Methods of producing three-dimensional objects from materials having multiple mechanisms of hardening

Patent metadata

Field	Value
Publication number	US-9676963-B2
Application number	US-201514977822-A
Country	US
Kind code	B2
Filing date	Dec 22, 2015
Priority date	Jun 23, 2014
Publication date	Jun 13, 2017
Grant date	Jun 13, 2017

Abstract

A method of forming a three-dimensional object is carried out by: (a) providing a carrier and an optically transparent member having a build surface, the carrier and the build surface defining a build region therebetween; (b) filling the build region with a polymerizable liquid, the polymerizable liquid including a mixture of (i) a light polymerizable liquid first component, and (ii) a second solidifiable component that is different from the first component; (c) irradiating the build region with light through the optically transparent member to form a solid polymer scaffold from the first component and also advancing the carrier away from the build surface to form a three-dimensional intermediate having the same shape as, or a shape to be imparted to, the three-dimensional object, and containing the second solidifiable component carried in the scaffold in unsolidified and/or uncured form; and (d) concurrently with or subsequent to the irradiating step, solidifying and/or curing the second solidifiable component in the three-dimensional intermediate to form the three-dimensional object.

First claim

We claim:

1. A method of forming a three-dimensional object, comprising:
(a) providing a carrier and an optically transparent member having a build surface, said carrier and said build surface defining a build region therebetween;
(b) filling said build region with a polymerizable liquid, said polymerizable liquid comprising a mixture of (i) a light polymerizable liquid first component, and (ii) a second solidifiable component that is different from said first component;
(c) irradiating said build region with light through said optically transparent member to form a solid polymer scaffold from said first component and also advancing said carrier away from said build surface to form a three-dimensional intermediate having the same shape as, or a shape to be imparted to, said three-dimensional object and containing said second solidifiable component carried in said scaffold in unsolidified and/or uncured form; and
(d) subsequent to said irradiating step, heating, microwave irradiating, or both heating and microwave irradiating, said second solidifiable component in said three-dimensional intermediate to form said three-dimensional object.

2. The method of claim 1 , wherein said second component comprises a polymerizable liquid solubilized in or suspended in said first component.

3. The method of claim 1 , wherein said second component comprises:
(i) a polymerizable solid suspended in said first component;
(ii) a polymerizable solid solubilized in said first component; or
(iii) a polymer solubilized in said first component.

4. The method of claim 1 , wherein said three-dimensional intermediate is collapsible or compressible.

5. The method of claim 1 , wherein said three-dimensional object comprises a polymer blend, interpenetrating polymer network, semi-interpenetrating polymer network, or sequential interpenetrating polymer network formed from said first component and said second component.

6. The method of claim 1 , wherein said polymerizable liquid comprises:
from 1 percent by weight to 99 percent by weight of said first component; and
from 1 percent by weight to 99 percent by weight of said second component.

7. The method of claim 1 , wherein said step (d) is carried out by:
heating said second solidifiable component.

8. The method of claim 1 , wherein: said second component comprises the precursors to a polyurethane, polyurea, or copolymer thereof, a silicone resin, an epoxy resin, a cyanate ester resin, or a natural rubber; and said solidifying step is carried out by heating.

9. A method of forming a three-dimensional object, comprising:
(a) providing a carrier and an optically transparent member having a build surface, said carrier and said build surface defining a build region therebetween;
(b) filling said build region with a polymerizable liquid, said polymerizable liquid comprising a mixture of (i) a light polymerizable liquid first component, and (ii) a second solidifiable component that is different from said first component;
(c) irradiating said build region with light through said optically transparent member to form a solid polymer scaffold from said first component and also advancing said carrier away from said build surface to form a three-dimensional intermediate having the same shape as, or a shape to be imparted to, said three-dimensional object and containing said second solidifiable component carried in said scaffold in unsolidified and/or uncured form; and
(d) subsequent to said irradiating step, heating, microwave irradiating, or both heating and microwave irradiating, said second solidifiable component in said three-dimensional intermediate under conditions in which said solid polymer scaffold degrades and forms a constituent necessary for the polymerization of said second component, to form said three-dimensional object.

