Lithium-lanthanum-titanium oxide sintered material, solid electrolyte containing the oxide, and lithium air battery and all-solid lithium battery including the solid electrolyte

Patent metadata

Field	Value
Publication number	US-9711822-B2
Application number	US-201314396955-A
Country	US
Kind code	B2
Filing date	Apr 22, 2013
Priority date	Apr 25, 2012
Publication date	Jul 18, 2017
Grant date	Jul 18, 2017

Abstract

A lithium-lanthanum-titanium oxide sintered material has a lithium ion conductivity 3.0×10 −4 Scm −1 or more at a measuring temperature of 27° C., the material is described by one of general formulas (1−a)La x Li 2-3x TiO 3 -aSrTiO 3 , (1−a)La x Li 2-3x TiO 3 -aLa 0.5 K 0.5 TiO 3 , La x Li 2-3x Ti 1-a M a O 3-a , Sr x-1.5a La a Li 1.5-2x Ti 0.5 Ta 0.5 O 3 (0.55≦x≦0.59, 0≦a≦0.2, M=at least one of Fe or Ga), amount of Al contained is 0.35 mass % or less as Al 2 O 3 , amount of Si contained is 0.1 mass % or less as SiO 2 , and average particle diameter is 18 μm or more.

First claim

The invention claimed is:

1. A sintered material comprising:
a lithium lanthanum titanium oxide described by the general formula La 0.57 Li 0.29 TiO 3 ;
a nonzero amount of Al 2 O 3 ;
a nonzero amount of SiO 2 ; and
having an average particle diameter of 18 μm or more,
wherein the nonzero amount of Al 2 O 3 is 0.35 mass % or less,
wherein the nonzero amount of SiO 2 is 0.1 mass % or less,
and
wherein a tabular sample of the sintered material having a thickness (L) adhered between two sheets of filter paper and sandwiched between two electrodes provides a lithium ion conductivity calculated by the formula (Scm −1 )=1/(R b +R gb )×(L/S) between 3.0×10 −4 Scm −1 and 6.0×10 −4 , in condition in which an impedance analyzer is used,
wherein each sheet of filter paper contains a IM lithium chloride water solution
wherein the measuring frequency is 5 to 13 MHz,
wherein the measuring temperature is 27° C.,
wherein R b is resistance inside of particle (Ω),
wherein R gb is resistance at interface of particle (Ω),
wherein L is thickness of the tabular sample of the sintered material (cm), and
wherein S is a surface area of one of the two electrodes (cm 2 ).

2. A solid electrolyte comprising the sintered material according to claim 1 .

3. A lithium air battery comprising the solid electrolyte according to claim 2 .

4. The lithium air battery according to claim 3 comprising an anode active material layer, solid electrolyte and a cathode active material layer, wherein electrolytic solution is contained between the anode active material layer and the solid electrolyte, and between the cathode active material layer and the solid electrolyte.

5. An all-solid lithium ion battery comprising the solid electrolyte according to claim 2 .

Assignees

• Toho Titanium Co Ltd
• Nakashima Sangyo Co Ltd
• The Gakushuin School Corp

Inventors

• Nakashima Mamoru
• Inaguma Yoshiyuki
• Nakashima Mikio

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• C04B2235/3201

  Alkali metal oxides or oxide-forming salts thereof · CPC title

• C01G49/0054

  containing one rare earth metal, yttrium or scandium · CPC title

• C04B2235/81

  Materials characterised by the absence of phases other than the main phase, i.e. single phase materials · CPC title

• C04B2235/786

  Micrometer sized grains, i.e. from 1 to 100 micron · CPC title