Polycrystalline diamond compact including a pre-sintered polycrystalline diamond table including a nonmetallic catalyst that limits infiltration of a metallic-catalyst infiltrant therein and applications therefor

Patent metadata

Field	Value
Publication number	US-9657529-B1
Application number	US-201514800573-A
Country	US
Kind code	B1
Filing date	Jul 15, 2015
Priority date	Aug 24, 2005
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

Embodiments of the invention relate to thermally-stable polycrystalline diamond compacts (“PDCs”), and methods of fabricating such PDCs. In an embodiment, a PDC includes a substrate and a pre-sintered polycrystalline diamond (“PCD”) table bonded to the substrate. The pre-sintered PCD table includes bonded diamond grains defining a plurality of interstitial regions. The pre-sintered PCD table further including a first region remote from the substrate including a nonmetallic catalyst and a metallic catalyst each of which is disposed interstitially between the bonded diamond grains thereof, and a second region bonded to the substrate including a metallic-catalyst infiltrant disposed interstitially between the bonded diamond grains thereof. A nonplanar boundary is located between the first region and the second region.

First claim

What is claimed is:

1. A polycrystalline diamond compact, comprising:
a substrate including a metallic-catalyst infiltrant therein; and
a pre-sintered polycrystalline diamond table bonded to the substrate, the pre-sintered polycrystalline diamond table including bonded diamond grains defining a plurality of interstitial regions, the pre-sintered polycrystalline diamond table further including:
a first region remote from the substrate including a nonmetallic catalyst and entrapped residual metallic catalyst each of which is disposed interstitially between the bonded diamond grains of the first region;
a second region bonded to the substrate including a portion of the metallic-catalyst infiltrant infiltrated from the substrate disposed interstitially between the bonded diamond grains of the second region; and
a nonplanar boundary located between the first region and the second region.

2. The polycrystalline diamond compact of claim 1 wherein the nonmetallic catalyst infiltrant is infiltrated into the pre-sintered polycrystalline diamond table from the working surface thereof to no farther than an intermediate location therewithin.

3. The polycrystalline diamond compact of claim 1 wherein the nonmetallic catalyst includes at least one member selected from the group consisting of an inorganic nonmetallic catalyst and an organic nonmetallic catalyst.

4. The polycrystalline diamond compact of claim 3 wherein the nonmetallic catalyst includes at least one member selected from the group consisting of a carbonate, a sulfate, derivatives of a sulfate, a hydroxide, phosphorous, a chloride, sulfur, a polycyclic aromatic hydrocarbon, a derivative of a chlorinated hydrocarbon, and a semiconductor.

5. The polycrystalline diamond compact of claim 4 wherein the at least one member comprises a carbonate, and further wherein the carbonate comprises one or more alkali metal carbonates, one or more alkaline earth metal carbonates, or combinations thereof.

6. The polycrystalline diamond compact of claim 4 wherein the at least one member comprises a polycyclic aromatic hydrocarbon, and further wherein the polycyclic aromatic hydrocarbon is selected from the group consisting of naphthalene, anthracene, pentacene, perylene, coronene, derivatives thereof, and combinations thereof.

7. The polycrystalline diamond compact of claim 3 wherein the nonmetallic catalyst includes at least one material selected from the group consisting of a mixture including at least two carbonates having a eutectic or near eutectic composition, elemental phosphorus, elemental sulfur, a polycyclic aromatic hydrocarbon, and a derivative of a chlorinated hydrocarbon.

8. The polycrystalline diamond compact of claim 1 wherein the entrapped residual metallic catalyst in the first region is present in an amount of about 0.8 weight % to about 1.50 weight %.

9. The polycrystalline diamond compact of claim 1 wherein the nonplanar boundary exhibits a geometry characteristic of the metallic-catalyst infiltrant being partially infiltrated into the pre-sintered polycrystalline diamond table.

10. The polycrystalline diamond compact of claim 1 wherein the entrapped residual metallic catalyst in the first region was used to initially sinter the pre-sintered polycrystalline diamond table.

11. The polycrystalline diamond compact of claim 8 wherein the amount of the entrapped residual metallic catalyst present in the first region is about 0.86 weight % to about 1.47 weight %.

12. The polycrystalline diamond compact of claim 1 wherein the first region extends from an upper surface thereof to an intermediate depth of about 0.20 mm to about 1.5 mm.

13. The polycrystalline diamond compact of claim 12 wherein the intermediate depth is about 0.65 mm to about 0.90 mm.

14. The polycrystalline diamond compact of claim 1 wherein the nonmetallic catalyst occupies substantially all of the interstitial regions of the first region.

15. The polycrystalline diamond compact of claim 1 wherein the substrate comprises a cemented carbide substrate.

16. The polycrystalline diamond compact of claim 1 wherein the nonplanar boundary is characteristic of the metallic catalyst not being partially leached to a selected intermediate depth within the pre-sintered polycrystalline diamond table.

17. The polycrystalline diamond compact of claim 1 wherein the metallic-catalyst infiltrant comprises at least one member selected from the group consisting of iron, nickel, cobalt, and alloys thereof.

18. A polycrystalline diamond compact, comprising:
a substrate; and
a pre-sintered polycrystalline diamond table including an interfacial surface bonded to the substrate and an upper surface that generally opposes the interfacial surface, the pre-sintered polycrystalline diamond table including bonded diamond grains defining a plurality of interstitial regions, the pre-sintered polycrystalline diamond table further including:
a first region remote from the substrate and extending from the upper surface, the first region including a nonmetallic catalyst and entrapped residual metallic catalyst each of which is disposed interstitially between the bonded diamond grains of the first region;
a second region bonded to the substrate, the interstitial regions of the second region including a metallic-catalyst infiltrant disposed therein, the second region and being substantially free of the nonmetallic catalyst; and
a nonplanar boundary located between the first region and the second region.

19. The polycrystalline diamond compact of claim 18 wherein the nonmetallic catalyst is infiltrated into the pre-sintered polycrystalline diamond table from the upper surface thereof to no farther than an intermediate location therewithin.

20. A rotary drill bit, comprising:
a bit body configured to engage a subterranean formation; and
a plurality of polycrystalline diamond cutting elements affixed to the bit body, at least one of the polycrystalline diamond cutting elements including:
a substrate including a metallic-catalyst infiltrant therein; and
a pre-sintered polycrystalline diamond table bonded to the substrate, the pre-sintered polycrystalline diamond table further including bonded diamond grains defining a plurality of interstitial regions, the pre-sintered polycrystalline diamond table further including:
a first region remote from the substrate including a nonmetallic catalyst and entrapped residual metallic catalyst each disposed interstitially between the bonded diamond grains of the first region;
a second region bonded to the substrate including a portion of the metallic-catalyst infiltrant infiltrated from the substrate disposed interstitially between the bonded diamond grains of the second region; and
a nonplanar boundary located between the first region and the second region.

Assignees

• Us Synthetic Corp
• Us Synthetics Corp

Inventors

• Bertagnolli Kenneth E
• Vail Michael A

Classifications

• Y10T428/30

  Self-sustaining carbon mass or layer with impregnant or other layer · CPC title

• C04B2235/3843

  Titanium carbides · CPC title

• C04B2235/427

  Diamond · CPC title

• C04B2235/3274

  Ferrites · CPC title

• C04B2235/3821

  Boron carbides · CPC title