Color-strikable glass containers

Patent metadata

Field	Value
Publication number	US-9725354-B2
Application number	US-201213666629-A
Country	US
Kind code	B2
Filing date	Nov 1, 2012
Priority date	Nov 1, 2012
Publication date	Aug 8, 2017
Grant date	Aug 8, 2017

Abstract

Latent colorant material compositions, soda-lime-silica glass compositions, and related methods of manufacturing color-strikable glass containers. The latent colorant material compositions may be introduced into a plurality of base glass compositions having redox numbers in the range of −40 to +20 to produce color-strikable glass compositions and color-strikable glass containers. The latent colorant material compositions introduced into the base glass compositions include a mixture of cuprous oxide (Cu 2 O), stannous oxide (SnO), bismuth oxide (Bi 2 O 3 ), and carbon (C). After formation, the color-strikable glass containers may be heat-treated to strike red or black therein.

First claim

The invention claimed is:

1. A method of making glass containers, the method including the steps of:
(a) introducing a mixture of latent colorant materials comprising cuprous oxide (Cu2O), stannous oxide (SnO), bismuth oxide (Bi203), and carbon (C) into a soda-lime-silica base glass composition to produce a color-strikable glass composition, wherein the soda-lime-silica base glass composition comprises at least one colorant selected from the group consisting of: iron oxide (Fe 2 O 3 ), cobalt oxide (CoO), and chromium oxide (Cr203), and wherein the soda-lime-silica base glass composition comprises 0.2-0.6 wt. % iron oxide (Fe 2 O 3 ) when the at least one colorant comprises iron oxide (Fe 2 O 3 );
(b) forming color-strikable glass containers from the color-strikable glass composition, wherein the color-strikable glass containers are formulated to develop a red or visually black color upon heat treatment and striking at temperatures above 600 degrees Celsius;
(c) annealing the color-strikable glass containers at temperatures between 550 and 600 degrees Celsius without imparting a red or visually black color to the containers; and
(d) heating at least one of the color-strikable glass containers at a temperature above 600 degrees Celsius for 10 to 90 minutes to strike red or black coloration in the at least one color-strikable glass container to produce at least one red or black glass container.

2. The method set forth in claim 1 , wherein said step (d) includes heating the at least one color-strikable glass container at a temperature between 630 and 650 degrees Celsius for 30 to 40 minutes to strike red or black coloration in the at least one color-strikable glass container to produce at least one red or black glass container.

3. The method set forth in claim 1 , wherein the soda-lime-silica base glass composition comprises 0.2-0.3 wt. % Fe 2 O 3 , and the at least one color-strikable glass container is heated in said step (d) to strike red coloration in the at least one color-strikable glass container to produce at least one red glass container.

4. The method set forth in claim 1 , wherein the soda-lime-silica base glass composition is an amber glass composition including 0.2-0.6 wt. Fe 2 O 3 , and the at least one color-strikable glass container is heated in said step (d) to strike black coloration in the at least one color-strikable glass container to produce at least one black glass container.

5. The method set forth in claim 1 wherein the mixture of latent colorant materials is introduced into the soda-lime-silica base glass composition in a glass batch furnace.

6. The method set forth in claim 1 , wherein the soda-lime-silica base glass composition is a cobalt blue glass composition including 0.01-0.15 wt. % CoO, and the at least one color-strikable glass container is heated in said step (d) to strike black coloration in the at least one color-strikable glass container to produce at least one black glass container.

7. The method set forth in claim 1 , wherein the soda-lime-silica base glass composition is an emerald green glass composition including 0.01-0.4 wt. % Cr 2 O 3 , and the at least one color-strikable glass container is heated in said step (d) to strike black coloration in the at least one color-strikable glass container to produce at least one black glass container.

8. The method set forth in claim 1 , wherein the color-strikable glass containers are annealed in step (c) at temperature between 550 and 600 degrees Celsius for 30 to 90 minutes.

9. The method set forth in claim 1 wherein the soda-lime-silica base glass composition comprises 0.005-0.15 wt. % sulfur trioxide (SO 3 ).

10. The method set forth in claim 1 wherein the soda-lime-silica base glass composition comprises 0.005-0.02 wt. % sulfur trioxide (SO 3 ).

