Method of making alkali metal hydrides

Patent metadata

Field	Value
Publication number	US-9663364-B2
Application number	US-201514757132-A
Country	US
Kind code	B2
Filing date	Nov 23, 2015
Priority date	Jul 21, 2015
Publication date	May 30, 2017
Grant date	May 30, 2017

Abstract

A method is provided for making alkali metal hydrides by mechanochemically reacting alkali metal and hydrogen gas under mild temperature (e.g room temperature) and hydrogen pressure conditions without the need for catalyst, solvent, and intentional heating or cooling.

First claim

We claim:

1. A method of making alkali metal hydride, comprising mechanochemically reacting an alkali metal and hydrogen gas in the presence of preformed alkali metal hydride powder at a temperature of about 0 to about 100 degrees C. to form the alkali metal hydride.

2. The method of claim 1 wherein the hydrogen gas is provided initially or over time in a stoichiometric amount to convert substantially all of the alkali metal to alkali metal hydride.

3. The method of claim 1 where the hydrogen gas comprises essentially pure lightest isotope protium— 1 H.

4. The method of claim 1 where the hydrogen gas comprises essentially pure heavy isotope deuterium— 2 H.

5. The method of claim 1 where the hydrogen gas comprises essentially pure heaviest isotope tritium— 3 H.

6. The method of claim 1 where the hydrogen gas comprises a mixture of 1 H, 2 H and 3 H, in which any of the isotopes is present in concentrations ranging between 1 and 99 vol. %.

7. The method of claim 2 including providing a hydrogen gas pressure of about 1 to 350 bars.

8. The method of claim 7 wherein the hydrogen gas pressure is from 25 to 350 bars.

9. The method of claim 1 wherein the temperature is from 10 to 40 degrees C.

10. The method of claim 9 wherein the temperature is about 20 to about 26 degrees C.

11. The method of claim 1 wherein a reaction time is 20 hours or less.

12. The method of claim 1 wherein the alkali metal comprises at least one of Li, Na, K, Rb, and Cs.

13. The method of claim 12 wherein the metal comprises at least two of Li, Na, K, Rb, and Cs to form a mixed metal hydride.

14. The method of claim 1 including providing a mixture of the alkali metal and the pre-formed alkali metal hydride and the hydrogen gas in a reactor.

15. The method of claim 1 wherein the alkali metal hydride includes an alkali metal deuteride or alkali metal tritide.

16. The method of claim 1 wherein the alkali metal and hydrogen gas are reacted in the presence of the preformed alkali metal hydride powder in a ball mill.

17. The method of claim 16 wherein the ball mill is a magnetic ball mill.

18. The method of claim 16 wherein the ball mill is a planetary mill.

19. The method of claim 16 wherein the ball mill is a commercial scale mill.

20. A method of making lithium hydride, comprising mechanochemically reacting lithium metal and hydrogen gas in the presence of preformed lithium hydride powder at a temperature of about 0 to about 100 degrees C. to form the lithium hydride.

Assignees

• Univ Iowa State Res Found Inc

Inventors

• Pecharsky Vitalij K
• Gupta Shalabh
• Pruski Marek
• Hlova Ihor
• Castle Andra

Classifications

• C01B6/24

  Hydrides containing at least two metals; Addition complexes thereof (C01B6/13 - C01B6/23 take precedence) · CPC title

• C01B6/04 Primary

  Hydrides of alkali metals, alkaline earth metals, beryllium or magnesium; Addition complexes thereof · CPC title