High-strength hot-rolled steel sheet

Patent metadata

Field	Value
Publication number	US-9689060-B2
Application number	US-201214237286-A
Country	US
Kind code	B2
Filing date	Aug 15, 2012
Priority date	Aug 17, 2011
Publication date	Jun 27, 2017
Grant date	Jun 27, 2017

Abstract

This high-strength hot-rolled steel plate contains specific amounts of C, Si, Mn, Al, V and also Ti and/or Nb so as to fulfill C−12(V/51+Ti/48+Nb/93)>0.03, and the rest consists of iron and unavoidable impurities. Ferrite is the main microstructure, the remaining microstructure is one or more selected from the group consisting of bainite, martensite and retained austenite, wherein the average particle diameter of precipitated carbides (the total content of V, Ti and Nb is 0.02% or greater) in the ferrite is less than 6 nm.

First claim

The invention claimed is:

1. A high-strength hot-rolled steel sheet, comprising, by mass %:
C: 0.05 to 0.20%;
Si: 0.5 to 1.7%;
Mn: 1.0 to 2.5%;
Al: 0.001 to 0.10%;
V: 0.0005 to 0.10%; and
one component selected from the group consisting of Ti, Nb, and mixtures thereof, in the following amounts: Ti: 0.05 to 0.20%; Nb: 0.02 to 0.20%; and mixtures thereof comprising 0.05 to 0.20% Ti and 0.02 to 0.20% Nb;
with the remaining mass % comprising iron; and inevitable impurities;
wherein:
the steel sheet has a tensile strength of 786 MPa or more;
the steel sheet has a microstructure comprising, by area ratio based on the total microstructure:
ferrite: 50 to 90%;
bainite: 10 to 50%; and
martensite+retained austenite: less than 10%;
an average particle size of precipitated carbides present in the ferrite is less than 6 nm;
a total content of V, Ti, and Nb forming the precipitated carbides is 0.02% or more; and
the steel sheet satisfies the following Expression 1:
C−12×(V/51+Ti/48+Nb/93)>0.03,

where element symbols in the Expression 1 correspond to mass %.

2. The steel sheet according to claim 1 , wherein the microstructure in the steel sheet comprises, by area ratio based on the total microstructure:
ferrite: 60 to 80%;
bainite: 20 to 40%; and
martensite+retained austenite: less than 10%.

3. The steel sheet according to claim 1 , wherein an average particle size of the bainite is more than 5 μm.

4. The steel sheet according to claim 1 , further comprising in mass % one or more of:
Cu: 0.01 to 1.0%;
Ni: 0.01 to 1.0%;
Cr: 0.01 to 1.0%; and
Mo: 0.01 to 1.0%.

5. The steel sheet according to claim 2 , further comprising in mass % one or more of:
Cu: 0.01 to 1.0%;
Ni: 0.01 to 1.0%;
Cr: 0.01 to 1.0%; and
Mo: 0.01 to 1.0%.

6. The steel sheet according to claim 3 , further comprising in mass % one or more of:
Cu: 0.01 to 1.0%;
Ni: 0.01 to 1.0%;
Cr: 0.01 to 1.0%; and
Mo: 0.01 to 1.0%.

7. The steel sheet according to claim 1 , wherein the Si content in the high-strength hot-rolled steel sheet is 0.9 to 1.7 mass %.

8. The steel sheet according to claim 1 , wherein the Si content in the high-strength hot-rolled steel sheet is more than 0.5 to 1.7 mass %.

Assignees

• Murakami Toshio
• Kinefuchi Masao
• Hata Hideo
• Kobe Steel Ltd

Inventors

• Murakami Toshio
• Kinefuchi Masao
• Hata Hideo

Classifications

• C22C38/16

  containing copper · CPC title

• C22C38/14

  containing titanium or zirconium · CPC title

• C22C38/001

  containing N · CPC title

• C22C38/02

  containing silicon · CPC title

• C21D2211/002

  Bainite · CPC title