High refractive index glass bead with high retroreflectivity, and method of preparing the same

Patent metadata

Field	Value
Publication number	US-9670091-B2
Application number	US-201414759929-A
Country	US
Kind code	B2
Filing date	Jan 9, 2014
Priority date	Jan 9, 2013
Publication date	Jun 6, 2017
Grant date	Jun 6, 2017

Abstract

The present disclosure provides a retroreflective glass bead that includes at least one high refractive oxide selected from the group consisting of TiO 2 , BaO, La 2 O and Bi 2 O 3 ; and at least one additive selected from the group consisting of MgO, CaO, ZnO, ZrO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O and SrO. The glass bead according to the present invention have excellent retroreflectivity according to optical properties and excellent durability and productivity due to a simple structure, and also can be produced in various colors due to high chemical stability. Thus, the retroreflective aggregate including the glass bead according to the present invention exhibits very high visibility under various circumstances such as rainy or dry conditions. In addition, the method of producing a glass bead according to the present invention can reduce manufacturing costs while ensuring excellent productivity.

First claim

The invention claimed is:

1. A glass bead comprising:
at least one high refractive oxide selected from the group consisting of TiO 2 , and BaO; and
at least one additive selected from the group consisting of MgO, CaO, ZnO, ZrO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O and SrO,
wherein the glass bead has a light transmittance of 65% or more, and a refractive index of 1.7 to 2.0.

2. The glass bead according to claim 1 , further comprising at least one glass stabilizer selected from the group consisting of SiO 2 and B 2 O 3 .

3. The glass bead according to claim 2 , wherein the glass bead comprises Li 2 O, SrO and B 2 O 3 .

4. The glass bead according to claim 3 , comprising: 20 wt % to 60 wt % of TiO 2 ; 15 wt % to 55 wt % of BaO; 0.1 wt % to 10 wt % of Li 2 O; 0.1 wt % to 10 wt % of SrO; and 1 wt % to 40 wt % of B 2 O 3 .

5. A glass bead comprising:
TiO 2 , BaO, or a mixture thereof;
La 2 O, Bi 2 O 3 , or a mixture there of; and
at least one additive selected from the group consisting of MgO, CaO, ZnO, ZrO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O and SrO,
wherein the glass bead has a light transmittance of 65% or more, and a refractive index of 2.0 to 2.5.

6. The glass bead according to claim 5 , comprising:
15 wt % to 85 wt % of TiO 2 , BaO, or a mixture thereof;
5 wt % to 75 wt % of La 2 O, Bi 2 O 3 , or a mixture thereof; and
1 wt % to 15 wt % of ZrO 2 .

7. The glass bead according to claim 1 , wherein the glass bead comprises at least one colorant selected from the group consisting of CuO, CeO 2 , CoO, NiO, and Fe 2 O 3 in an amount of 0.1 parts by weight to 15 parts by weight based on 100 parts by weight of the high refractive oxide(s) and the additive(s).

8. The glass bead according to claim 1 , wherein the glass bead has a particle diameter of 1 μm to 1000 μm.

9. A retroreflective aggregate comprising the glass bead according to claim 1 .

10. The retroreflective aggregate according to claim 9 , wherein the retroreflective aggregate comprises a glass bead having refractive index (nd) of 1.7 to 2.0, and a glass bead having refractive index (nd) of 2.0 to 2.5 in a weight ratio of 1:0.1 to 7.

11. The retroreflective aggregate according to claim 9 , wherein the retroreflective aggregate is a panel, a road sign or a visible paint.

12. A method of producing a glass bead, the method comprising:
crushing glassy materials to prepare a glass scrap; and
injecting the glass scrap using compressed air from a lower inlet of a bead forming furnace, which is divided into a cooling zone and a heating zone from top to bottom, toward the cooling zone, and
softening the glass scrap while passing through the heating zone, and solidifying the softened glass scrap while passing through the upper cooling zone.

13. The method according to claim 12 , wherein the glass scrap has a particle diameter of 1 μm to 1000 μm.

14. The method according to claim 12 , wherein the heating zone has a temperature ranging from 1000° C. to 1400° C., and the cooling zone has a temperature ranging from 10° C. to a temperature of the heating zone.

15. The glass bead according to claim 5 , wherein the glass bead consists of:
TiO 2 , BaO, or a mixture thereof;
La 2 O, Bi 2 O 3 , or a mixture there of; and
at least one additive selected from the group consisting of MgO, CaO, ZnO, ZrO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O and SrO.

Assignees

• Oci Co Ltd

Inventors

• Ryu Hae-Yoon
• Cho Sang-Je

Classifications

• C03C3/064

  containing boron · CPC title

• C03C12/02 Primary

  Reflective beads · CPC title

• Y10T428/2982

  Particulate matter [e.g., sphere, flake, etc.] · CPC title

• C03C3/062

  with less than 40% silica by weight · CPC title

• C03C3/14

  containing boron · CPC title