High-strength hot rolled steel sheet

Patent metadata

Field	Value
Publication number	US-9657382-B2
Application number	US-201214369269-A
Country	US
Kind code	B2
Filing date	Dec 14, 2012
Priority date	Dec 27, 2011
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

A high-strength hot rolled steel sheets with excellent stretch flangeability has small variations in mechanical properties in individual coils. Variations in strength from place to place in a coil are decreased by minimally reducing the Si and Mn contents to suppress the occurrence of problems such as segregation. Further, the microstructure of the steel sheets is configured such that a ferrite phase represents an area ratio of not less than 95%, the ferrite crystal grains have an average grain size of not less than 1 μm, and the ferrite crystal grains contain TiC with an average particle size of not more than 7 nm dispersed in the crystal grains.

First claim

The invention claimed is:

1. A high-strength hot rolled steel sheet with a yield strength of not less than 530 MPa, the steel sheet having a chemical composition including, by mass %:
C: more than 0.010% and not more than 0.06%,
Si: not more than 0.3%,
Mn: not more than 0.48%,
P: not more than 0.03%,
S: not more than 0.02%,
Al: not more than 0.1%,
N: not more than 0.01% and Ti: 0.05 to 0.10%,
the balance comprising Fe and inevitable impurities, the steel sheet comprising a metal microstructure including a ferrite phase with an area ratio of not less than 95%, the ferrite crystal grains having an average grain size of not less than 1 μm, the ferrite crystal grains containing TiC precipitate particles dispersed in the crystal grains, the TiC precipitate particles having an average particle size of not more than 7 nm, and the steel sheet having a ΔYS of 20 MPa or less.

2. The steel sheet according to claim 1 , wherein the chemical composition further includes, by mass %, B: not more than 0.0020%.

3. The steel sheet according to claim 1 , wherein the chemical composition further includes, by mass %, one or more selected from the group consisting of Cu, Ni, Cr, Co, Mo, Sb, W, As, Pb, Mg, Ca, Sn, Ta, Nb, V, REM, Cs, Zr and Zn in a total content of not more than 1%.

4. The steel sheet according to claim 1 , wherein the TiC has a ratio of the number of Ti atoms to the number of C atoms, Ti/C, of less than 1.

5. The steel sheet according to claim 1 , further comprising a coating on a surface thereof.

6. The steel sheet according to claim 5 , wherein the coating is a zinc coating or a zinc-containing alloy coating.

7. The steel sheet according to claim 2 , wherein the chemical composition further includes, by mass %, one or more selected from the group consisting of Cu, Ni, Cr, Co, Mo, Sb, W, As, Pb, Mg, Ca, Sn, Ta, Nb, V, REM, Cs, Zr and Zn in a total content of not more than 1%.

8. The steel sheet according to claim 2 , wherein the TiC has a ratio of the number of Ti atoms to the number of C atoms, Ti/C, of less than 1.

9. The steel sheet according to claim 3 , wherein the TiC has a ratio of the number of Ti atoms to the number of C atoms, Ti/C, of less than 1.

10. The steel sheet according to claim 2 , further comprising a coating on a surface thereof.

11. The steel sheet according to claim 3 , further comprising a coating on a surface thereof.

12. The steel sheet according to claim 4 , further comprising a coating on a surface thereof.

Assignees

• Jfe Steel Corp

Inventors

• Funakawa Yoshimasa
• Yamamoto Tetsuo
• Uchomae Hiroshi
• Nakano Hiroshi
• Kizu Taro

Classifications

• C21D8/0415

  Rapid solidification; Thin strip casting · CPC title

• C22C38/28

  with titanium or zirconium · CPC title

• C22C38/22

  with molybdenum or tungsten · CPC title

• C22C38/60 Primary

  containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur · CPC title

• C22C38/001

  containing N · CPC title