Chemical additives for water flux enhancement

Patent metadata

Field	Value
Publication number	US-9724651-B2
Application number	US-201514799427-A
Country	US
Kind code	B2
Filing date	Jul 14, 2015
Priority date	Jul 14, 2015
Publication date	Aug 8, 2017
Grant date	Aug 8, 2017

Abstract

Provided are flux enhancing inclusion complexes for preparing highly permeable thin film composite membranes, and processes that include adding the flux enhancing inclusion complexes to the organic phase or aqueous phase prior to interfacial polymerization of the thin film composite membrane. The thin film composite membranes are suitable for nanofiltration, and reverse and forward osmosis. The provided processes can include contacting a porous support membrane with an aqueous phase containing a polyamine to form a coated support membrane, and applying an organic phase containing a polyfunctional acid halide and a flux enhancing inclusion complex to the coated support membrane to interfacially polymerize the polyamine and the polyfunctional acid halide to form a discrimination layer to form thin film composite membranes.

First claim

What is claimed is:

1. A flux enhancing inclusion complex, comprising:
a host component having a cavity, wherein the host component comprises a crown ether or derivative thereof, or at least two glyme molecules; and
a guest component within the cavity, wherein the guest component includes a metal chelate containing a metal atom or metal ion, and a bidentate ligand.

2. The complex of claim 1 , wherein the crown ether is selected from among 12-crown-4, 15-crown-5, 18-crown-6, 20-crown-6, 21-crown-7, 24-crown-8, dicyclohexyl-18-crown-6, dibenzo-18-crown-6, 1,10-diaza-18-crown-6, 1,7,13-triaza-18-crown-6, and 1,4,10,13-tetraaza-18-crown-6, and the crown ether is unsubstituted or is substituted with one or more substituents selected from among vinyl, benzo, amido, aryl, thia, aza, alkyl, haloalkyl, and nitro substituents and combinations thereof.

3. The complex of claim 1 , wherein the metal atom or metal ion is selected from among Group 2 or Group 13 of the periodic table.

4. The complex of claim 1 , wherein the metal atom or metal ion is an alkaline earth metal.

5. The complex of claim 1 , wherein the bidentate ligand is selected from among:

wherein each of R 1 , R 2 , R 3 , R 4 and R 5 separately is selected from among a C 1 -C 10 alkyl, a halogenated C 1 -C 10 alkyl, a 5-membered aromatic ring, a 6-membered aromatic ring, an aromatic bicyclic ring system containing two fused 6-membered rings, and an aromatic bicyclic ring system containing a 5-membered ring fused to a 6-membered aromatic ring.

6. The complex of claim 1 , wherein the bidentate ligand is an acetylacetonate (acac) or fluorinated acetylacetonate.

7. The complex of claim 1 , wherein the metal chelate containing a bidentate ligand and a metal atom or metal ion is selected from among Al(acac) 3 , Al(F6acac) 3 , Ba(acac) 2 , Ba(F6acac) 2 , Be(acac) 2 , Be(F6acac) 2 , Ca(acac) 2 , Ca(F6acac) 2 , Cd(acac) 2 , Cd(F6acac) 2 , Ce(acac) 3 , Ce(F6acac) 3 , Cr(acac) 3 , Co(acac) 3 , Cu(acac) 2 , Cu(F6acac) 2 , Dy(acac) 3 , Er(acac) 3 , Fe(acac) 2 , Fe(acac) 3 , Ga(acac) 3 , Hf(acac) 4 , In(acac) 3 , K(acac), Li(acac), Mg(acac) 2 , Mg(F6acac) 2 , Mn(acac) 2 , Mn(acac) 3 , MoO 2 (acac) 2 , MoO 2 (F6acac) 2 , Na(acac), Nd(acac) 3 , Nd(F6acac) 3 , Ni(acac) 2 , Ni(F6acac) 2 , Pd(acac) 2 , Pr(acac) 3 , Pr(F6acac) 3 , Ru(acac) 3 , Ru(F6acac) 3 , Sc(acac) 2 , Sc(F6acac) 2 , Sm(acac) 3 , Sn(acac) 2 , Sn(acac) 2 Cl 2 , t-butyl-Sn(acac) 2 , t-butyl-Sn(acac) 2 Cl 2 , Sn(F6acac) 2 , Sr(acac) 2 , Sr(F6acac) 2 , Tb(acac) 3 , V(acac) 3 , Y(acac) 3 , Y(F6acac) 3 , Zn(acac) 2 , Zn(F6acac) 2 , and Zr(acac) 4 , wherein F6acac refers to 1,1,1,5,5,5-hexafluoroacetylacetonate.

