Method of manufacturing preforms for optical fibres having low water peak

Patent metadata

Field	Value
Publication number	US-9656902-B2
Application number	US-201214758011-A
Country	US
Kind code	B2
Filing date	Dec 28, 2012
Priority date	Dec 28, 2012
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

A method of manufacturing at least one optical fibre preform comprising: providing a plurality of partially porous intermediate preforms, each partially porous intermediate preform having a longitudinal axis and comprising a respective soot intermediate clad layer formed around a respective glass core rod comprising a central core region of radius a and an inner clad region of radius b to define a first core-to-clad ratio a/b; consolidating the formed soot intermediate clad layers to form a respective plurality of intermediate glass preforms, each of the plurality of intermediate glass preforms comprising an intermediate clad region having an external radius c to define a second core-to-clad ratio a/c of from 0.20 to 0.30 , and overcladding at least one intermediate glass preform by forming an overclad region surrounding the intermediate clad region to form an optical fibre glass preform, wherein consolidating comprises exposing the plurality of intermediate preforms to a consolidation hot zone of a single furnace body while rotating each of the intermediate preforms about its respective longitudinal axis.

First claim

The invention claimed is:

1. A method of manufacturing an optical fibre preform comprising:
providing a plurality of partially porous intermediate preforms, each partially porous intermediate preform having a longitudinal axis and comprising a respective soot intermediate clad layer formed around a respective glass core rod comprising a central core region of radius a and an inner clad region of external radius b to define a first core-to-clad ratio a/b;
operatively connecting the plurality of partially porous intermediate preforms to a respective plurality of holding shafts comprised in a support structure comprising a support member, each of the plurality of holding shafts being rotatably engaged to the support member
consolidating the formed soot intermediate clad layers to form a respective plurality of intermediate glass preforms, each of the plurality of intermediate glass preforms comprising an intermediate clad region of external radius c to define a second core-to-clad ratio a/c of from 0.20 to 0.30; and
overcladding at least one intermediate glass preform by forming an overclad region surrounding the intermediate clad region to form an optical fibre glass preform, wherein consolidating comprises exposing the plurality of partially porous intermediate glass preforms to a consolidation hot zone of a single furnace body while rotating each of the plurality of partially porous intermediate preforms about its respective longitudinal axis, wherein:
the plurality of holding shafts are arranged peripherally with respect to a drive shaft transmitting rotation to the plurality of holding shafts by means of a slave driving mechanism.

2. The method of claim 1 ,
wherein the plurality of holding shafts are geared shafts disposed concentrically around the drive shaft transmitting rotation to the plurality of holding shafts by means of a rotation transmission mechanism.

3. The method of claim 2 , wherein the plurality of holding shafts are interlocked with a respective slave gear meshing with a master gear interlocked with the drive shaft.

4. The method of claim 1 , wherein the furnace body is vertically oriented and consolidating comprises simultaneously moving the plurality of partially porous intermediate glass preforms relative to the consolidation hot zone along a longitudinal direction of the furnace.

5. The method of claim 1 , wherein rotating each of the plurality of partially porous intermediate glass preforms comprises uniformly rotating each of the plurality of partially porous intermediate preforms at an equal rotational speed.

6. The method of claim 1 , wherein providing a plurality of partially porous intermediate preforms comprises:
providing a respective plurality of glass core rods, each glass core rod having a first core-to-clad ratio a/b, and
depositing soot material around each glass core rod by a flame hydrolysis process to form a soot intermediate clad layer surrounding the inner clad region.

7. The method of claim 6 , wherein the soot material deposited around each glass core rod is silica soot.

8. The method of claim 6 , wherein the flame hydrolysis deposition process is an outside vapour deposition process.

9. The method of claim 1 , wherein the core-to-clad ratio a/b is equal to or less than 0.40.

10. The method of claim 1 , wherein overcladding the at least one intermediate glass preform comprises:
depositing soot material around the intermediate glass preform by a flame hydrolysis process to form a soot overclad layer, and
consolidating the soot overclad layer so as to form an optical fibre preform.

11. The method of claim 10 , wherein the flame hydrolysis deposition process is an outside vapour deposition process.

12. The method of claim 1 , further comprising the step of drawing the optical fiber preform to fabricate an optical fiber.

Assignees

• Prysmian Spa

Inventors

• Adigrat Antonio
• Caronna Valeria
• Cocchini Franco
• Collaro Antonio
• Grieco Stefano
• Nivelli Ida

Classifications

• C03B37/01486

  Means for supporting, rotating or translating the preforms being formed, e.g. lathes (C03B37/01884 takes precedence) · CPC title

• C03B37/01446 Primary

  Thermal after-treatment of preforms, e.g. dehydrating, consolidating, sintering (C03B37/01853 takes precedence) · CPC title

• C03B37/0146

  Furnaces therefor, e.g. muffle tubes, furnace linings · CPC title

• C03B37/027

  Fibres composed of different sorts of glass, {e.g. glass optical fibres}(C03B37/0253, C03B37/028 take precedence) · CPC title

• C03B37/0126 Primary

  Means for supporting, rotating, translating the rod, tube or preform · CPC title