Method for preparing rotolined articles

Patent metadata

Field	Value
Publication number	US-9718090-B2
Application number	US-201414566774-A
Country	US
Kind code	B2
Filing date	Dec 11, 2014
Priority date	May 21, 2008
Publication date	Aug 1, 2017
Grant date	Aug 1, 2017

Abstract

Method for rotolining metallic hollow articles with metallocene-produced polyethylene.

First claim

The invention claimed is:

1. A method for preparing a rotolined article comprising:
providing a metallic hollow article comprising an iron containing alloy to be lined as a mold;
feeding an additional layer material into the mold to obtain a filled mold, wherein the additional layer material is selected from a group consisting of polyamide (PA), ethylene vinyl alcohol (EVOH), polypropylene (PP), polyethylene (PE), and combinations thereof;
placing the filled mold into a pre-heated oven;
rotating the filled mold about two perpendicular axes;
feeding an inner skin layer composition into the mold to obtain a filled mold, wherein the inner skin layer composition comprises a polyethylene-based resin consisting of a metallocene-produced homopolymer of ethylene, a metallocene-produced copolymer of ethylene, or mixtures thereof, in amounts ranging from 70 to 99.5 wt % based on a total weight of the inner skin layer composition; and a material selected from a group consisting of a functionalized polyolefin (FPO), an ionomer, a polyolefin (PO) grafted to a non-polyolefin (NPO) in the form of a block copolymer (PO)g-(NPO), and combinations thereof, in amounts ranging from 0.5 to 30 wt % based on the total weight of the inner skin layer;
placing the filled mold into a pre-heated oven;
rotating the filled mold about two perpendicular axes;
cooling the mold; and
retrieving the rotolined article, wherein the metallic hollow article forms an outer skin layer of the rotolined article, wherein the inner skin layer composition forms an inner skin layer of the rotolined article, wherein the additional layer material forms at least one additional layer of the rotolined article, wherein the at least one additional layer comprises a first additional layer that is positioned between the outer skin layer and the inner skin layer, and wherein the first additional layer is applied directly to the outer skin layer and the inner skin layer.

2. A method comprising:
feeding an additional layer composition into a metallic hollow article, wherein the additional layer composition comprises polypropylene, polyethylene, polyamide, or ethylene vinyl alcohol;
rotating the metallic hollow article in an oven about two perpendicular axes;
feeding an inner skin layer composition into the metallic hollow article, wherein the inner skin layer composition comprises a polyethylene-based resin comprising from 40 to 99.5 weight percent of metallocene-prepared homo- or co- polymer of ethylene or a mixture thereof, based on a total weight of the inner skin layer composition; and from 0.5 to 60 weight percent of a functionalized or grafted polyolefin (FPO), an ionomer, a polyolefin (PO) grafted to a non-polyolefin (NPO) in the form of a block copolymer (PO)g-(NPO), or combinations thereof, based on the total weight of the inner skin layer composition;
rotating the metallic hollow article in an oven about two perpendicular axes;
cooling the mold; and
retrieving a rotolined article, wherein the metallic hollow article forms an outer skin layer of the rotolined article, the inner skin layer composition forms an inner skin layer of the rotolined article, and the additional layer composition forms at least one additional layer of the rotolined article;
wherein the at least one additional layer comprises a first additional layer that is positioned between the outer skin layer and the inner skin layer, wherein the first additional layer is applied directly to the outer skin layer and the inner skin layer.

3. The method of claim 2 , wherein the oven is at a temperature ranging from 280 to 300° C.

4. The method of claim 2 , wherein the metallic hollow article is a pipe.

5. The method of claim 2 , wherein the metallic hollow article is a vessel.

6. The method of claim 2 , wherein the metallic hollow article comprises an iron containing alloy.

7. The method of claim 2 , wherein the metallic hollow article comprises steel.

8. The method of claim 2 , wherein the inner skin layer composition comprises at least 70 weight percent of the metallocene-prepared homo- or co- polymer of ethylene or the mixture thereof, based on the total weight of the inner skin layer composition.

9. The method of claim 2 , wherein the inner skin layer composition comprises from 0.5 to 30 weight percent of functionalized polyethylene, ionomer, or combinations thereof, based on the total weight of the inner skin layer composition.

10. The method of claim 2 , wherein the inner skin layer composition comprises the functionalized polyolefin, and wherein the functionalized polyolefin is a functionalized polypropylene.

11. The method of claim 2 , wherein the inner skin layer composition comprises the functionalized polyolefin, and wherein the functionalized polyolefin is a polyolefin grafted with anhydride.

12. The method of claim 2 , wherein the inner skin layer composition comprises the ionomer, and wherein the ionomer is poly(ethylene-co-methacrylic acid).

13. The method of claim 2 , wherein the inner skin layer composition comprises the ionomer, and wherein the ionomer is a sodium or zinc salt of a copolymer derived from ethylene and methacrylic acid.

14. The method of claim 2 , wherein the metallocene-prepared homo- or co-polymer of ethylene has a melt flow index (M12) of at least 0.5 dg/min. and at most 25 dg/min., measured following ASTM D 1238 at a temperature of 190° C. and a load of 2.16 kg.

15. The method of claim 2 , wherein the metallocene-prepared homo- or co-polymer of ethylene has a density of at least 0.920 g/cc and at most 0.965 g/cc, measured following ASTM D 1505 at 23° C.

16. The method of claim 2 , wherein the metallocene-prepared homo- or co-polymer of ethylene has a bimodal or multimodal molecular weight distribution.

17. The method of claim 2 , wherein the metallocene-prepared homo- or co-polymer of ethylene has polydispersity ranging from 2 to 20.

18. The method of claim 2 , wherein the at least one additional layer further comprises a second additional layer positioned on a side of the inner skin layer opposite to the outer skin layer.

19. A method comprising:
feeding an inner skin layer composition into a metallic hollow article having an additional layer formed thereon, wherein the additional layer is formed of a composition comprising polypropylene, polyethylene, polyamide, or ethylene vinyl alcohol, and wherein the inner skin layer composition comprises:
a polyethylene-based resin comprising from 40 to 99.5 weight percent of metallocene-prepared homo- or co- polymer of ethylene or a mixture thereof, based on a total weight of the inner skin layer composition; and from 0.5 to 60 weight percent of a functionalized or grafted polyolefin (FPO), an ionomer, a polyolefin (PO) grafted to a non-polyolefin (NPO) in the form of a block copolymer (PO)g-(NPO), or combinations thereof, based on the total weight of the inner skin layer composition;

rotating the metallic hollow article in the oven about two perpendicular axes;
cooling the mold; and
retrieving a rotolined article, wherein the metallic hollow article forms an outer skin layer of the rotolined article, wherein the inner skin layer composition forms an inner skin layer of the rotolined article, wherein the additional layer is positioned between the outer skin layer and the inner skin layer, and wherein the additional layer is applied directly to the outer skin layer and the inner skin layer.

Assignees

• Total Res & Technology Feluy

Inventors

• Maziers Eric

Classifications

• B32B27/08

  of synthetic resin · CPC title

• B32B27/306

  comprising vinyl acetate or vinyl alcohol (co)polymers · CPC title

• B32B2597/00

  Tubular articles, e.g. hoses, pipes · CPC title

• B32B2307/306

  Resistant to heat · CPC title

• B28B21/80

  adapted to centrifugal or rotational moulding · CPC title