Absorbable implants for plastic surgery

Patent metadata

Field	Value
Publication number	US-9655715-B2
Application number	US-201514694681-A
Country	US
Kind code	B2
Filing date	Apr 23, 2015
Priority date	Jul 11, 2013
Publication date	May 23, 2017
Grant date	May 23, 2017

Abstract

Absorbable implants for breast surgery that conform to the breast parenchyma and surrounding chest wall have been developed. These implants support newly lifted breast parenchyma, and/or a breast implant. The implants have mechanical properties sufficient to support a reconstructed breast, and allow the in-growth of tissue into the implant as it degrades. The implants have a strength retention profile allowing the support of the breast to be transitioned from the implant to regenerated host tissue, without significant loss of support. Three-dimensional implants for use in minimally invasive mastopexy/breast reconstruction procedures are also described, that confer shape to a patient's breast. These implants are self-reinforced, can be temporarily deformed, implanted in a suitably dissected tissue plane, and resume their preformed three-dimensional shape. The implants are preferably made from poly-4-hydroxybutyrate (P4HB) and copolymers thereof. The implants have suture pullout strengths that can resist the mechanical loads exerted on the reconstructed breast.

First claim

We claim:

1. An implant for securing a breast of a patient in a lifted position or contouring a patient's breast, the implant having a three-dimensional shape and comprising:
(a) a support component with an upper section, a lower section, medial side, lateral side, and an outlying border; and
(b) a shape memory component with rounded edges, wherein the shape memory component is a continuous or interrupted ring forming an outlying border to which the support component is attached,
wherein the support component comprises ribbing in the upper and lower sections of the support component.

2. The implant of claim 1 wherein the support component comprises a mesh, a set of strips, a fabric, a woven construct, a non-woven construct, a knitted construct, a braided construct, scaffold, a porous film, a nanospun, electrospun, or melt-blown construct.

3. The implant of claim 2 wherein the support component comprises a thin mesh defining a body and plurality of tabs extending therefrom; wherein the shape memory component comprises a rib extending along a perimeter of the body of the mesh and wherein the rib urges the body to assume a three dimensional predetermined shape following release from a constrained shape.

4. The implant of claim 1 wherein the implant assumes a preformed shape following temporary deformation.

5. The implant of claim 1 wherein the three-dimensional shape is selected from the group consisting of a partial dome, dome, a crescent-shape, rectangle, hemisphere, hemi-ellipsoid, a canoe shape, a shape with a width of 8 to 20 cm at the base, a shape with a height or radius of curvature of 5 to 14 cm, a shape with a width that is 1 to 2 cm less than the width of the patient's breast when measured prior to surgery, and a shape with a height that is 0.5 to 5 cm less than the patient's nipple inframammary fold distance after mastopexy.

6. The implant of claim 1 wherein buckling or bunching of the implant is minimized upon placement.

7. The implant of claim 1 wherein the shape memory component has continuous dimensions or wherein the shape memory component has variable dimensions.

8. An implant for securing a breast of a patient in a lifted position or contouring a patient's breast, the implant having a three-dimensional shape and comprising:
(a) a support component with an upper section, a lower section, medial side, lateral side, and an outlying border; and
(b) a shape memory component with rounded edges;
wherein the dimensions of the shape memory component decrease from the middle of the implant towards the medial and lateral sides of the implant.

9. The implant of claim 1 further comprising one or more tabs radially extending from the outlying border.

10. The implant of claim 9 comprising between two and twenty tabs.

11. The implant of claim 9 comprising a medial tab and a lateral tab.

12. The implant of claim 9 comprising between one and eighteen tabs between the medial and lateral tabs.

13. The implant of claim 10 comprising three tabs on each of the upper and lower sections between the medial and lateral tabs.

14. The implants of claim 9 wherein the tabs have widths ranging from 1-3 cm, and lengths ranging from 2-4 cm.

15. The implant of claim 7 further comprising a plurality of sutures extending through said tabs and for securing the tabs to supportive tissue.

