Low loss optical fiber and method of making the same

Patent metadata

Field	Value
Publication number	US-9658395-B2
Application number	US-201514825297-A
Country	US
Kind code	B2
Filing date	Aug 13, 2015
Priority date	Oct 21, 2014
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

The core region of an optical fiber is doped with chlorine in a concentration that allows for the viscosity of the core region to be lowered, approaching the viscosity of the surrounding cladding. An annular interface region is disposed between the core and cladding and contains a concentration of fluorine dopant sufficient to match the viscosity of the core. By including this annular stress accommodation region, the cladding layer can be formed to include the relatively high concentration of fluorine required to provide the desired degree of optical signal confinement (i.e., forming a “low loss” optical fiber).

First claim

What is claimed is:

1. An optical fiber comprising
a chlorine-doped silica core region;
a fluorine-doped cladding region; and
a fluorine-doped annular stress-accommodation region disposed between the core region and the cladding region, the fluorine-doped annular stress-accommodation region including a concentration of a fluorine dopant of an amount such that the stress-accommodation region has a viscosity substantially the same as the core region,
the cladding region having a fluorine dopant concentration greater than the fluorine dopant concentration of the annular stress accommodation region for providing confinement of the propagating optical signal to the combination of the core region and the annular stress-accommodation region wherein the fluorine dopant concentration in the annular stress-accommodation region is between 0.3 mol % and 3.0 mol %.

2. The optical fiber of claim 1 wherein the core region includes a high concentration of Si—Cl bonds to provide a desired concentration of chlorine dopant.

3. The optical fiber of claim 1 wherein the core region includes chlorine dopant provided by SiCl 4 .

4. The optical fiber of claim 1 wherein the chlorine dopant concentration in the core region and the fluorine dopant in the annular stress-accommodation are determined such that the density of the core region essentially matches the density of the annular stress-accommodation region at a determined fictive temperature T f .

5. The optical fiber of claim 4 wherein the fictive temperature T f is about 1600° C.

6. The optical fiber of claim 4 wherein the optical fiber has an attenuation of less than 0.33 dB/km at a wavelength of 1385 nm.

7. The optical fiber of claim 4 wherein the chlorine dopant concentration in the silica core region is between 2000 ppm and 15,000 ppm by weight.

8. The optical fiber of claim 4 wherein the chlorine dopant concentration in the silica core region is between 2000 ppm and 15,000 ppm by weight and the fluorine dopant concentration in the annular stress-accommodation region is between 0.3 mol % and 3.0 mol %.

9. The optical fiber of claim 1 wherein the chlorine dopant concentration in the silica core region is between 2000 ppm and 15,000 ppm by weight.

10. The optical fiber of claim 1 wherein the chlorine dopant concentration in the silica core region is between 2000 ppm and 15,000 ppm by weight and the fluorine dopant concentration in the annular stress-accommodation region is between 0.3 mol % and 3.0 mol %.

11. The optical fiber of claim 1 wherein the silica core region is co-doped to include fluorine dopant in addition to the chlorine dopant.

12. The optical fiber of claim 11 wherein the optical fiber has a group refractive index lower than the group refractive index value of pure silica.

13. The optical fiber of claim 1 wherein the silica core region is substantially free of any germanium dopant.

14. The optical fiber of claim 1 wherein the chlorine dopant concentration in the core region and the fluorine dopant in the annular stress-accommodation are determined such that the fraction of optical power present in the cladding region is less than 2%.

15. The optical fiber of claim 1 wherein the optical fiber has an attenuation of less than 0.175 dB/km at a propagating signal wavelength of 1550 nm.

16. The optical fiber of claim 1 wherein the optical fiber has an effective area of more than 100 μm 2 at a wavelength of 1550 nm.

17. The optical fiber of claim 1 wherein the average residual stress is less than 100 MPa in the core region and the annular stress-accommodation region.

Assignees

• Ofs Fitel Llc

Inventors

• Borel Peter I
• Jensen Rasmus V S
• Levring Ole A
• Olsen Jorgen Ostgaard
• Peckham David W
• Trevor Dennis J
• Wisk Patrick W
• Yan Man F

Classifications

• C03B37/027 Primary

  Fibres composed of different sorts of glass, {e.g. glass optical fibres}(C03B37/0253, C03B37/028 take precedence) · CPC title

• C03B37/01453

  for doping the preform with flourine · CPC title

• C03B37/01861

  Means for changing or stabilising the diameter or form of tubes or rods · CPC title

• C03C2203/44

  chlorine containing · CPC title

• C03B2203/22

  Radial profile of refractive index, composition or softening point · CPC title