10. The method of claim 1 , wherein said irradiating and said advancing steps are carried out while also concurrently:
(i) continuously maintaining a dead zone of polymerizable liquid in contact with said build surface, and
(ii) continuously maintaining a gradient of polymerization zone between said dead zone and said solid polymer and in contact with each thereof, said gradient of polymerization zone comprising said first component in partially cured form.

11. The method of claim 10 , further comprising vertically reciprocating said carrier with respect to the build surface to enhance or speed the refilling of the build region with the polymerizable liquid.

12. The method of claim 1 , said light polymerizable liquid first component comprising monomers, prepolymers, or both monomers and prepolymers that can be polymerized by exposure to actinic radiation or light.

13. The method of claim 12 , said monomers, prepolymers, or monomers and prepolymers of said light polymerizable liquid first component comprising reactive end groups selected from the group consisting of acrylates, methacrylates, α-olefins, N-vinyls, acrylamides, methacrylamides, styrenics, epoxides, thiols, 1,3-dienes, vinyl halides, acrylonitriles, vinyl esters, maleimides, and vinyl ethers.

14. The method of claim 12 , said second solidifiable component comprising monomers, prepolymers, or both monomers and prepolymers comprising reactive end groups selected from the group consisting of: epoxy/amine, epoxy/hydroxyl, oxetane/amine, oxetane/alcohol, isocyanate/hydroxyl, isocyanate/amine, isocyanate/carboxylic acid, cyanate ester, anhydride/amine, amine/carboxylic acid, amine/ester, hydroxyl/carboxylic acid, hydroxyl/acid chloride, amine/acid chloride, vinyl/Si—H, Si—Cl/hydroxyl, Si—Cl/amine, hydroxyl/aldehyde, amine/aldehyde, hydroxymethyl or alkoxymethyl amide/alcohol, aminoplast, alkyne/azide, click chemistry reactive groups, alkene/sulfur, alkene/thiol, alkyne/thiol, hydroxyl/halide, isocyanate/water, Si—OH/hydroxyl, Si—OH/water, Si—OH/Si—H, Si—OH/Si—OH, perfluorovinyl, diene/dienophiles, olefin metathesis polymerization groups, olefin polymerization groups for Ziegler-Natta catalysis, and ring-opening polymerization groups and mixtures thereof.

15. The method of claim 1 , wherein said three-dimensional object comprises an interpenetrating polymer network (IPN), said interpenetrating polymer network comprising a sol-gel composition, a hydrophobic-hydrophilic IPN, a phenolic resin, a polyimide, a conductive polymer, a natural product-based IPN, a sequential IPN, a polyolefin, or a combination thereof.

16. The method of claim 1 , wherein said three-dimensional object comprises:
(i) enclosed cavities, partially open cavities, repeating unit cells, open cell foams, closed cell foams, or combinations thereof;
(ii) a waveguide, prism, lens, or combination thereof; or
(iii) a wall, strut, beam, tie, or combination thereof.

17. The method of claim 1 , wherein said polymerizable liquid further comprises thermoplastic particles.

18. The method of claim 9 , wherein said second component comprises a polymerizable liquid solubilized in or suspended in said first component.

19. The method of claim 9 , wherein said second component comprises:
(i) a polymerizable solid suspended in said first component;
(ii) a polymerizable solid solubilized in said first component; or
(iii) a polymer solubilized in said first component.

20. The method of claim 9 , wherein said three-dimensional intermediate is collapsible or compressible.

21. The method of claim 9 , wherein said three-dimensional object comprises a polymer blend, interpenetrating polymer network, semi-interpenetrating polymer networ

Assignees

• Carbon3D Inc
• Carbon Inc

Inventors

• Rolland Jason P
• Chen Kai
• Poelma Justin
• Goodrich James
• Pinschmidt Robert
• Desimone Joseph M
• Robeson Lloyd M

Classifications

• B29K2105/251

  Particles, powder or granules (expandable particles B29K2105/046) · CPC title

• B29K2105/0091

  IPN, i.e. interpenetrating polymer networks · CPC title

• B29K2105/0073

  Solution · CPC title

• B29C64/286

  Optical filters, e.g. masks · CPC title

• C08G18/8175

  with esters of acrylic or alkylacrylic acid having only one group containing active hydrogen · CPC title