Structural polyurethane adhesive

Patent metadata

Field	Value
Publication number	US-9683152-B2
Application number	US-201314423442-A
Country	US
Kind code	B2
Filing date	Aug 20, 2013
Priority date	Aug 24, 2012
Publication date	Jun 20, 2017
Grant date	Jun 20, 2017

Abstract

A two-component polyurethane adhesive is described. The polyurethane adhesive has high strength and extensibility, wherein the mechanical properties are only slightly dependent on the temperature. The polyurethane adhesive is suitable as a structural adhesive that is decomposed by heating in such a way that adhesive bonds can be undone in a temperature range of interest. The adhesive can include a triol, a diol, an alkoxylated aromatic diol, a polyamine, a polyisocyanate, and a polyurethane polymer having isocayanate groups in certain ratios.

First claim

The invention claimed is:

1. A polyurethane adhesive comprising a first and a second component, wherein
the first component consists essentially of:
a) at least one triol A1 having a molecular weight in the range of 1,000 g/mol to 10,000 g/mol,
b) at least one diol A2 having two primary hydroxyl groups and a molecular weight in the range of 60 g/mol to 150 g/mol, and
c) at least one alkoxylated aromatic diol A3 having a molecular weight in the range of 300 g/mol to 1,000 g/mol; and
d) at least one aliphatic polyamine A4 having a molecular weight in the range of 60 g/mol to 500 g/mol; and

the second component comprises:
e) at least one polyisocyanate B1 and
f) at least one polyurethane polymer B2 having isocyanate groups;

wherein the triol A1, the diol A2 and the alkoxylated diol A3 are present in such an amount that
g) the weight ratio A1/(A2+A3)≦10,
h) the weight ratio A1/A2≦15, and
i) the weight ratio A2/A3 is in the range of 0.5 to 7.5.

2. The polyurethane adhesive according to claim 1 , wherein the triol A1 is a polyether triol.

3. The polyurethane adhesive according to claim 1 , wherein the triol A1 has primary hydroxyl groups.

4. The polyurethane adhesive according to claim 1 , wherein the diol A2 is selected from the group consisting of 1,3-propanediol, 1,4-butanediol and 1,5-pentanediol.

5. The polyurethane adhesive according to claim 1 , wherein the alkoxylated aromatic diol A3 is an ethoxylated and/or propoxylated and/or butoxylated aromatic diol.

6. The polyurethane adhesive according to claim 5 , wherein the alkoxylated aromatic diol A3 is a propoxylated bisphenol A or a propoxylated bisphenol F.

7. The polyurethane adhesive according to claim 1 , wherein the polyamine A4 is selected from the group consisting of 1,5-diamino-2-methylpentane, 2,2,4- and 2,4,4-trimethylhexamethylene diamine, 1,8-octanediamine, 1,10-decanediamine, 1,12-dodecanediamine, 1-amino-3-aminomethyl-3,5,5-trimethylcyclohexane, 2- and 4-methyl-1,3-diaminocyclohexane and mixtures thereof, 1,3-bis(aminomethyl)cyclohexane, 1,4-bis(aminomethyl)cyclohexane, 2,5(2,6)-bis(aminomethyl)bicyclo[2,2,1]heptane, 3(4),8(9)-bis(aminomethyl)tricyclo[5.2.1.0 2,6 ]decane, bis(2-aminoethyl)ether, 3,6-dioxaoctane-1,8-diamine, 4,7-dioxadecane-1,10-diamine, 4,7-dioxadecane-2,9-diamine, 4,9-dioxadodecane-1,12-diamine, 5,8-dioxadodecane-3,10-diamine, 1,3-bis(aminomethyl)benzene and 1,4-bis(aminomethyl)benzene.

8. The polyurethane adhesive according to claim 1 , wherein the weight ratio A1/(A2+A3) is in the range of 3 to 10.

9. The polyurethane adhesive according to claim 1 , wherein the weight ratio A1/A2 is in the range of 5 to 10.

10. The polyurethane adhesive according to claim 1 , wherein the polyisocyanate B1 is a form of 4,4′-, 2,4′- and 2,2′-diphenylmethane diisocyanate that is liquid at room temperature and arbitrary mixtures of these isomers (MDI) in the form of polymeric MDI or MDI having fractions of oligomers or derivatives.

11. The polyurethane adhesive according to claim 1 , wherein the urethane groups and the free isocyanate groups of the polyurethane polymer B2 are derived from 4,4′-diphenylmethane diisocyanate.

12. A method for bonding a first substrate to a second substrate, the method comprising the following steps:
mixing of the two components of a polyurethane adhesive according to claim 1 ,
applying the mixed polyurethane adhesive to at least one of the substrate surfaces to be bonded,
joining the substrates to be bonded within the open time, and
curing the polyurethane adhesive.

13. The method according to claim 12 , wherein one substrate is, or both substrates are, a metal or a ceramic or a glass fiber-reinforced plastic material or a carbon fiber-reinforced plastic material.

14. An article obtained from the method for bonding according to claim 12 .

Assignees

• Sika Tech Ag

Inventors

• Kelch Steffen
• Roock Wolfgang
• Ittrich Florian

Classifications

• C08G18/4879

  containing aromatic groups · CPC title

• C09J175/04

  Polyurethanes · CPC title

• C08G18/4829 Primary

  Polyethers containing at least three hydroxy groups (C08G18/4833 - C08G18/5096 take precedence) · CPC title

• C08G18/3206

  aliphatic · CPC title

• C08G18/10

  Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step · CPC title