Polyvinyl acetal film and uses thereof

Patent metadata

Field	Value
Publication number	US-9676930-B2
Application number	US-201113637758-A
Country	US
Kind code	B2
Filing date	Mar 30, 2011
Priority date	Mar 31, 2010
Publication date	Jun 13, 2017
Grant date	Jun 13, 2017

Abstract

A polyvinyl acetal film as an intermediate film for a laminated glass, can provide a laminated glass that exhibits a low degree of yellowness and excellent surface appearance, and is useful as a sealing material or intermediate film that can prolong the life of a laminated glass provided with a solar cell or functional unit. The content of corrosion-causing substance in the polyvinyl acetal film is low, so that the polyvinyl acetal film permits high-temperature lamination and ensures excellent productivity. A solar cell module and a laminated glass are prepared using the polyvinyl acetal film. A plasticized polyvinyl acetal film which comprises 15 to 60 parts by mass of a plasticizer having a total number of 28 or more of carbon atoms and oxygen atoms constituting a molecule based on 100 parts by mass of a polyvinyl acetal resin, and which has an acid value of 5.0 meq/kg or less.

First claim

The invention claimed is:

1. A laminated glass comprising, as an intermediate film of the laminated glass, a plasticized polyvinyl acetal film,
the plasticized polyvinyl acetal film comprising 15 to 60 parts by mass of a plasticizer and 100 parts by mass of a polyvinyl acetal resin, and the plasticized polyvinyl acetal film having an acid value after heating at 140° C. for 4 hours of 10.0 meq/kg or less, as measured in accordance with JIS 6728:1977;
wherein the plasticized polyvinyl acetal film has an acid value before heating at 140° C. for 4 hours of 5.0 meq/kg or less, as measured in accordance with JIS 6728:1977.

2. The laminated glass according to claim 1 ,
wherein the combined total number of carbon atoms and oxygen atoms in a molecule of the plasticizer is greater than or equal to 28.

3. The laminated glass according to claim 1 , wherein the combined total number of carbon atoms and oxygen atoms in a molecule of the plasticizer is greater than 29.

4. The laminated glass according to claim 1 , wherein the plasticizer is represented by the following chemical formula (1):
R 2 —X—R 1 —Y—R 3   (1)

in which R 1 is a divalent saturated hydrocarbon group optionally containing an oxygen atom, R 2 and R 3 are a linear or branched saturated hydrocarbon group optionally containing an oxygen atom, which may be the same or different, and X and Y are COO or OCO, and may be the same or different.

5. The laminated glass according to claim 1 , the plasticized polyvinyl acetal film containing a total of 50 ppm or less of chloride ions, sulfate ions, and nitrate ions.

6. The laminated glass according to claim 1 , wherein before heating, the polyvinyl acetal resin has an acid value of 3.0 meq/kg or less and the plasticizer has an acid value of 10.0 meq/kg or less, as measured in accordance with JIS K 6728:1977.

7. A method for producing a laminated glass according to claim 1 , comprising:
mixing 15 to 60 parts by mass of a plasticizer with 100 parts by mass of a polyvinyl acetal resin to form a mixture,
and molding the mixture;
wherein the combined total number of carbon atoms and oxygen atoms in a molecule of the plasticizer is greater than or equal to 28.

8. The method for producing a laminated glass according to claim 7 , wherein the combined total number of carbon atoms and oxygen atoms in a molecule of the plasticizer is greater than 29.

9. The method for producing a laminated glass according to claim 7 , wherein the polyvinyl acetal resin has an average primary particle size of 10 μm or less.

10. The method for producing a laminated glass according to claim 7 , wherein before heating, the polyvinyl acetal resin has an alkali titer value of 0.1 to 30 and an acid value of 3.0 meq/kg or less, as measured in accordance with JIS K 6728:1977.

11. The method for producing a laminated glass according to claim 7 , wherein the polyvinyl acetal resin contains a total of 100 ppm or less of chloride ions, sulfate ions, and nitrate ions.

12. The method for producing a laminated glass according to claim 7 , wherein the polyvinyl acetal resin is prepared by first adding aldehyde to an aqueous solution of a polyvinyl alcohol resin and then adding a catalyst.

13. The method for producing a laminated glass according to claim 7 , wherein a plasticizer having an acid value of 10.0 meq/kg or less, as measured in accordance with JIS K 6728:1977, is mixed with a polyvinyl acetal resin having an acid value of 3.0 meq/kg or less, as measured in accordance with JIS K 6728:1977, to form a mixture, and the mixture is molded.

14. The method for producing a laminated glass according to claim 7 , wherein a volatile component is removed by reducing pressure while mixing the polyvinyl acetal resin and the plasticizer.

15. The method for producing a laminated glass according to claim 7 , wherein the temperature of the resin during molding ranges from 150 to 220° C.

16. The laminated glass according to claim 1 , further comprising a functional unit at a position in contact with the plasticized polyvinyl acetal film.

Assignees

• Isoue Koichiro
• Asanuma Yoshiaki
• Kuraray Co

Inventors

• Isoue Koichiro
• Asanuma Yoshiaki

Classifications

• C08J2329/14

  Homopolymers or copolymers of acetals or ketals obtained by polymerisation of unsaturated acetals or ketals or by after-treatment of polymers of unsaturated alcohols · CPC title

• B32B17/10688

  Adjustment of the adherence to the glass layers · CPC title

• B32B17/10761

  containing vinyl acetal · CPC title

• B32B17/10871

  in combination with particular heat treatment · CPC title

• C08F6/26

  Treatment of polymers prepared in bulk {also solid polymers or polymer melts, (C08F6/001, C08F6/006, C08F6/008, C08F6/02, C08F6/04 take precedence)} · CPC title