Heat sealable laminate and method for producing same

Patent metadata

Field	Value
Publication number	US-9670383-B2
Application number	US-201213984359-A
Country	US
Kind code	B2
Filing date	Feb 10, 2012
Priority date	Feb 11, 2011
Publication date	Jun 6, 2017
Grant date	Jun 6, 2017

Abstract

The present invention relates to a laminate comprising at least three layers, paper/polyethylene/polyethylene terephthalate, wherein the polyethylene terephthalate is directly coated on the polyethylene surface, with no adhesive layer or the like being interposed, and the polyethylene terephthalate layer has heat sealability; and a method for producing a laminate having polyethylene coated on at least one surface of a paper substrate, the method involving extrusion laminating polyethylene terephthalate onto a surface of the polyethylene, wherein an air gap expressed as the distance from a lip opening of a die to the polyethylene surface is 25 cm or less.

First claim

The invention claimed is:

1. A method for producing a paper-based heat sealable laminate, comprising:
coating polyethylene on at least one surface of a paper substrate, and coating polyethylene terephthalate on a film of the polyethylene by an extrusion lamination process by using an extruder, wherein:
the polyethylene terephthalate is a homopolyethylene terephthalate having an intrinsic viscosity of 0.72 to 0.88 dL/g,
the polyethylene is a low-density polyethylene, and the surface of the film has been treated,
an air gap, expressed as a distance from a lip opening of a T-die of the extruder to a surface of the coating of the polyethylene, is 25 cm or less,
an extrusion temperature of the homopolyethylene terephthalate during melt extrusion in the extrusion lamination process is in a range of not lower than Tm+25° C. but lower than Tm+70° C., based on a melting point (Tm) of the homopolyethylene terephthalate, the extrusion pressure is in a range of 3.5 to 6.5 MPa, and, after the extrusion lamination with the homopolyethylene terephthalate, the laminate coated with the homopolyethylene terephthalate is cooled by the cooling rolls.

2. The method according to claim 1 , wherein the coated polyethylene terephthalate has a thickness of 10 to 60 μm.

Assignees

• Yamauchi Kunio
• Iwaya Isao
• Nissin Foods Holdings Co Ltd

Inventors

• Yamauchi Kunio
• Iwaya Isao

Classifications

• B32B27/32

  comprising polyolefins {(comprising vinyl (co)polymers or acrylic (co)polymers B32B27/30)} · CPC title

• B32B27/36

  comprising polyesters · CPC title

• B32B2250/03

  3 layers · CPC title

• B32B37/153

  at least one layer is extruded and immediately laminated while in semi-molten state · CPC title

• Y10T428/1352

  Polymer or resin containing [i.e., natural or synthetic] · CPC title