optical alignment direction and passing light with a polarization direction parallel to a polarization axis of the first polarizing layer after being exposed to a polarized ultraviolet light,
wherein the substrate is the only substrate in the polarizer, and no additional substrate is configured on the polarizing layer.

2. The polarizer of claim 1 , wherein:
the first polarizing layer includes at least a first region and a second region; and
the first region and the second region have different polarization axis directions.

3. The polarizer of claim 1 , wherein:
the first polarizing layer is made of a base material and a polarizing material doped into the base material.

4. The polarizer of claim 3 , wherein:
the polarizing material is a dichroic organic dye.

5. The polarizer of claim 3 , wherein:
the base material is a polyimide, a cinnamic acid derivative, or an azo-based optical alignment material.

6. The polarizer of claim 1 , wherein:
the substrate is a rigid substrate.

7. The polarizer of claim 6 , wherein:
the substrate is made of glass.

8. The polarizer of claim 1 , further including:
a quarter-wavelength thin film formed on the first polarizing layer.

9. The polarizer of claim 8 , wherein:
the quarter-wavelength thin film has a thickness approximately between 28 nm and 100 nm.

10. A polarizer, comprising:
a substrate made of a transparent material;
a first polarizing layer formed on the substrate having an optical alignment direction after being exposed to a polarized ultraviolet light and
a second polarizing layer formed on the first polarizing layer and having a polarization axis direction different from a polarization axis direction of at least one of the first region and the second region,
wherein the substrate is the only substrate in the polarizer, and no additional substrate is configured on the polarizing layer,
the first polarizing layer includes at least a first region and a second region, and
the first region and the second region have different polarization axis directions.

11. The polarizer of claim 10 , wherein:
the second polarizing layer includes at least a third region and a fourth region; and
the third region and the fourth region have different polarization axis directions.

12. A method of fabricating a polarizer, comprising:
providing a substrate;
forming a first polarizing layer on the substrate;
pre-baking the first polarizing layer including at least a first region and a second region;
irradiating a polarized ultraviolet light on the first polarizing layer, wherein the first region and the second region are irradiated by the polarized ultraviolet light with different polarization directions; and
curing the first polarizing layer on the substrate to form the polarizer without adding any additional substrate on the first polarizing layer,
wherein the first polarizing layer formed on the substrate has an optical alignment direction and passes light with a polarization direction parallel to a polarization axis of the first polarizing layer after being irradiated by the polarized ultraviolet light.

13. The polarizer fabrication method of claim 12 , further including:
forming a second polarizing layer on the first polarizing layer having a polarization axis direction different from a polarization axis direction of at least one of the first region and the second region.

14. The polarizer fabrication method of claim 13 , wherein:
the second polarizing layer includes at least a third region and a fourth region; and
the third region and the fourth region have different polarization axis directions.

15. The polarizer fabrication method of claim 12 , wherein:
the first polarizing layer is made of a base material and a polarizing material doped into the base material;
the polarizing material is a dichroic organic dye; and
the base material is a polyimide, a cinnamic acid derivative, or an azo-based optical alignment material.

16. The polarizer fabrication method of claim 12 , wherein:
the substrate is a rigid substrate.

17. The polarizer of claim 16 , wherein:
the substrate is made of glass.

18. The polarizer fabrication method of claim 12 , further including:
forming a quarter-wavelength thin film on the polarizing layer, having a thickness approximately between 28 nm and 100 nm.

19. The polarizer fabrication method of claim 12 , wherein:
the polarized ultraviolet light has an energy level approximately between 300 mj and 1000 mj;
during the pre-baking process, the baking temperature is approximately between 90° C. and 130° C., and the baking time is approximately between 60 seconds and 120 seconds; and
during the curing process, the baking temperature is approximately between 210° C. and 230° C., and the baking time is approximately between 20 minutes and 50 minutes.

Assignees

• Xiamen Tianma Micro Electronics Co Ltd
• Tianma Microelectronics Co Ltd

Inventors

• Zhang Long
• Shen Poping
• Zhou Ting

Classifications

• C03C17/28

  with organic material (C03C17/34, C03C17/44 take precedence) · CPC title

• G02B5/305 Primary

  including organic materials, e.g. polymeric layers · CPC title