11. A method of making glass containers, the method including the steps of:
preparing a soda-lime-silica glass composition having a redox number in the range of −40 to +10 and including: 60-75 wt. % SiO 2 , 7-15 wt. % Na 2 O, 6-12 wt. % CaO, 0.1-3.0 wt. % Al 2 O 3 , 0.0-2.0 wt. % MgO, 0.0-2.0 wt. % K 2 O, and 0.01-0.25 wt. % SO 3 ;
mixing a latent colorant material composition into the soda-lime-silica glass composition to produce a color-strikable glass composition including: 0.0875-0.35 wt. cuprous oxide (Cu 2 O), 0.06-0.5 wt. % stannous oxide (SnO), 0.0125-0.05 wt. % bismuth oxide (Bi 2 O 3 ), and 0.02-0.10 wt. % carbon (C);
forming color-strikable glass containers from the color-strikable glass composition, wherein the amount of sulfur trioxide (SO 3 ) retained in the glass containers is in the range of 0.005-0.15 wt. %;
annealing the color-strikable glass containers at temperatures between 550 and 600 degrees Celsius without imparting a red or visually black color to the containers;
raising the temperature of a first one of the color-strikable glass containers above 600 degrees Celsius to strike red or black coloration therein to produce a red or black glass container; and
maintaining a second one of the color-strikable glass containers at a temperature below 600 degrees Celsius to produce a generally colorless, arctic blue, amber, cobalt blue, or emerald green glass container.

12. The method set forth in claim 11 wherein the latent colorant material composition is mixed into the soda-lime-silica glass composition in a glass batch furnace.

13. The method set forth in claim 11 wherein the soda-lime-silica glass composition has a redox number in the range of −4 to −40, and the amount of sulfur trioxide (SO 3 ) retained in the glass containers is in the range of 0.005-0.02 wt. %.

14. A method of making glass containers, the method including:
(a) providing a mixture of latent colorant materials including cuprous oxide (Cu 2 O), stannous oxide (SnO), bismuth oxide (Bi 2 O 3 ), and carbon (C);
(b) mixing said mixture of latent colorant materials with soda-lime-silica glass precursor materials to produce a batch of raw materials, wherein the soda-lime-silica glass precursor materials include at least one colorant selected from the group consisting of iron oxide, cobalt oxide, and chromium oxide;
(c) melting the batch of raw materials in a glass batch furnace to produce molten glass having a color-strikable glass composition and comprising at least one colorant selected from the group consisting of: iron oxide (Fe 2 O 3 ), cobalt oxide (CoO), and chromium oxide (Cr 2 O 3 ), wherein the molten glass comprises 0.2-0.6 wt. % iron oxide (Fe 2 O 3 ) when the at least one colorant comprises iron oxide (Fe 2 O 3 );
(d) forming color-strikable glass containers from the molten glass;
(e) annealing the color-strikable glass containers at temperatures between 550 and 600 degrees Celsius without imparting a red or visually black color to the containers;
(f) maintaining a first one of the color-strikable glass containers at a temperature below 600 degrees Celsius to produce a generally colorless, light blue, amber, blue, or green glass container; and
(g) heating a second one of the color-strikable glass containers at a temperature above 600 degrees Celsius to strike red or black coloration therein to produce a red or black glass container.

15. The method set forth in claim 14 wherein the glass containers formed in step (d) exhibit light blue, amber, cobalt blue, or emerald green coloration prior to being heat treated at a temperature above 600 degrees Celsius.

16. The method set forth in claim 14 wherein said step (g) includes heating the second one of the color-strikable glass containers at a temperature above 600 degrees Celsius for 10 to 90 minutes.

1

Assignees

• Owens Brockway Glass Container

Inventors

• Ordway Edward
• Howse Terence K
• Baker Daniel
• Barton Stephen
• Click Carol A

Classifications

• C03B32/00

  Thermal after-treatment of glass products not provided for in groups {C03B19/00} , C03B25/00 - C03B31/00 {or C03B37/00}, e.g. crystallisation, eliminating gas inclusions or other impurities; {Hot-pressing vitrified, non-porous, shaped glass products} · CPC title

• C09C1/0009

  Pigments for ceramics (C09C1/0015, C09C1/0078 take precedence) · CPC title

• C03C3/087

  containing calcium oxide, e.g. common sheet or container glass · CPC title

• Y10T428/131

  Glass, ceramic, or sintered, fused, fired, or calcined metal oxide or metal carbide containing [e.g., porcelain, brick, cement, etc.] · CPC title

• C03C3/078

  containing an oxide of a divalent metal, e.g. an oxide of zinc · CPC title