Method of producing structure for producing casting, and structure such as mold

Patent metadata

Field	Value
Publication number	US-9719211-B2
Application number	US-201314758131-A
Country	US
Kind code	B2
Filing date	Dec 25, 2013
Priority date	Dec 28, 2012
Publication date	Aug 1, 2017
Grant date	Aug 1, 2017

Abstract

Provided is a method of producing a structure for producing a casting, including: a process (I) of obtaining a slurry composition containing an organic fiber, an inorganic fiber, a thermosetting resin, and water; a process (II) of obtaining a fiber laminate by subjecting the slurry composition to papermaking; and a process (III) of dehydrating the fiber laminate and thereafter drying the resultant, in which the process (I) includes a process (I-1) of beating a mixture containing the organic fiber and water, a process (I-2) of mixing the mixture obtained in the process (I-1) and water, and a process (I-3) of mixing the mixture obtained in the process (I-2) and the inorganic fiber, the thermosetting resin is mixed in at least any of the process (I-1), the process (I-2), and the process (I-3), and an average fiber length of the inorganic fiber in the structure for producing a casting is 1 mm or longer and 5 mm or shorter.

First claim

The invention claimed is:

1. A method of producing a structure for producing a casting, the method comprising:
a process (I) of obtaining a slurry composition containing an organic fiber, an inorganic fiber, a thermosetting resin, and water;
a process (II) of obtaining a fiber laminate by subjecting the slurry composition to papermaking; and
a process (III) of dehydrating the fiber laminate and thereafter drying the resultant,
wherein the process (I) includes:
a process (I-1) of beating a mixture containing the organic fiber and water,
a process (I-2) of mixing the mixture obtained in the process (I-1) and water, and
a process (I-3) of mixing the mixture obtained in the process (I-2) and the inorganic fiber,

the thermosetting resin is mixed in at least any of the process (I-1), the process (I-2), and the process (I-3), and
an average fiber length of the inorganic fiber in the structure for producing a casting is 1 mm or longer and 5 mm or shorter.

2. The method of producing a structure for producing a casting according to claim 1 ,
wherein a content of the inorganic fiber in the structure for producing a casting is 1 part by mass or more and 6 parts by mass or less with respect to 100 parts by mass of the structure for producing a casting.

3. The method of producing a structure for producing a casting according to claim 1 ,
wherein, in the process (I), the inorganic fiber is used in a proportion of 0.14 mass % or less with respect to an amount of the water with which the inorganic fiber is initially mixed.

4. The method of producing a structure for producing a casting according to claim 1 ,
wherein the average fiber length of the inorganic fiber used in the process (I) is 1 mm or longer and 5 mm or shorter.

5. The method of producing a structure for producing a casting according to claim 1 ,
wherein the inorganic fiber is a carbon fiber.

6. A method of producing a casting, which uses the structure for producing a casting obtained in the producing method according to claim 1 .

7. The method of producing a structure for producing a casting according to claim 1 ,
wherein a ratio of a major axis to a minor axis of the inorganic fiber in the structure for producing a casting is 1 or higher, and is 5000 or lower.

8. The method of producing a structure for producing a casting according to claim 1 ,
wherein a mass ratio of the organic fiber to the inorganic fiber in the structure for producing a casting is, in terms of inorganic fiber/organic fiber, 0.05 or higher, and is 1.0 or lower.

9. The method of producing a structure for producing a casting according to claim 1 ,
wherein the content of the inorganic fiber in the slurry composition obtained in the process (I) is 0.03 mass % or more, and is 0.2 mass % or less.

10. The method of producing a structure for producing a casting according to claim 1 ,
wherein the ratio of the major axis to the minor axis of the inorganic fiber in the raw material slurry is 1 or higher, and is 5000 or lower.

11. The method of producing a structure for producing a casting according to claim 1 ,
wherein a content of the inorganic fiber in the slurry composition obtained in the process (I) is, with respect to 100 parts by mass of the sum of the organic fiber, the inorganic fiber, the inorganic particles, and the thermosetting resin used in the entire process (I), 1 part by mass or more, and is 6 parts by mass or less.

12. A method of producing a structure for producing a casting, the method comprising:
a process (I) of obtaining a slurry composition containing an organic fiber, an inorganic fiber, inorganic particles, a thermosetting resin, and water;
a process (II) of obtaining a fiber laminate by subjecting the slurry composition to papermaking; and
a process (III) of dehydrating the fiber laminate and thereafter drying the resultant,
wherein the process (I) includes:
a process (I-1) of beating a mixture containing the organic fiber and water,
a process (I-2) of mixing the mixture obtained in the process (I-1) and water, and
a process (I-3) of mixing the mixture obtained in the process (I-2) and the inorganic fiber,

the thermosetting resin is mixed in at least any of the process (I-1), the process (I-2), and the process (I-3),
the inorganic particles are mixed in at least any of the process (I-1), the process (I-2), and the process (I-3), and
an average fiber length of the inorganic fiber in the structure for producing a casting is 1 mm or longer and 5 mm or shorter.

13. A method of producing a structure for producing a casting according to claim 12 , the method including:
a process (I) of obtaining a slurry composition containing the organic fiber, the inorganic fiber, the inorganic particles, the thermosetting resin, and water;
a process (II) of obtaining the fiber laminate by subjecting the slurry composition to papermaking; and
a process (III) of dehydrating the fiber laminate and thereafter drying the resultant,
wherein the process (I) includes:
a process (I-1) of beating a mixture containing the organic fiber, the thermosetting resin, and water,
a process (I-2) of mixing the mixture obtained in the process (I-1) and water, and
a process (I-3) of mixing the mixture obtained in the process (I-2), the inorganic fiber, and the inorganic particles,

the average fiber length of the inorganic fiber in the structure for producing a casting is 1 mm or longer and 5 mm or shorter.

Assignees

• Kao Corp

Inventors

• Ikenaga Haruki

Classifications

• D21H15/02

  characterised by configuration · CPC title

• D21H21/18 Primary

  Reinforcing agents · CPC title

• D21H13/36

  Inorganic fibres or flakes · CPC title

• B22C9/02

  Sand moulds or like moulds for shaped castings · CPC title

• D21H17/63

  Inorganic compounds · CPC title