Surface modified calcium carbonate containing minerals and its use

Patent metadata

Field	Value
Publication number	US-9650517-B2
Application number	US-201314408630-A
Country	US
Kind code	B2
Filing date	Jul 10, 2013
Priority date	Jul 13, 2012
Publication date	May 16, 2017
Grant date	May 16, 2017

Abstract

The present invention is related to ball-shaped spherical surface modified spherical calcium carbonate comprising minerals, the process for preparing such ball-shaped spherical surface modified spherical calcium carbonate comprising minerals, and their use.

First claim

The invention claimed is:

1. A process for producing ball-shaped spherical surface modified calcium carbonate comprising particles comprising the steps of:
a) providing at least one aqueous calcium carbonate containing mineral slurry;
b) providing at least one water-soluble acid;
c) providing gaseous CO 2 generated in situ and/or supplied externally;
d) contacting the aqueous calcium carbonate containing mineral slurry of step a) with the acid of step b) and with the CO 2 of step c) under stirring conditions to obtain ball-shaped spherical surface modified calcium carbonate comprising particles; and
e) optionally dewatering the aqueous slurry,
wherein at least one processing agent is added before, during or after the aqueous calcium carbonate containing mineral slurry of step a) is contacted with the acid of step b) and the CO 2 of step c), and
wherein the processing agent is selected from the group consisting of ferrous sulfate, ferric sulfate, ferrous chloride, aluminum sulfate, and their hydrated forms, and
wherein the processing agent is added in an amount of up to 8 wt.- % based on the dry weight of the slurry.

2. The process according to claim 1 , wherein the calcium carbonate containing mineral is selected from the group consisting of marble, chalk, limestone, calcite, dolomite, precipitated calcium carbonate (PCC), and any mixture thereof.

3. The process according to claim 1 , wherein the calcium carbonate containing mineral in the slurry has a weight median particle diameter of 0.01 μm to 10 μm.

4. The process according to claim 1 , wherein the calcium carbonate containing mineral in the slurry has a weight median particle diameter of 0.02 μm to 2 μm.

5. The process according to claim 1 , wherein the calcium carbonate containing mineral in the slurry has a weight median particle diameter of 0.5 μm to 1 μm.

6. The process according to claim 1 , wherein the slurry of step a) has a solids content of greater than 4 wt.- %, based on the weight of the slurry.

7. The process according to claim 1 , wherein the slurry of step a) has a solids content of from 5 wt.- % to about 20 wt.- %, based on the weight of the slurry.

8. The process according to claim 1 , wherein the slurry of step a) is stabilized by the addition of one or more dispersants.

9. The process according to claim 1 , wherein the at least one water-soluble acid of step b) has a pK a from 0 to 6.

10. The process according to claim 1 , wherein the at least one water-soluble acid of step b) has a pK a from 0 to 2.5.

11. The process according to claim 1 , wherein the at least one water-soluble acid of step b) is phosphoric acid, citric acid, boric acid, or any mixture thereof.

12. The process according to claim 1 , wherein the at least one water-soluble acid is dosed in a molar amount relative to the numbers of moles of the calcium carbonate containing mineral in the range from 0.01 mol/mol to about 1 mol/mol.

13. The process according to claim 1 , wherein the at least one water-soluble acid is dosed in a molar amount relative to the numbers of moles of the calcium carbonate containing mineral in the range from 0.1 to 0.6 mol/mol.

14. The process according to claim 1 , wherein the at least one water-soluble acid provided in step b) is added in one or more steps to the aqueous calcium carbonate containing mineral slurry.

15. The process according to claim 1 , wherein the at least one water-soluble acid provided in step b) is added in one step to the aqueous calcium carbonate containing mineral slurry.

16. The process according to claim 1 , wherein the addition of the at least one water-soluble acid of step b) and the contacting of the aqueous calcium carbonate containing mineral slurry of step a) with the acid of step b) and with the CO 2 generated in situ and/or supplied externally of step d) take place in a stirred reactor under stirring conditions such as to develop a laminar flow.

17. The process according to claim 1 , wherein the process takes place in an aqueous environment in a temperature range above and including 20° C.

18. The process according to claim 1 , wherein the process takes place in an aqueous environment in a temperature range from 25° C. to 95° C.

19. The process according to claim 1 , wherein the process takes place in an aqueous environment in a temperature range from 30° C. to 80° C.

20. The process according to claim 1 , wherein the process takes place in an aqueous environment in a temperature range from 50° C. to 75° C.

21. The process according to claim 1 , wherein the processing agent is added in an amount of from 0.01 wt. % to 5 wt. % based on the dry weight of the slurry.

22. The process according to claim 1 , wherein the processing agent is added in an amount of from 0.4 wt. % to 3 wt. % based on the dry weight of the slurry.

23. The process according to claim 1 , wherein the processing agent is dosed in one or more steps to the aqueous calcium carbonate containing mineral slurry.

24. The process according to claim 1 , wherein the processing agent is dosed in one step to the aqueous calcium carbonate containing mineral slurry.

25. The process according to claim 1 , wherein the processing agent is aluminum sulfate or its hydrate.

26. The process according to claim 1 , wherein the processing agent is aluminum sulfate hexadecahydrate.

27. The process according to claim 25 , wherein the aluminum sulfate is added up to 5 wt. % based on the weight of the dry slurry.

28. The process according to claim 1 , wherein the processing agent is added before, during or after step b).

Assignees

• Omya Int Ag

Inventors

• Gerard Daniel Edward
• Schoelkopf Joachim
• Gane Patrick Arthur Charles
• Lehner Fritz
• Werner Dennis

Classifications

• C09C1/02 Primary

  Compounds of alkaline earth metals or magnesium {(C09C1/0003, C09C1/0009, C09C1/0015, C09C1/0078 take precedence; dolomitic solids C09C1/009)} · CPC title

• C01P2004/32

  Spheres · CPC title

• D21H17/00

  Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution · CPC title

• D21H17/675

  Oxides, hydroxides or carbonates · CPC title

• C09C1/021 Primary

  Calcium carbonates · CPC title