Multi-core optical fiber, optical cable, and optical connector

Patent metadata

Field	Value
Publication number	US-9726816-B2
Application number	US-201615080878-A
Country	US
Kind code	B2
Filing date	Mar 25, 2016
Priority date	Oct 22, 2014
Publication date	Aug 8, 2017
Grant date	Aug 8, 2017

Abstract

An MCF of the present embodiment has eight or more cores. A diameter of a common cladding is not more than 126 μm. Optical characteristics of each core are as follows: a TL at a predetermined wavelength of 1310 nm is not more than 0.4 dB/km; an MFD at the predetermined wavelength is from 8.0 μm to 10.1 μm; a BL in a BR of not less than 5 mm or in the BR of not less than 3 mm and, less than 5 mm is not more than 0.25 dB/turn at the predetermined wavelength; λ0 is from 1300 nm to 1324 nm; λcc is not more than 1260 nm; an XT or XTs at the predetermined wavelength is not more than 0.001/km.

First claim

The invention claimed is:

1. A multi-core optical fiber comprising:
eight or more core units each having a core, an inner cladding surrounding the core, and a trench surrounding the inner cladding;
a common cladding individually surrounding each of the eight or more core units; and
a resin coating surrounding the common cladding,
wherein each of the cores, each of the inner claddings, each of the trenches, and the common cladding are comprised of silica-based glass,
wherein a diameter of the common cladding is not more than 126 μm,
wherein when relative RI differences of each core, each inner cladding, each trench, the common cladding, and the coating with respect to a predetermined RI are defined as Δ1, Δ2, Δ3, Δ4, and Δ5, respectively, each core, each inner cladding, each trench, the common cladding, and the coating satisfy the following conditions:
Δ5>Δ1>Δ2>Δ3; and

Δ1>Δ4>Δ3,

wherein optical characteristics of each core are as follows:
a transmission loss is not more than 0.5 dB/km or not more than 0.4 dB/km at a wavelength of 1310 nm;
a mode field diameter 1 s from 8.0 μm to 10.1 μm at the wavelength of 1310 nm;
a bending loss in a bending radius of not less than 5 mm or in the bending radius of not less than 3 mm and, less than 5 mm is not more than 0.25 dB/tum at the wavelength of 1310 nm;
a zero dispersion wavelength is from 1300 nm to 1324 nm;
a cable cutoff wavelength is not more than 1260 nm; and
an inter-neighboring-core crosstalk between a concerned core, out of the cores, and a core neighboring to the concerned core or a secondary inter-neighboring-core crosstalk between the concerned core and another core neighboring to the core neighboring to the concerned core is not more than 0.001/km at the wavelength of 1310 am.

2. The multi-core optical fiber according to claim 1 , wherein the diameter of the common cladding is not less than 124 μm.

3. The multi-core optical fiber according to claim 1 , wherein the transmission loss of an outmost core a core center of which is located at a smallest distance from the coating, out of the cores, is larger than 0.5 dB/km at a wavelength of 1550 nm or at a wavelength of 1625 nm, or, the transmission losses of the cores are larger than 0.4 dB/km at the wavelength of 1550 nm or at the wavelength of 1625 nm.

4. The multi-core optical fiber according to claim 1 , wherein the cores are arranged on an identical circumference centered at a center of a cross section of the common cladding.

5. The multi-core optical fiber according to claim 4 , wherein the cores are arranged at equal intervals.

6. The multi-core optical fiber according to claim 1 , wherein when Conditions 0 to 10 are defined as below using 2a as a diameter of each core, 2b as a diameter of each inner cladding, and 2c as a diameter of each trench:
(Condition 0)
5.27 μm≦2 a≦ 8.05 μm

0.375≦ a/b≦ 0.45

0.478≦ b/c≦ 0.816

0.26%≦Δ1−Δ4≦0.42%

−0.05%≦Δ2−Δ4≦0.15%

0.25%≦Δ1−Δ2≦0.385%

Δ3−Δ4≦−0.5%;

(Condition 1)
6.16 μm≦2 a≦ 7.01 μm

0.385≦ a/b≦ 0.473

0.597≦ b/c≦ 0.729

0.266%≦Δ1≦0.409%

−0.034%≦Δ2≦0.071%

−0.566%≦Δ3≦−0.284%

−0.015%≦Δ4≦0.222%;

(Condition 2)
6.73 μm≦2 a≦ 8.08 μm

0.357≦ a/b≦ 0.530

0.687≦ b/c≦ 0.815

0.297%≦Δ1≦0.403%

−0.053%≦Δ2≦0.034%

−0.694%≦Δ3≦−0.271%

−0.017%≦Δ4≦0.196%;

(Condition 3)
6.47 μm≦2 a ≦7.64 μm

0.359≦ a/b≦ 0.435

0.695≦ b/c≦ 0.819

0.264%≦Δ1≦0.409%

−0.067%≦Δ2≦0.060%

−1.020%≦Δ3≦−0.392%

−0.017%≦Δ4;

(Condition 4)
7.14 μm≦2 a≦ 8.10 μm

0.322≦ a/b≦ 0.483

0.744≦ b/c≦ 0.859

0.328%≦Δ1≦0.412%

−0.037%≦Δ2≦0.043%

−1.426%≦Δ3≦−0.495%

−0.022%≦Δ4≦0.161%;

