Absorbent fabric made from hygro yarns

Patent metadata

Field	Value
Publication number	US-9677202-B2
Application number	US-201414529171-A
Country	US
Kind code	B2
Filing date	Oct 31, 2014
Priority date	Oct 17, 2005
Publication date	Jun 13, 2017
Grant date	Jun 13, 2017

Abstract

A process is described wherein pile yarn is woven with cotton weft and warp yarns to produce terry fabrics, such as towels. The fabric is then washed in warm water to dissolve the PVA fibers. The amount of fibers dissolved, depends upon the count of the yarn or yarns used. By dissolving the PVA fibers, a hollow air space is produced throughout the pile yarn, corresponding to an increase in the air space in the pile yarn. By increasing the air space in the pile yarn, the resulting towels are softer and bulkier than standard cotton towels. The present invention further relates to pile yarn in terry woven fabric (warp yarn), or weft yarn, in the case of flat fabrics.

First claim

I claim:

1. A method for making an absorbent fabric, comprising:
(a) forming a plurality of slivers comprising,
(i) a first sliver made from one of cotton; blends of polyester and cotton; blends of polyester and viscose; blends of cotton and modal; blends of cotton; silk and modal; blends of cotton and bamboo; blends of cotton and sea weed fibers; blends of cotton and silver fibers; blends of cotton and charcoal fibers; and any combination thereof, and
(ii) a water-soluble sliver made from water-soluble fibers;

(b) forming a roving from the plurality of slivers, comprising forming a twist in the roving by wrapping the plurality of slivers such that the water-soluble sliver forms a core of the roving, and such that a sheath is formed around the core, the sheath comprising the first sliver;
(c) spinning the roving into a yarn; and
(d) using the yarn to form the absorbent fabric, including dissolving the water-soluble fibers from the water-soluble sliver of the yarn to provide space within the yarn itself for absorbing water.

2. The method of claim 1 , wherein the spinning of the roving is performed using a ring spinning frame.

3. The method of claim 1 , wherein the forming of the roving is performed using a speed frame.

4. The method of claim 3 , wherein the forming of the twist in the roving is performed using the speed frame.

5. The method of claim 1 , wherein the forming of the twist comprises forming a Z or S twist in the roving.

6. The method of claim 1 , wherein the first sliver comprises cotton fibers, and wherein the method further comprises forming the first sliver by carding the cotton fibers and drawing the cotton fibers on a draw frame.

7. The method of claim 1 , further comprising forming the water-soluble sliver by carding polyvinyl alcohol (PVA) fibers and drawing the PVA fibers on a draw frame.

8. The method of claim 1 , wherein, prior to dissolving the water-soluble fibers, only the water-soluble fibers from the water-soluble sliver define the core of the yarn.

9. The method of claim 8 , wherein the yarn includes a Z or S twist.

10. The method of claim 8 , wherein the first sliver comprises cotton fibers, and wherein the water-soluble fibers comprise polyvinyl alcohol (PVA) fibers.

11. The method of claim 8 , wherein the PVA fibers are present in an amount of between about 8% to about 25% by weight of the yarn after performing the spinning of said step (d).

12. The method of claim 1 , wherein the water-soluble fibers are dissolved in water at a temperature from about 50° C. to about 110° C.

13. The method of claim 1 , wherein the yarn includes a Z or S twist, and wherein a hollow core defined throughout the yarn resulting from and characteristic of the PVA fibers from the water-soluble sliver having been dissolved.

14. The method of claim 13 , wherein the fabric comprises a towel.

15. The method of claim 13 , wherein the fabric comprises an undergarment.

16. The method of claim 13 , wherein the fabric comprises a sweater.

17. The method of claim 13 , wherein the fabric comprises a baby article.

18. The method of claim 13 , wherein the fabric comprises a table cloth.

19. A method for making an absorbent fabric, comprising:
(a) forming a plurality of slivers comprising,
(i) a water-soluble sliver made from water-soluble fibers, and
(ii) a second sliver comprised of at least one of cotton; cotton blends; silk fibers; modal fibers; acrylic fibers; blends of cotton and bamboo; blends of cotton and sea weed fibers; blends of cotton and silver fibers; and blends of cotton and charcoal fibers;

(b) forming a roving from the plurality of slivers, comprising forming a twist in the roving by wrapping the plurality of slivers such that the water-soluble sliver forms a core of the roving, and such that the second sliver forms a sheath around the core;
(c) spinning the roving into a yarn; and
(d) using the pile yarn to form the absorbent fabric, including dissolving the water-soluble fibers from the water-soluble sliver of the pile yarn to provide space within the pile yarn itself for absorbing water.

20. A method for making an absorbent fabric, comprising:
(a) forming a plurality of slivers comprising,
(i) a water-soluble sliver made from water-soluble fibers, and
(ii) a second sliver comprised of at least one of cotton; blends of polyester and cotton; blends of polyester and viscose; blends of cotton and modal; blends of cotton; silk and modal; blends of cotton and bamboo; blends of cotton and sea weed fibers; blends of cotton and silver fibers; and blends of cotton and charcoal fibers;

(b) forming a roving from the plurality of slivers, comprising forming a twist in the roving by wrapping the plurality of slivers such that the water-soluble sliver forms a core of the roving, and such that the second sliver forms a sheath around the core;
(c) spinning the roving into a yarn; and
(d) using the yarn as a weft yarn or a warp yarn to form the absorbent fabric, including dissolving the water-soluble fibers from the water-soluble sliver of the yarn to provide space within the yarn itself for absorbing water.

Assignees

• Welspun India Ltd

Inventors

• Mandawewala Rajesh R

Classifications

• D03D27/00

  Woven pile fabrics · CPC title

• B32B5/26

  another layer {next to it} also being fibrous or filamentary {(relative arrangement of fibres or filaments of different layers B32B5/12)} · CPC title

• D06C19/00

  Breaking or softening of fabrics (by stretching D06C3/00; by calendering, pressing, or beetling D06C15/00; by fulling D06C17/00) · CPC title

• D10B2503/00

  Domestic or personal · CPC title

• Y10T442/3073

  Strand material is core-spun [not sheath-core bicomponent strand] · CPC title