Rigid polyurethane foams

Patent metadata

Field	Value
Publication number	US-9657133-B2
Application number	US-52200208-A
Country	US
Kind code	B2
Filing date	Jan 9, 2008
Priority date	Jan 12, 2007
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

The invention relates to rigid polyurethane foams which can be produced by reacting a) polyisocyanates with b) compounds having at least two hydrogen atoms which are reacted toward isocyanate groups in the presence of c) blowing agents, wherein the polyisocyanate a) used is a mixture of diphenylmethane diisocyanate and polyphenylenepolymethylene polyisocyanates comprising a1) 30-35% by weight of diphenylmethane diisocyanate, a2) 21-28% by weight of polyphenylenepolymethylene polyisocyanate having three aromatic rings, a3) 8-13% by weight of polyphenylenepolymethylene polyisocyanate having four aromatic rings, a4) 24-41% by weight of polyphenylenepolymethylene polyisocyanate having five or more aromatic rings, where the percentages by weight of the components a1) to a4) are based on the total weight of the components a1) to a4) and add up to 100% by weight.

First claim

The invention claimed is:

1. A rigid polyurethane foam which is produced by reacting
a) a polyisocyanate component with,
b) at least one compound having at least two hydrogen atoms reactive with isocyanate groups, in the presence of
c) a blowing agent consisting of water, or an alkane having at least 4 carbon atoms, or a cycloalkane having at least 4 carbon atoms, or a mixture thereof,
wherein:
the polyisocyanate component a) is a mixture comprising
a1) 30-35% by weight of diphenylmethane diisocyanate,
a2) 21-28% by weight of a polyphenylenepolymethylene polyisocyanate having three aromatic rings,
a3) 8-13% by weight of a polyphenylenepolymethylene polyisocyanate having four aromatic rings, and
a4) 24-41% by weight of a polyphenylenepolymethylene polyisocyanate having five or more aromatic rings,

where the percentages by weight of the components a1) to a4) are based on the total weight of the components a1) to a4) and add up to 100% by weight;
the at least one compound b) is a mixture comprising
b1a) a polyether alcohol b1a) prepared by addition of ethylene oxide and propylene oxide onto an aromatic amine, and having a hydroxyl number ranging from 300 to 500 mg KOH/g,
b1b) a polyether alcohol b1b) prepared by addition of ethylene oxide and propylene oxide onto an aromatic amine, and having a hydroxyl number ranging from 300 to 500 mg KOH/g, and
b2) at least one polyether alcohol b2) prepared by addition of at least one alkylene oxide and glycerol onto a sugar;
the component a) comprises less than 10% by weight, based on the weight of the component a), of uretonimine;
a mean molecular weight of the polyether alcohol b1b) is greater than a mean molecular weight of the polyether alcohol b1a); and
a weight ratio of a sum of the weights of the polyether alcohols b1a) and b1b) to the weight of the at least one polyether b2) ranges from 1:1 to 1:6.

2. The rigid polyurethane foam according to claim 1 , wherein the component a) comprises less than 8% by weight, based on the weight of the component a), of uretonimine.

3. The rigid polyurethane foam according to claim 1 , wherein the component a) has a content of free NCO end groups of from 30 to 33% by weight.

4. The rigid polyurethane foam according to claim 1 which comprises isocyanurate groups.

5. The rigid polyurethane foam according to claim 1 , wherein at least one of the polyether alcohol b1a) and the polyether alcohol b1b) has been prepared by addition of ethylene oxide and propylene oxide onto toluenediamine.

6. The rigid polyurethane foam according to claim 5 , wherein the toluenediamine comprises at least 95% by weight, based on the weight of the toluenediamine, of ortho isomers.

7. The rigid polyurethane foam according to claim 1 , wherein the at least one polyether alcohol b2) is prepared by addition of propylene oxide and glycerol onto a sugar.

8. The rigid polyurethane foam according to claim 7 , wherein the at least one polyether alcohol b2) is prepared by addition of propylene oxide and glycerol onto sucrose.

