Abstract

A coating composition having a solids content of greater than 70% by weight and/or a Volatile Organic Content (VOC) of less than 250 g/l, comprising a novel polyester polyol and a curing agent, wherein the coating composition is capable of curing at ambient temperature, and which provides a coating having excellent durability.

First claim

The invention claimed is:

1. A coating composition having at least one of a solids content of greater than 70% by weight and a Volatile Organic Content (VOC) of less than 250 g/l, comprising a polyester polyol, the polyester polyol prepared from reactants comprising:
a) from 10 to 40 weight percent of one or more polyols comprising 3 or more hydroxyl groups per molecule,
b) from 10 to 40 weight percent of one or more aromatic polycarboxylic acids comprising 2 or more acid groups per molecule or corresponding ester(s) and/or anhydride(s) thereof, and
c) from 30 to 75 weight percent of one or a mixture of C 6 -C 20 monobasic fatty acids, wherein the one or the mixture of C 6 -C 20 monobasic fatty acids have an iodine value of less than 30 cg/g and is a liquid in conformity with ASTM (1996) D4359-90,

wherein the polyester polyol has a hydroxyl value (OHV) of greater than 60 and less than 200 mgKOH/g, and the weight percent of each component (a), (b) or (c) is the percentage of the weight of that component to the total weight of (a)+(b)+(c),
and at least one isocyanate-functional curing agent, and
wherein the coating composition is capable of curing at ambient temperature.

2. The coating composition of claim 1 , wherein the polyester polyol is prepared from reactants comprising:
from 10 to 40 weight percent of component (a),
from 10 to 30 weight percent of component (b), and
from 35 to 75 weight percent of component (c) wherein the weight percent of each component (a), (b) or (c) is the percentage of the weight of that component to the total weight of (a)+(b)+(c).

3. The coating composition of claim 1 wherein the polyester polyol is prepared from reactants comprising:
from 17 to 30 weight percent of component (a),
from 14 to 25 weight percent of component (b), and
from 46 to 67 weight percent of component (c)
wherein the weight percent of each component (a), (b) or (c) is the percentage of the weight of that component to the total weight of (a)+(b)+(c).

4. The coating composition of claim 1 , wherein the one or more polyols comprising 3 or more hydroxyl groups is pentaerythritol.

5. The coating composition of claim 1 , wherein the one or the mixture of C 6 -C 20 monobasic fatty acids is one or a mixture of C 6 -C 14 fatty acids, or one or a mixture of C 8 -C 10 fatty acids, wherein the one or the mixture of C 6 -C 20 monobasic fatty acids have an iodine value of less than 30 cg/g.

6. The coating composition of claim 1 , wherein the one or more aromatic polycarboxylic acids comprises one or a mixture of isophthalic acid, terephthalic acid and phthalic acid.

7. The coating composition of claim 1 , wherein at least 50 mole % of the one or more aromatic polycarboxylic acids is isophthalic acid.

8. The coating composition of claim 1 , wherein the polyester polyol has a number average molecular weight (Mn) ranging from 1000 to 5000.

9. The coating composition of claim 1 , wherein the polyester polyol has a number average molecular weight (Mn) ranging from 1500 to 2500.

10. The coating composition of claim 1 having a viscosity in the range of 1 to 20 poise at 25° C.

11. The coating composition of claim 1 , wherein the stoichiometric ratio of isocyanate groups: hydroxyl groups ranges from 0.5:1 to 3:1.

12. A substrate coated with the coating composition of claim 1 .

13. A method of coating a substrate, the method comprising applying the coating composition of claim 1 to a substrate and allowing the coating composition to cure at an ambient temperature to form a coating layer on the substrate.

14. The coating composition of claim 1 , in the form of a two-pack composition, one pack comprising the curing agent and the other pack comprising the polyester polyol.

15. The coating composition of claim 3 , wherein the one or more polyols comprising 3 or more hydroxyl groups is pentaerythritol.

16. The coating composition of claim 3 , wherein the one or the mixture of C 6 -C 20 monobasic fatty acids is one or a mixture of C 6 -C 14 fatty acids, or one or a mixture of C 8 -C 10 fatty acids, wherein the one or the mixture of C 6 -C 20 monobasic fatty acids have an iodine value of less than 30 cg/g.

17. The coating composition of claim 3 , wherein the one or more aromatic polycarboxylic acids comprises one or a mixture of isophthalic acid, terephthalic acid and phthalic acid.

18. The coating composition of claim 3 , wherein at least 50 mole % of the one or more aromatic polycarboxylic acids is isophthalic acid.

19. The coating composition of claim 3 , wherein the polyester polyol has a number average molecular weight (Mn) ranging from 1500 to 2500.

20. The coating composition of claim 3 having a viscosity in the range of 1 to 20 poise at 25° C.

Assignees

• Akzo Nobel Coatings Int Bv
• Akzo Nobel Coating Int B V

Inventors

• Nixon Steven Alister
• Pritchard Susan

Classifications

• C09D167/08 Primary

  Polyesters modified with higher fatty oils or their acids, or with natural resins or resin acids · CPC title

• C08G18/4288

  modified by higher fatty oils or their acids or by resin acids · CPC title

• C09D175/06

  from polyesters · CPC title

• C08L67/08 Primary

  Polyesters modified with higher fatty oils or their acids, or with resins or resin acids · CPC title

• C09D175/04 Primary

  Polyurethanes · CPC title