Integrated shape memory polymer and caul tool

Patent metadata

Field	Value
Publication number	US-9724870-B2
Application number	US-201313833693-A
Country	US
Kind code	B2
Filing date	Mar 15, 2013
Priority date	Mar 15, 2013
Publication date	Aug 8, 2017
Grant date	Aug 8, 2017

Abstract

A method of forming a composite material part using an integrated shape memory polymer (SMP) and caul tool comprises the steps of: placing a caul on a positive feature of a mold, deforming the SMP from a relaxed state such that the SMP integrates with the caul to form an integrated SMP and caul tool, placing composite material on the integrated SMP and caul tool, heating the composite material to cure the composite material to form a composite material part while the SMP remains deformed, and stimulating the SMP to return to the relaxed state such that the SMP separates from the caul and the composite material part.

First claim

Having thus described various embodiments of the invention, what is claimed as new and desired to be protected by Letters Patent includes the following:

1. A method of forming a composite material part, the method comprising the steps of:
placing a caul on a positive feature of a mold, wherein the caul is rigid, wherein the positive feature protrudes outward or inward from a surface of the mold, wherein portions of the surface of the mold are not covered by the caul;
deforming a shape memory polymer (SMP) from a relaxed state against the caul and mold into a geometry that interlocks with features of the caul such that the SMP forms a trapped geometry around the caul to thereby form an integrated SMP and caul tool;
placing composite material on the integrated SMP and caul tool, wherein at least a portion of the composite material rests directly against the SMP and at least a portion of the composite material rests directly against the caul;
heating the composite material to cure the composite material to form a composite material part while the SMP remains deformed; and
stimulating the SMP to return to the relaxed state such that the SMP separates from the caul and the composite material part.

2. The method of claim 1 , wherein the mold is shaped to correspond with at least a portion of an inner mold line (IML) surface of a fuselage, wherein the positive feature is shaped to correspond with a stringer or frame of the fuselage.

3. The method of claim 1 , wherein the caul has a coefficient of thermal expansion roughly equal to that of the composite material.

4. The method of claim 1 , wherein deforming the SMP from the relaxed state includes the steps of:
heating the SMP to a temperature above the glass transition temperature of the SMP material,
applying a pressure differential to the SMP sufficient to cause the SMP to inflate such that the SMP wraps around the interlocking features included on the caul, and
reducing the temperature of the SMP to below the glass transition temperature.

5. The method of claim 4 , wherein expansion of the SMP forms negative features that correspond to additional positive features of the mold.

6. The method of claim 5 , wherein composite material is placed in the negative features of the integrated SMP and caul tool.

7. The method of claim 1 , wherein the composite material is heated during curing to a temperature below the glass transition temperature.

8. The method of claim 1 , wherein stimulating the SMP to return to the relaxed state includes heating the SMP to a temperature above the glass transition temperature.

9. The method of claim 1 , wherein the step of deforming the SMP includes triggering the SMP from the relaxed state, forcing portions of the SMP to wrap around beveled edges of the caul, thus retaining the caul via interlocking geometry of the deformed SMP, and then triggering the SMP to become rigid again while the SMP remains deformed.

10. The method of claim 9 , wherein the caul is symmetrical about a plane extending along a longitudinal axis of the caul.

Assignees

• Spirit Aerosys Inc

Inventors

• Morrow Christopher J

Classifications

• B29C61/02 Primary

  Thermal shrinking · CPC title

• B29C70/44

  using isostatic pressure, e.g. pressure difference-moulding, vacuum bag-moulding, autoclave-moulding or expanding rubber-moulding · CPC title

• B29C33/48

  with means for collapsing or disassembling · CPC title

• B29C70/549

  Details of caul plates, e.g. materials or shape · CPC title