Transmission belt

Patent metadata

Field	Value
Publication number	US-9709129-B2
Application number	US-201514590744-A
Country	US
Kind code	B2
Filing date	Jan 6, 2015
Priority date	Jul 6, 2012
Publication date	Jul 18, 2017
Grant date	Jul 18, 2017

Abstract

At least part of a belt body of a transmission belt contacting a cord is made of a rubber composition containing ethylene-α-olefin elastomer as a rubber component and formed in such a manner that the rubber component is mixed with α,β-unsaturated fatty acid metallic salt and then is crosslinked using sulfur.

First claim

What is claimed is:

1. A transmission belt comprising:
a cord embedded in a belt body made of a rubber composition,
wherein at least part of the belt body contacting the cord is made of a rubber composition containing ethylene-α-olefin elastomer as a rubber component and formed in such a manner that the rubber component is mixed with silica, carbon black and an α,β-unsaturated fatty acid metallic salt and then is crosslinked using sulfur,
wherein a content of the sulfur is 2 to 4 parts by mass with respect to 100 parts by mass of the rubber component, a content of the silica is 30 to 90 parts by mass with respect to 100 parts by mass of the rubber component, a content of the carbon black is 10 to 55 parts by mass with respect to 100 parts by mass of the rubber component and a content of the α,β-unsaturated fatty acid metallic salt is 0.5 to 5 parts by mass with respect to 100 parts by mass of the rubber component, and
wherein a sum of the content of the carbon black and the silica is 70 to 100 parts by mass with respect to 100 parts by mass of the rubber component.

2. The transmission belt of claim 1 , wherein the α,β-unsaturated fatty acid metallic salt is zinc dimethacrylate.

3. The transmission belt of claim 1 , wherein
a content of the silica is equal to or greater than 75% by mass with respect to a content of the carbon black.

4. The transmission belt of claim 1 , wherein the carbon black is FEF carbon black.

5. The transmission belt of claim 1 , wherein a BET adsorption specific surface area of the silica is 50 to 200 cm2/g.

6. The transmission belt of claim 1 , wherein
a complex modulus of the rubber composition is 20 to 30 MPa measured under conditions of a temperature atmosphere of 120° C., a tension mode, a frequency of 10 Hz, a dynamic strain of 1.0%, and a static load of 0.294 MPa, according to JIS K6394.

7. The transmission belt of claim 1 , wherein the belt body is a V-ribbed belt body or a flat belt body.

8. The transmission belt of claim 1 , wherein the content of the sulfur is 2.5 to 4 parts by mass with respect to 100 parts by mass of the rubber component.

9. The transmission belt of claim 1 , wherein a ratio by mass of the silica to the carbon black is in a range from 75 to 900.

Assignees

• Bando Chemical Ind

Inventors

• Matsuda Hisashi

Classifications

• F16G1/21 Primary

  built-up from superimposed layers, e.g. zig-zag folded · CPC title

• F16G5/06 Primary

  with reinforcement bonded by the rubber · CPC title

• F16G5/20

  with a contact surface of special shape, e.g. toothed · CPC title

• F16G5/10

  with metal reinforcement · CPC title

• B29D29/103 Primary

  Multi-ribbed driving belts · CPC title