Steel material for nitriding and nitrided component

Patent metadata

Field	Value
Publication number	US-9718256-B2
Application number	US-201314386028-A
Country	US
Kind code	B2
Filing date	Feb 4, 2013
Priority date	Mar 22, 2012
Publication date	Aug 1, 2017
Grant date	Aug 1, 2017

Abstract

A steel material for nitriding has a composition comprising, by mass percent, C: more than 0.15% and not more than 0.35%, Si≦0.20%, Mn: 0.10 to 2.0%, P≦0.030%, S≦0.050%, Cr: 0.80 to 2.0%, V: 0.10 to 0.50%, Al: 0.01 to 0.06%, N≦0.0080%, O≦0.0030%, and optionally one or more elements of Mo, Cu, Ni, Ti, Nb, Zr, Pb, Ca, Bi, Te, Se and Sb, the balance being Fe and impurities. The composition satisfies the conditions of [20≦(669.3×log e C−1959.6×log e N−6983.3)×(0.067×Mo+0.147×V)≦80] and [140×Cr+125×Al+235×V≧160]. The microstructure is a ferritic-pearlitic structure, a ferritic-bainitic structure, or a ferritic-pearlitic-bainitic structure. The area fraction of ferrite is 20% or more and the precipitate content of V is 0.10% or less.

First claim

The invention claimed is:

1. A steel material for nitriding, having a chemical composition comprising, by mass percent, C: more than 0.15% and not more than 0.35%, Si: 0.20% or less, Mn: 0.10 to 2.0%, P: 0.030% or less, S: 0.050% or less, Cr: 0.80 to 2.0%, V: 0.10 to 0.50%, Al: 0.01 to 0.06%, N: 0.0080% or less, and O: 0.0030% or less, with the balance being Fe and impurities, and further the Fn1 expressed by the formula (1) described below is 20 to 80, and the Fn2 expressed by the formula (2) described below is 160 or more; wherein
a microstructure of the steel material is a ferritic-pearlitic structure, a ferritic-bainitic structure, or a ferritic-pearlitic-bainitic structure,
an area fraction of ferrite in the microstructure is 20% or more, and
a content of V in precipitates determined by an extraction residue analysis is 0.10% or less:
Fn 1=(669.3×log e C−1959.6×log e N−6983.3)×(0.067×Mo+0.147×V)  (1);

Fn 2=140×Cr+125×Al+235×V  (2);

where, each symbol C, N, Mo, V, Cr and Al in the above formulas (1) and (2) represents the content by mass percent of the element concerned.

2. A steel material for nitriding, having a chemical composition comprising, by mass percent, C: more than 0.15% and not more than 0.35%, Si: 0.20% or less, Mn: 0.10 to 2.0%, P: 0.030% or less, S: 0.050% or less, Cr: 0.80 to 2.0%, V: 0.10 to 0.50%, Al: 0.01 to 0.06%, N: 0.0080% or less, O: 0.0030% or less, and one or more kinds of elements selected from the items <a> to <d> described below with the balance being Fe and impurities, and further the Fn1 expressed by the formula (1) described below is 20 to 80, and the Fn2 expressed by the formula (2) described below is 160 or more; wherein
a microstructure of the steel material is a ferritic-pearlitic structure, a ferritic-bainitic structure, or a ferritic-pearlitic-bainitic structure,
an area fraction of ferrite in the microstructure is 20% or more, and
a content of V in precipitates determined by an extraction residue analysis is 0.10% or less:
Fn 1=(669.3×log e C−1959.6×log e N−6983.3)×(0.067×Mo+0.147×V)  (1);

Fn 2=140×Cr+125×Al+235×V  (2);

where, each symbol C, N, Mo, V, Cr and Al in the above formulas (1) and (2) represents the content by mass percent of the element concerned;
<a> Mo: less than 0.10%;
<b> Cu: 0.50% or less and Ni: 0.50% or less;
<c> Ti: 0.20% or less, Nb: 0.10% or less and Zr: 0.10% or less;
<d> Pb: 0.50% or less, Ca: 0.010% or less, Bi: 0.30% or less, Te: 0.30% or less, Se: 0.30% or less, and Sb: 0.30% or less.

3. A nitrided component having a chemical composition according to claim 1 , wherein a core hardness thereof is 180 or more in Vickers hardness, a surface hardness thereof is 650 or more in Vickers hardness, and an effective case depth thereof is 0.20 mm or more.

4. A nitrided component having a chemical composition according to claim 2 , wherein a core hardness thereof is 180 or more in Vickers hardness, a surface hardness thereof is 650 or more in Vickers hardness, and an effective case depth thereof is 0.20 mm or more.

Assignees

• Nippon Steel & Sumitomo Metal Corp

Inventors

• Gyotoku Yuya
• Horimoto Masayuki
• Imataka Hideki
• Tanaka Kosuke

Classifications

• C23C8/26 Primary

  of ferrous surfaces · CPC title

• Y02P10/212

  Cross-Sectional Technologies · mapped topic

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• C22C38/26

  with niobium or tantalum · CPC title

• C22C38/60

  containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur · CPC title