Abstract

Tire treads and tires having such tire treads are included, such treads manufactured with a rubber composition that includes mostly, if not entirely, a polybutadiene rubber having cis-1,4 bond content of at least 95%. The rubber composition further includes between 60 phr and 95 phr of a plasticizing resin having a Tg of at least 25° C. and between 0 phr and 15 phr of a liquid plasticizer. Additionally the rubber composition is reinforced with at least 90 phr of a silica reinforcing filler. Alternatively, in some embodiments, the rubber composition may be reinforced with an organic filler, an inorganic filler or combinations thereof. In some of these embodiments, the rubber composition includes at least 90 phr of such reinforcing filler.

First claim

What is claimed is:

1. A tread for a tire, the tread comprising a rubber composition that is based upon a cross-linkable elastomer composition, the cross-linkable elastomer comprising, per 100 parts by weight of rubber (phr):
100 phr of a polybutadiene rubber having a cis-1,4 bond content of at least 95%;
between 60 phr and 95 phr of a plasticizing resin having a glass transition temperature of at least 25° C.;
between 0 phr and 3 phr of a liquid plasticizer; and
at least 90 phr of a silica reinforcing filler.

2. The tread of claim 1 , wherein the rubber composition has a glass transition temperature of between −35° C. and 0° C.

3. The tread of claim 1 , wherein the plasticizing resin has a glass transition temperature of between 40° C. and 85° C.

4. The tread of claim 1 , wherein the plasticizing resin is a C5-C9 petroleum resin.

5. The tread of claim 1 , wherein the tire is an automobile tire.

6. The tread of claim 1 , wherein the tire is a light truck tire.

7. A tread for a tire, the tread comprising a rubber composition that is based upon a cross-linkable elastomer composition, the cross-linkable elastomer comprising, per 100 parts by weight of rubber (phr):
100 phr of a polybutadiene rubber having a cis-1,4 bond content of at least 95%;
between 60 phr and 95 phr of a plasticizing resin having a glass transition temperature of at least 25° C.;
between 0 phr and 3 phr of a liquid plasticizer; and
a reinforcing filler selected from the group consisting of an organic filler, an inorganic filler and combinations thereof.

8. The tread of claim 7 , wherein the elastomer comprises at least 90 phr of the reinforcing filler.

9. The tread of claim 7 , wherein the reinforcing filler is silica.

10. The tread of claim 7 , wherein the rubber composition has a glass transition temperature of between −35° C. and 0° C.

11. The tread of claim 7 , wherein the plasticizing resin has a glass transition temperature of between 40° C. and 85° C.

12. The tread of claim 7 , wherein the plasticizing resin is a C5-C9 petroleum resin.

13. The tread of claim 7 , wherein the tire is an automobile tire.

14. The tread of claim 7 , wherein the tire is a light truck tire.

15. The tread of claim 1 , wherein the cross-linkable elastomer comprises no liquid plasticizer.

16. The tread of claim 7 , wherein the cross-linkable elastomer comprises no liquid plasticizer.

Assignees

• Michelin & Cie
• Michelin Rech Tech

Inventors

• Saintigny Xavier
• Piffard Olivier

Classifications

• C08K5/18

  with aromatically bound amino groups · CPC title

• C08K3/22

  of metals · CPC title

• C08L9/00 Primary

  Compositions of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08K3/36

  Silica · CPC title

• C08K3/04

  Carbon · CPC title