Seamless steel pipe for line pipe

Patent metadata

Field	Value
Publication number	US-9651175-B2
Application number	US-201414909152-A
Country	US
Kind code	B2
Filing date	Jun 13, 2014
Priority date	Aug 6, 2013
Publication date	May 16, 2017
Grant date	May 16, 2017

Abstract

There is provided a seamless steel pipe for line pipe, wherein a chemical composition consists, by mass percent, of C: 0.03-0.10%, Si: ≦0.50%, Mn: 1.0-2.0%, P: ≦0.050%, S: ≦0.005%, Cr: 0.05-1.0%, Mo: 0.01-0.30%, Al: 0.001-0.10%, N: ≦0.01%, Ni: 0.04-2.0%, Ca: 0.0005-0.0050%, Cu: 0-2.0%, Ti: 0-0.05%, Nb: 0-0.05%, V: 0-0.10%, the balance: Fe and impurities, and satisfies the conditions of Cu+Ni: ≧0.10%, and Mo+V: ≦0.30%, wherein in a scale formed on the surface of the steel pipe, metal particles consisting mainly of Ni or Cu having an average circle-equivalent diameter of 0.1-5 μm exist, and a distance from a boundary between the base metal of the steel pipe and the scale to a region in which the metal particles do not exist is 20 μm or longer.

First claim

What is claimed is:

1. A seamless steel pipe for line pipe, wherein a chemical composition consists, by mass percent, of
C: 0.03 to 0.10%,
Si: 0.50% or less,
Mn: 1.0 to 2.0%,
P: 0.050% or less,
S: 0.005% or less,
Cr: 0.05 to 1.0%,
Mo: 0.01 to 0.30%,
Al: 0.001 to 0.10%,
N: 0.01% or less,
Ni: 0.04 to 2.0%,
Ca: 0.0005 to 0.0050%,
Cu: 0 to 2.0%,
Ti: 0 to 0.05%,
Nb: 0 to 0.05%,
V: 0 to 0.10%,
the balance: Fe and impurities, and
the chemical composition satisfies the conditions of
Cu+Ni: 0.10% or more, and
Mo+V: 0.30% or less, wherein
in a scale formed on the surface of the steel pipe, metal particles comprising Ni or Cu having an average circle-equivalent diameter of 0.1 to 5 μm exist, and a distance from a boundary between the base metal of the steel pipe and the scale to a region in which the metal particles do not exist is 20 μm or longer.

2. The seamless steel pipe for line pipe according to claim 1 , wherein
the chemical composition contains, by mass percent,
one or more elements selected from
Cu: 0.01 to 2.0%,
Ti: 0.003 to 0.05%,
Nb: 0.01 to 0.05%, and
V: 0.02 to 0.10%.

3. The seamless steel pipe for line pipe according to claim 1 , wherein
the chemical composition consists, by mass percent, of
C: 0.03 to 0.10%,
Si: 0.30% or less,
Mn: 1.00 to 1.80%,
P: 0.020% or less,
S: 0.003% or less,
Ti: 0.001 to 0.015%,
Al: 0.001 to 0.050%,
Ni: 0.04 to 0.30%,
Cu: 0 to 0.30%,
Cr: 0.05 to 0.40%,
Mo: 0.02 to 0.15%,
V: 0.02 to 0.09%,
Ca: 0.0005 to 0.0030%,
N: 0.008% or less,
the balance: Fe and impurities, and
the chemical composition satisfies the conditions of
Cu+Ni: 0.10 to 0.50%, and
Mo+V: 0.05 to 0.20%.

4. The seamless steel pipe for line pipe according to claim 3 , wherein the highest hardness at a position 1 mm deep from the surface is 230 HV10 or lower.

5. The seamless steel pipe for line pipe according to claim 1 , wherein:
a metal micro-structure of the steel pipe contains bainite of 50% or more in area fraction; and
a wall thickness of the steel pipe is 30 mm or larger.

6. The seamless steel pipe for line pipe according to claim 1 , wherein at a position 10 μm distant from the boundary to the scale side, the number density of the metal particles observed per unit area is 5×10 3 pieces/mm 2 or higher.

7. The seamless steel pipe for line pipe according to claim 1 , wherein a difference between the average hardness at the position 1 mm deep from the surface of the steel pipe and the average hardness in the central portion of the wall thickness is 30 HV10 or smaller.

8. The seamless steel pipe for line pipe according to claim 1 , wherein a difference between the maximum value and the minimum value of the hardness at the position 1 mm deep from the surface of the steel pipe is 40 HV10 or smaller.

Assignees

• Nippon Steel & Sumitomo Metal Corp

Inventors

• Arai Yuji
• Ueda Yukimasa
• Murata Kei
• Hidaka Yasuyoshi

Classifications

• C21D8/10

  during manufacturing of tubular bodies · CPC title

• C21D9/08 Primary

  for tubular bodies or pipes · CPC title

• Y10T428/12611

  Oxide-containing component · CPC title

• C21D6/004

  containing Cr and Ni · CPC title

• C22C38/40

  with nickel · CPC title