Cutting tool

Patent metadata

Field	Value
Publication number	US-9694426-B2
Application number	US-201314769989-A
Country	US
Kind code	B2
Filing date	Nov 29, 2013
Priority date	Feb 27, 2013
Publication date	Jul 4, 2017
Grant date	Jul 4, 2017

Abstract

There is provided a cutting tool having high wear resistance and fracture resistance by reducing the occurrence of thermal cracking on a cutting edge even during a cutting process of a heat-resistant alloy in which the cutting edge reaches high temperatures. The cutting tool is made from a cemented carbide that is composed mainly of a WC phase and contains 11.5-12.5% by mass of Co and 0.2-0.6% by mass of Cr in terms of Cr 3 C 2 . The WC phase has a mean particle size of 0.85-1.05 μm, an antimagnetic force (Hc) of 13.0-16.0 kA/m, and a Rockwell hardness (HRA) of 89.5-90.5.

First claim

The invention claimed is:

1. A cutting tool comprising:
a cemented carbide that is composed mainly of a WC phase and contains 11.5-12.5% by mass of Co and 0.2-0.6% by mass of Cr in terms of Cr 3 C 2 , wherein
the WC phase has a mean particle size of 0.85-1.05 μm,
the cemented carbide has an antimagnetic force (Hc) of 13.0-16.0 kA/m, and a Rockwell hardness (HRA) of 89.5-90.5,
the Co exists in a bonding phase that establishes a bond between the WC phases,
tungsten (W) is contained in the bonding phase, and
a content ratio of the tungsten reaches a maximum value at a location which lies at depths in a range of 50-200 μm from a surface of the cemented carbide.

2. The cutting tool according to claim 1 , wherein a deflective strength is 3.5 GPa or more, and a Weibull coefficient is 10 or more.

3. The cutting tool according to claim 1 , wherein saturation magnetization (Ms) is 165-200 kA/m, and a fracture toughness value (K 1C ) is 16 MPa·m 1/2 or more.

4. The cutting tool according to claim 1 , wherein the surface of the cemented carbide is coated with a coating layer.

5. The cutting tool according to claim 4 , wherein the cemented carbide has on the surface a TiN layer having a mean thickness of 0-0.7 μm, a TiCN layer having a mean thickness of 1-3 μm, an intermediate layer having a mean thickness of 0-0.1 μm and being composed of any one of TiCO, TiNO, and TiCNO, an Al 2 O 3 layer having a mean thickness of 0.3-0.7 μm, and an outermost layer made of a TiC x N y layer (0<x, 0.5≦y, and x+y=1) having a mean thickness of 0-0.7 μm, these layers being laminated in sequence from a substrate side.

6. The cutting tool according to claim 4 , wherein the surface of the cemented carbide is coated with a coating layer having a mean thickness of 3.0-5.5 μm and being composed of Ti 1-a-b Al a M b (C 1-x N x ) (M is at least one kind selected from Cr, Si, W, Mo, Ta, Hf, Nb, Zr, and Y, 0.2≦a≦0.7, 0≦b≦0.4, and 0≦x≦1).

7. The cutting tool according to claim 6 , wherein the coating layer comprises a multilayer structure made by alternately laminating a first thin layer composed of Ti 1-a1-b1 Al a1 M b1 (C 1-x1 N x1 ) (M is at least one kind selected from Cr, Si, W, Mo, Ta, Hf, Nb, Zr, and Y, 0.2≦a1≦0.7, 0≦b1≦0.4, and 0≦x1≦1), and a second thin layer composed of Ti 1-a2-b2 Al a2 M b2 (C 1-x2 N x2 ) (M is at least one kind selected from Cr, Si, W, Mo, Ta, Hf, Nb, Zr, and Y, 0.2≦a2≦0.7, 0≦b2≦0.4, 0≦x2≦1, except for a1=a2, b1=b2, and x1=x2).

Assignees

• Kyocera Corp

Inventors

• Makino Takahiko

Classifications

• B23B2222/28

  Details of hard metal, i.e. cemented carbide · CPC title

• C22C29/02

  based on carbides or carbonitrides · CPC title

• C23C30/005

  on hard metal substrates · CPC title

• B22F2207/03

  of the metallic binder phase in cermets · CPC title

• B23B2228/105

  with specified thickness · CPC title