Abstract

The present invention relates to an aqueous calcium carbonate containing composition, to methods for producing such aqueous calcium carbonate containing compositions and to the use of the aqueous calcium carbonate containing composition in paper, paper coating, plastics and/or paint applications and as filler in paper.

First claim

The invention claimed is:

1. An aqueous calcium carbonate containing composition comprising
a) a calcium carbonate containing material in an amount of at least 10 wt.-%, based on the total dry weight of the composition,
b) at least one anionically charged comb polymer having a specific charge of −5 to −500 C/g at pH 8,
c) optionally at least one binding agent in an amount of at least 2.5 wt.-%, based on the total dry weight of the composition, and
d) at least one salt of a divalent or trivalent cation in an amount of between 1 and 20 wt.-%, based on the total dry weight of the composition, whereby at least 95 wt.-% of the total amount of salt is dissolved within the composition, and
wherein the composition has a Brookfield viscosity of below 2500 mPa·s when measured 1 minute after stirring at a rotational speed of 100 rpm at a temperature of 25° C.

2. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer has an average molecular weight M W in the range between 10,000 and 10,000,000 g/mol.

3. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer has an intrinsic viscosity in the range of 5 to 500 ml/g.

4. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer has a specific charge from −10 C/g to −500 C/g at pH 8.

5. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer comprises structural units of formula (I)

wherein R 1 , R 2 , R 3 , R 4 , R 5 and R 6 are independently selected from hydrogen or alkyl groups, having 1 to 40 carbon atoms,
X is a negatively charged functional group,
Y represents a functional linkage group, which is independently selected from the group consisting of ether, ester, urethane and amide groups,
Z is a positively charged functional group,
R 7 and R 8 are independently selected from hydrogen or alkyl groups having 1 to 4 carbon atoms,
R 9 is selected from hydrogen or an alkyl group having 1 to 40 carbon atoms,
a, b, c and d are integers such that 5≦(a+b+c)·d≦150, and
n, m and o are selected such that the anionically charged polymer has a specific charge from −5 C/g to −500 C/g at pH 8.

6. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer comprises
a) 5 wt.-% to 40 wt.-%, based on the total amount of monomers, of (meth)acrylic acid,
b) 60 wt.-% to 95 wt.-%, based on the total amount of monomers, of at least one monomer of Formula (II)
R-(OE) α -(OP) β -R′   (II)

wherein R is a polymerizable functional group selected from methacrylate or methacryl-urethane,
OE and OP designates ethylene oxide and propylene oxide, respectively,
α and β are integers each having a value from 0 to 150 and at least one of α or β has a value of greater than 0,
R′ represents hydrogen or an alkyl group having 1 to 4 carbon atoms.

7. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one anionically charged comb polymer comprises
a) 5 wt.-% to 20 wt.-%, based on the total amount of monomers, of (meth)acrylic acid,
b) 80 wt.-% to 95 wt.-%, based on the total amount of monomers, of at least one monomer of Formula (II)
R-(OE) α -(OP) β -R′   (II)

wherein R is a polymerizable functional group selected from methacrylate or methacryl-urethane,
OE and OP designates ethylene oxide and propylene oxide, respectively,
α and β are integers each having a value from 0 to 150 and at least one of α or β has a value of greater than 0,
R′ represents hydrogen or an alkyl group having 1 to 4 carbon atoms.

8. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises the at least one anionically charged comb polymer in an amount from 0.01 to 10 wt.-%, based on the total dry weight of the composition.

9. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises the at least one anionically charged comb polymer in an amount from 0.15 to 1.75 wt.-%, based on the total dry weight of the composition.

10. The aqueous calcium carbonate containing composition of claim 1 , wherein the calcium carbonate containing material is a ground calcium carbonate, a precipitated calcium carbonate, a modified calcium carbonate or a mixture thereof.

11. The aqueous calcium carbonate containing composition of claim 1 , wherein the calcium carbonate containing material has a weight median particle size d 50 from 0.1 to 100 μm.

12. The aqueous calcium carbonate containing composition of claim 1 , wherein the calcium carbonate containing material has a weight median particle size d 50 from 0.4 to 3.0 μm.

13. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises the calcium carbonate containing material in an amount from 10 to 70 wt.-%, based on the total dry weight of the composition.

14. The aqueous calcium carbonate containing composition of claim 1 , wherein the binding agent is selected from the group consisting of polyvinyl alcohol, polyvinyl acetate, starch, proteins, casein, cellulose, cellulosic derivatives, ethylhydroxylethyl cellulose and/or carboxymethyl cellulose, and any mixture thereof.

15. The aqueous calcium carbonate containing composition of claim 1 , wherein the binding agent is preferably the binding agent is selected from the group consisting of polyvinyl alcohol, polyvinyl acetate, and mixtures thereof.

16. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises the at least one binding agent in an amount between 2.5 and 20 wt.-%, based on the total dry weight of the composition.

17. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one salt of a divalent or trivalent cation is selected from the group consisting of a chloride salt of a divalent or trivalent cation, a bromide salt of a divalent or trivalent cation, a sulfate salt of a divalent or trivalent cation, and any mixture thereof.

18. The aqueous calcium carbonate containing composition of claim 1 , wherein the at least one salt of a divalent or trivalent cation is a chloride salt of a divalent or trivalent cation selected from the group consisting of calcium chloride, magnesium chloride, strontium chloride, zinc chloride, manganese chloride, and any mixture thereof.

19. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises the at least one salt of a divalent or trivalent cation in an amount of between 3 and 17 wt.-%, based on the total dry weight of the composition, whereby at least 95 wt.-% of the total amount of salt is dissolved within the composition.

20. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition comprises one or more further additives, fixation aids, or cationic homopolymers based on monomer units of diallyl dialkyl ammonium salts or polyethylene imines.

21. The aqueous calcium carbonate containing composition of claim 1 , wherein the composition has a solids content from 10 to 70 wt.-%, based on the total dry weight of the composition.

22. The aqueous

Assignees

• Omya Int Ag

Inventors

• Rentsch Samuel
• Gerard Daniel E
• Buri Matthias
• Gane Patrick A C
• Kukkamo Vesa

Classifications

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• C01P2006/22

  Rheological behaviour as dispersion, e.g. viscosity, sedimentation stability · CPC title

• C09D129/04

  Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids · CPC title

• D21H17/00

  Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution · CPC title

• C09C1/021 Primary

  Calcium carbonates · CPC title