Local J-coupling dye-zeolite antenna composite materials

Patent metadata

Field	Value
Publication number	US-9724433-B2
Application number	US-201214360877-A
Country	US
Kind code	B2
Filing date	Dec 10, 2012
Priority date	Dec 12, 2011
Publication date	Aug 8, 2017
Grant date	Aug 8, 2017

Abstract

A dye loaded zeolite composite material comprises a plurality of zeolite crystals each having a plurality of straight through uniform channels extending between the proximal face and the distal face and having a channel axis parallel to and a channel width transverse to a longitudinal crystal axis A. Each channel contains a substantially linear arrangement of dye molecules comprising first and second dye molecules having an elongated shape with a longitudinal extension exceeding said channel width and a lateral extension not exceeding said channel width. Each dye molecule consists of a chromophore moiety arranged between a pair of terminal moieties, wherein: the chromophore moieties of the first and second dye molecules are substantially identical, the terminal moieties of the first dye molecules have a lateral extension larger than half of the channel width, the terminal moieties of the second dye molecules have a lateral extension smaller than half of the channel width, the linear arrangement of dye molecules comprises at least one pair of second dye molecules adjacent each other.

First claim

The invention claimed is:

1. A dye loaded zeolite composite material, comprising:
a plurality of zeolite crystals, each one of said crystals having a proximal face and a distal face opposed therefrom and substantially parallel to said proximal face,
each one of said crystals having a plurality of straight through uniform channels extending between the proximal face and the distal face and having a channel axis parallel to and a channel width transverse to a longitudinal crystal axis A,
each channel having a proximal channel end located at the proximal face and a distal channel end located at the distal face, said channels containing a substantially linear arrangement of dye molecules,
each one of said dye molecules having an elongated shape with a longitudinal extension exceeding a channel width and a lateral extension not exceeding said channel width, and
said linear arrangement of dye molecules comprising first dye molecules and second dye molecules, each one of said first and second dye molecules consisting of a chromophore moiety arranged between a pair of terminal moieties,
wherein the chromophore moieties of said first dye molecules and of said second dye molecules are substantially identical, but the terminal moieties of said first dye molecules have a lateral extension larger than half of said channel width so that the terminal moieties of said first dye molecules act as spacer elements and energy can be transported from one to the other of two adjacent first dye molecules via FRET (Foerster resonance energy transfer), while the terminal moieties of said second dye molecules have a lateral extension smaller than half of said channel width so that the terminal moieties of said dye molecules allow for the overlap of the terminal moieties of two adjacent second dye molecules and thus enable J-coupling between these adjacent second dye molecules, and
said linear arrangement of dye molecules comprises at least one pair of second dye molecules adjacent each other.

2. The dye loaded zeolite composite material according to claim 1 , wherein the terminal moieties of said first dye molecules are identical.

3. The dye loaded zeolite composite material according to claim 1 , wherein the terminal moieties of said second dye molecules are identical.

4. The dye loaded zeolite composite material according to claim 1 , wherein the molar ratio of said first dye molecules to said second dye molecules is at least 20.

5. The dye loaded zeolite composite material according to claim 1 , wherein said linear arrangement of dye molecules further comprises third dye molecules, said third dye molecules having an electronic excitation energy that is larger than the electronic excitation energy of said first and second dye molecules.

6. The dye loaded zeolite composite material according to claim 1 , wherein said channel ends are provided with closure units.

7. The dye loaded zeolite composite material according to claim 6 , wherein said closure units are formed by a plurality of closure molecules having an elongated shape and consisting of a head moiety and a tail moiety, the tail moiety having a longitudinal extension of more than a dimension of crystal unit cells along the longitudinal crystal axis A and the head moiety having a lateral extension that is larger than said channel width and will prevent said head moiety from penetrating into a channel, a channel being terminated, in plug-like manner, at a proximal or distal end thereof, by a closure molecule whose tail moiety penetrates into said channel and whose head moiety substantially occludes said channel end while projecting over said proximal or distal face, respectively.

8. The dye loaded zeolite composite material according to claim 6 , wherein said closure units are formed by a closure layer comprising, at one side thereof, a plurality of protruding moieties having a longitudinal extension of more than a dimension of crystal unit cells along the longitudinal crystal axis A and a lateral extension that is smaller than said channel width, each one of said protruding moieties penetrating in plug-like manner the end of an associated channel.

9. The dye loaded zeolite composite material according to claim 8 , wherein said closure layer is attached to a solid substrate.

10. A method of producing a dye loaded zeolite composite material according to claim 1 , comprising the steps of:
a) providing an amount of zeolite crystals, each one of said crystals having a pair of substantially parallel faces, each one of said crystals further having a plurality of straight through uniform channels extending between said two faces and having a channel axis parallel to and a channel width transverse to a longitudinal crystal axis A;
b) either: loading a first amount of first dye molecules into the zeolite channels followed by adding thereto a second amount of second dye molecules, thereby forming a dye loaded zeolite composite material having a terminal acceptor configuration;
or else: loading a first amount of second dye molecules into the zeolite channels followed by adding thereto a second amount of first dye molecules, thereby forming a dye loaded zeolite composite material having an internal acceptor configuration.

11. The method according to claim 10 , further comprising the step, after loading said first dye molecules and said second dye molecules, of closing said zeolite channels.

12. The method according to claim 11 , wherein said closing step comprises adding closure molecules having an elongated shape and consisting of a head moiety and a tail moiety, the tail moiety having a longitudinal extension of more than a dimension of crystal unit cells along the longitudinal crystal axis A and the head moiety having a lateral extension that is larger than a channel width and will prevent said head moiety from penetrating into said channel, said channel being terminated, in generally plug-like manner, at the proximal or distal end thereof located at a proximal or distal face of said pair of substantially parallel faces, respectively, by a closure molecule whose tail moiety penetrates into said channel and whose head moiety substantially occludes said proximal or distal channel end while projecting over said proximal or distal face, respectively.

13. The method according to claim 11 , wherein said closing step comprises forming a closure layer comprising, at one side thereof, a plurality of protruding moieties having a longitudinal extension of more than a dimension of crystal unit cells along the longitudinal crystal axis A and a lateral extension that is smaller than a channel width, each one of said protruding moieties penetrating in generally plug-ke manner the end of an associated channel.

Assignees

• Univ Zuerich
• Calzaferri Gion
• Kunzmann Andreas
• Unversität Zürich

Inventors

• Calzaferri Gion
• Kunzmann Andreas
• Bruehwiler Dominik

Classifications

• H05B33/20

  characterised by the chemical or physical composition or the arrangement of the material in which the electroluminescent material is embedded · CPC title

• C09K2211/1011

  Condensed systems · CPC title

• C01B37/04 Primary

  Aluminophosphates [APO compounds] · CPC title

• C09K2211/1092

  containing sulfur as the only heteroatom · CPC title

• H01L51/5012

  Electricity · mapped topic