8. The complex of claim 1 , wherein the bidentate ligand is a beta-diketonate or a fluorinated beta-diketonate.

9. The complex of claim 1 , wherein the bidentate ligand is selected from among pentane-2,4-dionate, 1,5-difluoro-pentane-2,4-dionate, 1,1,5,5-tetrafluoropentane-2,4-dionate, 1,1,1,5,5,5-hexafluoro-pentane-2,4-dionate, propane-1,3-dionate, butane-1,3-dionate, 4-fluorobutane-1,3-dionate, 4,4-difluorobutane-1,3-dionate, 4,4,4-trifluorobutane-1,3-dionate, heptane-3,5-dionate, 1-fluorohexane-2,4-dionate, 1,5-difluoropentane-2,4-dionate, 1,1,5-trifluoropentane-2,4-dionate, 1,1,5,5-tetrafluoro-pentane-2,4-dionate, 1,1,1,5,5-pentafluoro-pentane-2,4-dionate, 1,1,1,5,5,5-hexa-fluoropentane-2,4-dionate and octane-3,5-dionate and combinations thereof.

10. A process for preparing a thin film composite membrane, comprising:
(a) preparing an aqueous phase comprising a polyamine, and an organic phase comprising a polyfunctional acid halide, wherein the aqueous phase or organic phase or both further include the flux enhancing inclusion complex of claim 1 ;
(b) applying the aqueous phase to a surface of a porous support membrane to form a coated support membrane; and
(c) applying the organic phase to the coated support membrane and interfacially polymerizing the polyamine and the polyfunctional acid halide to form a discrimination layer of a thin film composite membrane comprising the porous support membrane and the discrimination layer, the thin film composite membrane having a water flux that is greater than the water flux of a thin film composite membrane prepared in the absence of the flux enhancing inclusion complex.

11. The process of claim 10 , wherein the amount of the flux enhancing inclusion complex included in the organic phase is from about 0.001 wt % to about 1 wt %, based on the weight of the organic phase.

12. The process of claim 10 , wherein the process further comprises adding a processing aid selected from among a surfactant, a co-solvent, a drying agent, a catalyst or any combination thereof to the aqueous phase or organic phase prior to applying the aqueous phase or organic phase to the porous support membrane, wherein the amount of processing aid is from about 0.001 wt % to about 10 wt % based on the weight of the aqueous phase or organic phase.

13. The process of claim 10 , further comprising adding hexamethyl phosphoramide or a dialkyl sulfoxide or a combination thereof to the aqueous phase or organic phase or both in an amount of from about 0.5 wt % to 5 wt % based on the weight of the aqueous phase or the organic phase, wherein the dialkyl sulfoxide is of the formula:

wherein each of R a and R b independently is selected from among C 1 -C 25 alkyl and C 1 -C 20 hydroxyalkyl.

14. The process of claim 10 , wherein the aqueous phase or the organic phase or both further comprises nanoparticles selected from among zeolites, fullerenes and carbon nanotubes and combinations thereof, wherein the nanoparticles are present in an amount from about 0.001 wt % to about 0.5 wt % based on the weight of the aqueous phase or the organic phase.

15. The process of claim 10 , wherein the thin film composite membrane is a reverse osmosis membrane.

16. A thin film composite membrane prepared according to the process of claim 10 .

17. The thin film composite membrane of claim 16 that is a reverse osmosis membrane.

18. The reverse osmosis membrane of claim 17 , wherein:
the membrane exhibits a water flux of at least 30 gfd when the membrane is exposed to deionized water containing 32,000 ppm NaCl at a temperature of 25° C. and a pressure of 800 psi; or
the membrane exhibits a salt rejection of at least 96% and a water flux of at least 35 gfd when the membrane is exposed to deionized water containing 32,000 ppm NaCl at a temperature of 25° C. and a pressure of 800 psi.

19. A method of purifying tap water or seawater or brackish water, comprising:
a) contacting the tap water with the reverse osmosis membrane of claim 17 at a hydrostatic pressure of about 100 psi or less; or
b) contacting the seawater with the reverse osmosis membrane of claim 17 at a hydrostatic pressure of about 800 psi or less; or
c) contacting the brackish water with the reverse osmosis membrane of claim 17 at a hydrostatic pressure of about 225 psi or less.

20. A reverse osmosis module, comprising a reverse osmosis membrane of claim 17 spirally wound around a central perforated tube.

21. A reverse osmosis membrane, comprising:
a support membrane; and
on a surface of the support membrane a discrimination layer formed by interfacially polymerizing a polyamine and a polyfunctional acid halide in th

Assignees

• Lg Nanoh2O Inc
• Lg Chemical Ltd

Inventors

• Jeon Hyung Joon
• Koehler Jeff
• Choi Hyungsam

Classifications

• B01D2325/20

  Specific permeability or cut-off range · CPC title

• B01D61/025

  Reverse osmosis; Hyperfiltration · CPC title

• C02F2103/08

  Seawater, e.g. for desalination · CPC title

• Y02A20/131

  Reverse-osmosis · CPC title

• B01D71/56

  Polyamides, e.g. polyester-amides · CPC title