16. The implant of claim 1 further comprising one or more orientation marks.

17. The implant of claim 1 wherein the implant has unidirectional or bidirectional curvature.

18. The implant of claim 17 wherein the curvature is either in the medial to lateral plane, or in the plane perpendicular to the medial to lateral plane, or in both planes.

19. The implant of claim 3 , wherein the rib is fused to the mesh.

20. The implant of claim 19 , wherein the rib comprises an absorbable material.

21. The implant of claim 3 , wherein the body comprises a rounded corner.

22. The implant of claim 21 , wherein a tab extends from the rounded corner.

23. The implant of claim 3 comprising a plurality of upper tabs spaced between a medial tab and a lateral tab.

24. The implant of claim 1 wherein the rounded edges of the shape memory component are at the medial and lateral sides of the implant.

25. The implant of claim 1 wherein the shape memory component is made from a filament, thread, strand, string, fiber, yarn, wire, film, tape, tube, fabric, felt, mesh, multifilament, or monofilament.

26. The implant of claim 1 wherein the support component comprises a mesh, monofilament mesh, multifilament mesh, strips, fabrics, woven constructs, non-woven constructs, knitted constructs, braided constructs, porous scaffolds, laminates, nanospuns, electrospuns, dry spuns, or melt-blown constructs, filaments, threads, strands, strings, fibers, yarns, wires, films, tapes, felts, foams, multifilaments and monofilaments.

27. The implant of claim 1 wherein either the support component or the shape memory component is resorbable, or wherein both the support component and the shape memory components are resorbable.

28. The implant of claim 1 wherein the support component is made from silk, silk fibroin, a polymer comprising glycolic acid, lactic acid, 1,4-dioxanone, trimethylene carbonate, 3-hydroxybutyric acid, ε-caprolactone, or 4-hydroxybuyrate.

29. The implant of claim 1 wherein the shape memory component comprises a polymer comprising glycolic acid, lactic acid, 1,4-dioxanone, trimethylene carbonate, 3-hydroxybutyric acid, ε-caprolactone, or 4-hydroxybuyrate.

30. The implant of claim 1 wherein the support component is made from a monofilament knitted mesh of poly-4-hydroxybutyrate and the shape memory component is made from poly-4-hydroxybutyrate extrudate.

31. The implant of claim 1 wherein the implant is replaced in vivo with regenerated host tissue that can support a reconstructed breast.

32. The implant of claims claim 1 wherein the implant cannot stretch more than 30% in any direction.

33. A method of forming the implant of claim 1 the method comprising the steps of:
(a) providing a first split metal mold comprising two halves and having a semicircular groove in one half of the mold;
(b) placing a shape memory component material selected from the group consisting of a filament, thread, strand, string, fiber, yarn, wire, film, tape, tube, fabric, felt, mesh, multifilament, or monofilament in the semicircular groove so that it forms a ring;
(c) placing a support component material between the molding halves, and clamping the two halves of the split metal mold together to form a block;
(d) heating the block at a temperature between 50° C. and 70° C.; cooling the block at a temperature between 0° C. and 25° C.; disassembling and removing a molded shape from the block;
(e) cutting the molded shape to remove unwanted shape memory material and mesh;
(f) placing the cut molded shape form in a second split metal mold consisting of an inwardly curving half and an outwardly curving half;
(g) clamping the halves of the mold together to form a block;
(h) heating the block at a temperature between 40° C. and 52° C.;
(i) cooling the block at a temperature between 0° C. and 25° C.;
(j) disassembling and removing the implant.

34. The method of claim 33 wherein the support compo

Assignees

• Tepha Inc

Inventors

• Limem Skander
• Stires Emily
• Marciante Rebecca
• Rizk Said
• Moses Arikha
• Felix Fabio
• Natta Bruce Van

Classifications

• B29C47/004

  Operations & Transport · mapped topic

• C08L67/04

  Polyesters derived from hydroxycarboxylic acids, e.g. lactones (C08L67/06 takes precedence) · CPC title

• A61F2230/0076

  ellipsoidal or ovoid · CPC title

• B29K2067/04

  Polyesters derived from hydroxycarboxylic acids · CPC title

• A61L27/58

  Materials at least partially resorbable by the body · CPC title