Abstract

A method of manufacturing a molded solid fuel including: a pulverization for pulverizing low-grade coal; a mixing for obtaining a slurry by mixing the pulverized low-grade coal and a solvent oil; a dehydration for obtaining a dehydrated slurry by heating and dehydrating the slurry; a solid-liquid separation for obtaining a cake by separating the solvent oil from the dehydrated slurry; a drying for obtaining powdery modified coal by heating the cake and further separating the solvent oil from the cake; and a molding for pressurizing and molding the powdery modified coal by using a molding machine, without the addition/mixture of a binder. In the molding, a coolant is sprayed onto the surface of the molding machine, and the surface temperature of the molding machine is kept equal to or below 100° C.

First claim

The invention claimed is:

1. A method of manufacturing a molded solid fuel, the method comprising:
a pulverization step of pulverizing low-grade coal;
a mixing step of mixing the pulverized low-grade coal and a solvent oil to produce a slurry;
a dehydration step of heating and dehydrating the slurry to produce a dehydrated slurry;
a solid-liquid separation step of separating the solvent oil from the dehydrated slurry to produce a cake;
a drying step of heating the cake to further separate the solvent oil from the cake to produce powdery upgraded coal; and
a molding step of pressure-molding the powdery upgraded coal by a molding machine without adding and/or mixing a binder,
wherein in the molding step, a coolant is sprayed onto a roll surface of the molding machine, to cool the surface to a degree sufficient that a roll surface temperature of the molding machine is maintained at 100° C. or lower,
wherein in the molding step, the molding machine is accommodated in a molding chamber having an opened carry-in part for the powdery upgraded coal produced in the drying step and an opened carry-out part for the molded solid fuel provided from the molding machine, and humidity in the molding chamber is maintained to 85% or more.

2. The method of manufacturing a molded solid fuel according to claim 1 , wherein water is used as the coolant.

3. The method of manufacturing a molded solid fuel according to claim 1 , wherein in the molding step, the coolant spray device is accommodated in the molding chamber, and the coolant is sprayed onto the surface of the molding machine.

4. The method of manufacturing a molded solid fuel according to claim 1 , wherein after the molding step, the molded solid fuel provided from the molding machine and the powdery upgraded coal as a non-molded material are sieved and separated from each other, and the powdery upgraded coal as undersize powder in such sieving is returned to the material supply line.

5. The method of manufacturing a molded solid fuel according to claim 4 , wherein after the molding step, the molded solid fuel provided from the molding machine and the powdery upgraded coal as a non-molded material are sieved and separated from each other, and the powdery upgraded coal as undersize powder in such sieving is returned to the material supply line.

6. A method of manufacturing a molded solid fuel, the method comprising:
a pulverization step of pulverizing low-grade coal;
a mixing step of mixing the pulverized low-grade coal and a solvent oil to produce a slurry;
a dehydration step of heating and dehydrating the slurry to produce a dehydrated slurry;
a solid-liquid separation step of separating the solvent oil from the dehydrated slurry to produce a cake;
a drying step of heating the cake to further separate the solvent oil from the cake to produce powdery upgraded coal; and
a molding step of pressure-molding the powdery upgraded coal by a molding machine without adding and/or mixing a binder,
wherein in the molding step, a coolant is sprayed onto a roll surface of the molding machine, to cool the surface to a degree sufficient that a roll surface temperature of the molding machine is maintained at 90° C. or lower,
wherein in the molding step, the molding machine is accommodated in a molding chamber having an opened carry-in part for the powdery upgraded coal produced in the drying step and an opened carry-out part for the molded solid fuel provided from the molding machine, and humidity in the molding chamber is maintained to 85% or more.

7. A method of manufacturing a molded solid fuel, the method comprising:
a pulverization step of pulverizing low-grade coal;
a mixing step of mixing the pulverized low-grade coal and a solvent oil to produce a slurry;
a dehydration step of heating and dehydrating the slurry to produce a dehydrated slurry;
a solid-liquid separation step of separating the solvent oil from the dehydrated slurry to produce a cake;
a drying step of heating the cake to further separate the solvent oil from the cake to produce powdery upgraded coal at an elevated temperature; and
a molding step of pressure-molding the powdery upgraded coal by a molding machine without adding and/or mixing a binder,
wherein in the molding step, a coolant is sprayed onto a roll surface of the molding machine, to cool the surface to a degree sufficient that a roll surface temperature of the molding machine is maintained at a temperature no greater than the elevated temperature of the powdery upgraded coal,
wherein in the molding step, the molding machine is accommodated in a molding chamber having an opened carry-in part for the powdery upgraded coal produced in the drying step and an opened carry-out part for the molded solid fuel provided from the molding machine, and humidity in the molding chamber is maintained to 85% or more.

8. The method of manufacturing a molded solid fuel according to claim 1 , wherein the humidity in the molding chamber is maintained to 99% or more.

9. The method of manufacturing a molded solid fuel according to claim 6 , wherein the humidity in the molding chamber is maintained to 99% or more.

10. The method of manufacturing a molded solid fuel according to claim 7 , wherein the humidity in the molding chamber is maintained to 99% or more.

Assignees

• Kobe Steel Ltd

Inventors

• Takahashi Yoichi
• Shigehisa Takuo
• Adachi Tsuyoshi

Classifications

• C10L9/00

  Treating solid fuels to improve their combustion · CPC title

• C10L2290/30

  Pressing, compressing or compacting · CPC title

• C10L5/361

  Briquettes · CPC title

• C10L5/04

  Raw material {of mineral origin} to be used; Pretreatment thereof {(pretreatment of fuels of non-mineral origin C10L5/40)} · CPC title

• Y02E50/30

  Fuel from waste, e.g. synthetic alcohol or diesel · CPC title