Process for the preparation of nitrile rubbers

Patent metadata

Field	Value
Publication number	US-9650502-B2
Application number	US-201214127831-A
Country	US
Kind code	B2
Filing date	Jun 26, 2012
Priority date	Jun 27, 2011
Publication date	May 16, 2017
Grant date	May 16, 2017

Abstract

Process for the preparation of a nitrile rubber comprising: —subjecting at least one α,β-unsaturated nitrile, at least one conjugated diene and, optionally, one or more further copolymerizable monomers, to emulsion polymerization, in the presence of at least one alkyl thiol containing from 12 to 16 carbon atoms and at least three tertiary carbon atoms and having the sulfur bound to one of said tertiary carbon atoms, at a pH ranging from 7 to 10, preferably from 8 to 9, obtaining a latex; —subjecting said latex to coagulation, in the presence of at least one metal sulfate selected from magnesium, sodium, potassium, preferably magnesium, at a temperature higher than or equal to 30° C., preferably ranging from 40° C. to 60° C., obtaining a coagulated nitrile rubber: —subjecting said coagulated nitrile rubber to washing with water, in the presence of at least one inorganic base, selected from sodium hydroxide, potassium hydroxide, calcium hydroxide, magnesium hydroxide, lithium hydroxide, preferably potassium hydroxide, at a pH higher than or equal to 10, preferably ranging from 11 to 12. The nitrile rubber thus obtained is capable of giving vulcanizable elastomeric compositions having a high vulcanization rate and a good vulcanization yield. Furthermore, said elastomeric compositions cause a low fouling of the molds and can consequently be advantageously used in injection molding processes.

First claim

The invention claimed is:

1. A process for the preparation of a nitrile rubber comprising:
subjecting at least one α,β-unsaturated nitrile, at least one conjugated diene and, optionally, one or more further copolymerizable monomers, to emulsion polymerization, in the presence of at least one alkyl thiol containing from 12 to 16 carbon atoms and at least three tertiary carbon atoms and having the sulfur bound to one of said tertiary carbon atoms, at a pH ranging from 7 to 10, obtaining a latex;
subjecting said latex to coagulation, in the presence of at least one metal sulfate selected from magnesium, sodium, and potassium, at a temperature higher than or equal to 30° C., obtaining a coagulated nitrile rubber; and
subjecting said coagulated nitrile rubber to washing with water, wherein to said water is added at least one inorganic base, selected from sodium hydroxide, potassium hydroxide, calcium hydroxide, magnesium hydroxide, and lithium hydroxide, at a pH higher than or equal to 10.

2. The process for the preparation of nitrile rubber according to claim 1 , wherein said emulsion polymerization is carried out at a pH ranging from 8 to 9.

3. The process for the preparation of nitrile rubber according to claim 1 , wherein said coagulation is carried out in the presence of magnesium sulfate.

4. The process for the preparation of nitrile rubber according to claim 1 , wherein said coagulation is carried out at a temperature ranging from 40° C. to 60° C.

5. The process for the preparation of nitrile rubber according to claim 1 , wherein said washing with water is carried out in the presence of potassium hydroxide.

6. The process for the preparation of nitrile rubber according to claim 1 , wherein said washing with water is carried out at a pH ranging from 11 to 12.

7. The process for the preparation of nitrile rubber according to claim 1 , wherein said α,β-unsaturated nitrile is selected from α,β-unsaturated nitriles having from 3 to 5 carbon atoms.

8. The process for the preparation of nitrile rubber according to claim 1 , wherein said conjugated diene is selected from conjugated dienes having from 4 to 6 carbon atoms.

9. The process for the preparation of nitrile rubber according to claim 1 , wherein said nitrile rubber is an acrylonitrile-butadiene (NBR) copolymer.

10. The process for the preparation of nitrile rubber according to claim 1 , wherein said one or more copolymerizable monomers are selected from α,β-unsaturated monocarboxylic or dicarboxylic acids, their esters or their amides, or mixtures thereof.

11. The process for the preparation of nitrile rubber according to claim 1 , wherein said alkyl thiol is selected from: 2,2,4,6,6-pentamethylheptane-4-thiol, 2,4,4,6,6,8,8-pentamethyl-nonane-4-thiol, or mixtures thereof.

12. The process for the preparation of nitrile rubber according to claim 11 , wherein said alkyl thiol is 2,2,4,6,6-pentamethylheptane-4-thiol.

13. The process for the preparation of nitrile rubber according to claim 1 , wherein said alkyl thiol is a mixture comprising:
2,2,4,6,6-pentamethylheptane-4-thiol;
2,4,4,6,6-pentamethylheptane-2-thiol;
2,3,4,6,6-pentamethylheptane-2-thiol; and
2,3,4,6,6-pentamethylheptane-3-thiol.

14. The process for the preparation of nitrile rubber according to claim 1 , wherein said alkyl thiol is used in an amount ranging from 0.05 parts by weight to 3 parts by weight per 100 parts by weight of the mixture of polymerization monomers.

15. The process for the preparation of nitrile rubber according to claim 1 , wherein said metal sulfate is present in the latex in an amount ranging from 0.5 phr to 200 phr.

16. The process for the preparation of nitrile rubber according to claim 1 , wherein the latex obtained from the polymerization has a concentration of solids ranging from 1% by weight to 40% by weight with respect to the total weight of the latex.

17. The process for the preparation of nitrile rubber according to claim 1 , wherein said washing with water is carried out at a temperature ranging from 35° C. to 90° C.

18. The process for the preparation of nitrile rubber according to claim 1 , wherein the amount of water used in said washing with water ranges from 0.5 phr to 20 phr.

19. A vulcanizable elastomeric composition comprising at least one nitrile rubber obtained according to claim 1 and at least one vulcanizing agent.

20. A method comprising:
injection moulding a vulcanizable elastomeric composition according to claim 19 .

Assignees

• Lima Romano
• Santi Davide
• Versalis Spa

Inventors

• Lima Romano
• Santi Davide

Classifications

• C08F236/12

  with nitriles · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• C08C3/02

  Purification · CPC title

• C08C1/15 Primary

  characterised by the coagulants used · CPC title

• C08C1/14

  Coagulation · CPC title