(Condition 5)
6.65 μm≦2 a≦ 7.01 μm

0.385≦ a/b≦ 0.410

0.597≦ b/c≦ 0.729

0.367%≦Δ1≦0.409%

−0.034%≦Δ2≦0.058%

−0.566%≦Δ3≦−0.284%

−0.015%≦Δ4≦0.222%;

(Condition 6)
6.47 μm≦2 a≦ 7.64 μm

0.359≦ a/b≦ 0.435

0.695≦ b/c≦ 0.819

0.349%≦Δ1≦0.409%

−0.067%≦Δ2≦0.054%

−1.020%≦Δ3≦—0.392%

−0.017%≦Δ4;

(Condition 7)
6.16 μm≦2 a≦ 7.01 μm

0.385≦ a/b≦ 0.473

0.597≦ b/c≦ 0.704

0.301%≦Δ1≦0.409%

−0.034%≦Δ2≦0.071%

−0.566%≦Δ3≦−0.317%

−0.015%≦Δ4≦0.132%;

(Condition 8)
6.73 μm≦2 a≦ 8.08 μm

0.357≦ a/b≦ 0.530

0.687≦ b/c≦ 0.796

0.339%≦Δ1≦0.403%

−0.053%≦Δ2≦0.034%

−0.694%≦Δ3≦−0.505%

−0.017%≦Δ4≦0.082%;

(Condition 9)
6.47 μm≦2 a≦ 7.64 μm

0.359≦ a/b≦ 0.435

0.695≦ b/c≦ 0.810

0.314%≦Δ1≦0.409%

−0.067%≦Δ2≦0.060%

−1.020%≦Δ3≦−0.477%

−0.017%≦Δ4≦0.126%;

(Condition 10)
7.14 μm≦2 a≦ 8.10 μm

0.322≦ a/b≦ 0.483

0.744≦ b/c≦ 0.848

0.355%≦Δ1≦0.412%

−0.037%≦Δ2≦0.043%

−1.426%≦Δ3≦−0.601%

−0.022%≦Δ4≦0.035%,

the aforementioned Δ1, Δ2, Δ3, Δ4, a, b, and c satisfy at least any one of the Conditions 0 to 10.

7. The multi-core optical fiber according to claim 1 , wherein as an optical characteristic of a cladding mode propagating in a portion of the common cladding located in a region surrounded by three or more cores out of the cores, the bending loss in the bending radius of 140 mm is not less than 19.3 dB/20 m at a wavelength of 1.26 μm.

8. The multi-core optical fiber according to claim 1 , wherein a portion of the common cladding located in a region surrounded by the eight or more core units comprises a cladding mode suppresser a relative RI difference of which with respect to the predetermined RI is lower than the aforementioned Δ4.

9. The multi-core optical fiber according to claim 8 , wherein the cladding mode suppressor is comprised of a glass having a thermal expansion coefficient different from that of the common cladding excluding the cladding mode suppressor, whereby a stress is applied to each of the cores, and
wherein each of the cores has a birefringence of not less than 10 −4 , or, a polarization crosstalk of not more than −6.9 dB in a fiber length of 30 m to 10 km.

10. The multi-core optical fiber according to claim 1 , which satisfies at least any one of Conditions 11 to 17 as defined below:
(Condition 11)
a neighboring core pitch of the cores is not less than 23.3 μm, and
a shortest distance between a core center of a core located closest to an outer periphery side of the common cladding, out of the cores, and the coating is not less than 17.7 μm;

(Condition 12)
a chromatic dispersion slope at the zero dispersion wavelength is not more than 0.092 ps/(nm 2 ·km);

(Condition 13)
the bending loss in the bending radius of 3 mm is not more than 0.10 dB/turn at the wavelength of 1310 nm;

(Condition 14)
one core of the cores is arranged at a center of the common cladding;

(Condition 15)
the cores have their respective RI profiles which are substantially identical with each other;

(Condition 16)
the cores have their respective RI profiles which are substantially identical with each other, except for the core arranged at the center of the common cladding;

(Condition 17)
the multi-core optical fiber is an all-solid optical fiber.

11. An optical cable including one or more optical fibers each having the same structure as the multi-core optical fiber according to claim 1 .

12. The optical cable according to claim 11 , wherein an average bending radius of the multi-core optical fibers in an unbent state of the optical cable is not more than 1 m, not more than 20 cm, not more than 10 cm, or, not more than 5 cm.

13. An optical connector holding one or more optical fibers each having the same structure as the mul

Assignees

• Sumitomo Electric Industries

Inventors

• Hayashi Tetsuya
• Shimakawa Osamu

Classifications

• G02B6/02214

  tailored to obtain the desired dispersion, e.g. dispersion shifted, dispersion flattened · CPC title

• G02B6/3885

  Multicore or multichannel optical connectors, i.e. one single ferrule containing more than one fibre, e.g. ribbon type (optical ribbon cable G02B6/4403, G02B6/448) · CPC title

• G02B6/0365

  arranged - - + · CPC title

• G02B6/02395

  Glass optical fibre with a protective coating, e.g. two layer polymer coating deposited directly on a silica cladding surface during fibre manufacture (G02B6/02052, G02B6/02057, G02B6/024, G02B6/032, G02B6/105, G02B6/14 take precedence; coating on fibre gratings G02B6/02104; multilayer core or cladding G02B6/036; reinforcing splice joints G02B6/2558; optical cables, i.e. comprising protective structures external to the protective coating such as a jacket or plural coated optical fibres G02B6/44; coating of glass to obtain optical fibres C03C25/104) · CPC title

• G02B6/02042 Primary

  Multicore optical fibres · CPC title