Abstract

A method for casting an internal feature within an object is provided. An internal mold is formed from a mold powder, comprising a base powder and an acid powder mixed into the base powder. A molten material is cast around the internal mold. The molten material is solidified. The internal mold is reacted with water, wherein the reacting causes the acid powder to neutralize the base powder.

First claim

What is claimed is:

1. A method for casting an internal feature within an object, comprising:
forming an internal mold from a mold powder, comprising:
a base powder; and
an acid powder mixed into the base powder;

casting a molten material around the internal mold;
solidifying the molten material; and
reacting the internal mold with water, wherein the reacting causes the acid powder to neutralize the base powder.

2. The method, as recited in claim 1 , wherein the acid powder and the base powder are inorganic, in that the acid powder and the base powder do not have any carbon hydrogen bonds.

3. The method, as recited in claim 2 , wherein the base powder is a bicarbonate salt.

4. The method, as recited in claim 3 , wherein the acid powder is boric acid.

5. The method, as recited in claim 4 , wherein the base powder is sodium bicarbonate.

6. The method, as recited in claim 1 , wherein the forming the internal mold comprises pressing the mold powder into a mold shape.

7. The method, as recited in claim 1 , wherein the forming the internal mold comprises 3D printing the mold powder into a mold shape.

8. The method, as recited in claim 1 , wherein the forming the internal mold comprises placing the powder in a backbone structure, and wherein the casting the molten material around the internal mold casts the molten material around the backbone structure.

9. The method, as recited in claim 8 , wherein the backbone structure comprises aluminum and wherein the molten material comprises aluminum.

10. The method, as recited in claim 1 , wherein the mold powder is completely soluble in water.

11. The method, as recited in claim 1 , wherein the mold powder consists essentially of acid powder and base powder.

12. The method, as recited in claim 11 , wherein the base powder is a bicarbonate salt.

13. The method, as recited in claim 12 , wherein the acid powder is boric acid.

14. The method, as recited in claim 13 , the ratio of the acid powder to base powder is from 2:1 to 1:2.

15. The method, as recited in claim 1 , wherein the reacting the internal mold with water comprises reacting the internal mold with water at a temperature of at least 20° C.

16. A method for casting an internal feature within an object, comprising:
forming an internal mold from a mold powder, consisting essentially of:
an inorganic base powder; and
an inorganic acid powder mixed into the base powder;

casting a molten material around the internal mold;
solidifying the molten material; and
reacting the internal mold with water at a temperature of at least 20° C., wherein the reacting causes the acid powder to neutralize the base powder.

Assignees

• Lam Res Corp
• Law Res Corp

Inventors

• Sharpless Leonard

Classifications

• B33Y10/00

  Processes of additive manufacturing · CPC title

• B22C1/18

  of inorganic agents {(B22C1/162 takes precedence)} · CPC title

• B22C9/24 Primary

  for hollow articles · CPC title

• B22C9/105

  Salt cores · CPC title

• B22D21/04

  Casting aluminium or magnesium {(no material; see B22D21/007)} · CPC title