9. The rigid polyurethane foam according to claim 1 , wherein:
the polyether alcohols b1a) and b1b) are both prepared by addition of ethylene oxide and propylene oxide onto toluenediamine; and
the at least one polyether alcohol b2) is prepared by addition of the at least one alkylene oxide and glycerol onto sucrose.

10. A process for producing a rigid polyurethane foam, the process comprising reacting
a) a polyisocyanate component with
b) at least one compound having at least two hydrogen atoms reactive with isocyanate groups in the presence of
c) a blowing agent consisting of water, or an alkane having at least 4 carbon atoms, or a cycloalkane having at least 4 carbon atoms, or a mixture thereof,
wherein:
the polyisocyanate a) is a mixture comprising
a1) 30-35% by weight of diphenylmethane diisocyanate,
a2) 21-28% by weight of polyphenylenepolymethylene polyisocyanate having three aromatic rings,
a3) 8-13% by weight of polyphenylenepolymethylene polyisocyanate having four aromatic rings, and
a4) 24-41% by weight of polyphenylenepolymethylene polyisocyanate having five or more aromatic rings,

where the percentages by weight of the components a1) to a4) are based on the total weight of the components a1) to a4) and add up to 100% by weight;
the at least one compound b) is a mixture comprising
b1a) a polyether alcohol b1a) prepared by addition of ethylene oxide and propylene oxide onto an aromatic amine, and having a hydroxyl number ranging from 300 to 500 mg KOH/g,
b1b) a polyether alcohol b1b) prepared by addition of ethylene oxide and propylene oxide onto an aromatic amine, and having a hydroxyl number ranging from 300 to 500 mg KOH/g, and
b2) at least one polyether alcohol b2) prepared by addition of at least one alkylene oxide and glycerol onto a sugar;
the component a) comprises less than 10% by weight, based on the weight of the component a), of uretonimine;
a mean molecular weight of the polyether alcohol b1b) is greater than a mean molecular weight of the polyether alcohol b1a); and
a weight ratio of a sum of the weights of the polyether alcohols b1a) and b1b) to the weight of the at least one polyether b2) ranges from 1:1 to 1:6.

11. The rigid polyurethane foam according to claim 9 , wherein the weight ratio of the sum of the weights of the polyether alcohols b1a) and b1b) to the weight of the at least one polyether alcohol b2) is from 1:1 to 1:1.27.

12. The rigid polyurethane foam according to claim 1 , which has a core density of less than 38 g/l.

13. The rigid polyurethane foam according to claim 1 , which has a core density of from 28 to 33 g/l.

14. The process according to claim 10 , wherein:
the blowing agent consists of water; and
the rigid polyurethane foam has a core density of less than 38 g/l.

15. The process according to claim 10 , wherein:
the blowing agent consists of at least one of said alkane and said cycloalkane, and water; and
the rigid polyurethane foam has a core density of from 28 to 33 g/l.

16. The process according to claim 15 , wherein the blowing agent consists of water and n-pentane.

17. The process according to claim 15 , wherein the blowing agent consists of water and cyclopentane.

18. The process according to claim 10 , wherein the blowing agent consists of at least one of said alkane and said cycloalkane.

Assignees

• Seifert Holger
• Klassen Johann
• Du Rieu Louis
• Wiegmann Werner
• Matzke Guenter
• Basf Se

Inventors

• Seifert Holger
• Klassen Johann
• Du Rieu Louis
• Wiegmann Werner
• Matzke Guenter

Classifications

• C08G18/7664 Primary

  containing alkylene polyphenyl groups · CPC title

• C08G18/4804

  Two or more polyethers of different physical or chemical nature · CPC title

• C08G18/797

  containing carbodiimide and/or uretone-imine groups · CPC title

• C07C263/00

  Preparation of derivatives of isocyanic acid · CPC title

• C08J9/22

  After-treatment of expandable particles; Forming foamed products · CPC title