Surface modified calcium carbonate containing minerals and its use

Patent metadata

Field	Value
Publication number	US-9637637-B2
Application number	US-201615272771-A
Country	US
Kind code	B2
Filing date	Sep 22, 2016
Priority date	Jul 13, 2012
Publication date	May 2, 2017
Grant date	May 2, 2017

Abstract

The present invention is related to ball-shaped spherical surface modified spherical calcium carbonate comprising minerals, the process for preparing such ball-shaped spherical surface modified spherical calcium carbonate comprising minerals, and their use.

First claim

The invention claimed is:

1. A product obtained by a process for producing ball-shaped spherical surface modified calcium carbonate comprising particles, wherein the process comprises the steps of:
a) providing at least one aqueous calcium carbonate containing mineral slurry;
b) providing at least one water-soluble acid;
c) providing gaseous CO 2 generated in situ and/or supplied externally;
d) contacting the aqueous calcium carbonate containing mineral slurry of step a) with the acid of step b) and with the CO 2 of step c) under stirring conditions to obtain ball-shaped spherical surface modified calcium carbonate comprising particles; and
e) optionally dewatering the aqueous slurry,
wherein at least one processing agent is added before, during or after the aqueous calcium carbonate containing mineral slurry of step a) is contacted with the acid of step b) and the CO 2 of step c), and
wherein the processing agent is selected from the group consisting of ferrous sulfate, ferric sulfate, ferrous chloride, aluminum sulfate, and their hydrated forms, and
wherein the processing agent is added in an amount of up to 8 wt. % based on the dry weight of the slurry.

2. The product according to claim 1 , wherein the calcium carbonate containing mineral of step a) is selected from the group consisting of marble, chalk, limestone, calcite, dolomite, precipitated calcium carbonate (PCC), and any mixture thereof.

3. The product according to claim 1 , wherein the calcium carbonate containing mineral of step a) has a weight median particle diameter of 0.01 μm to 10 μm.

4. The product according to claim 1 , wherein the calcium carbonate containing mineral of step a) has a weight median particle diameter of 0.02 μm to 2 μm.

5. The product according to claim 1 , wherein the slurry of step a) is stabilized by the addition of one or more dispersants.

6. The product according to claim 1 , wherein the at least one water-soluble acid of step b) is phosphoric acid, citric acid, boric acid, or any mixture thereof.

7. The product according to claim 1 , wherein the at least one water-soluble acid is dosed in a molar amount relative to the numbers of moles of the calcium carbonate containing mineral in the range from 0.01 mol/mol to 1 mol/mol.

8. The product according to claim 1 , wherein the processing agent is added in an amount of from 0.01 wt. % to 5 wt. % based on the dry weight of the slurry.

9. The product according to claim 1 , wherein the processing agent is added in an amount of from 0.4 wt. % to 3 wt. % based on the dry weight of the slurry.

10. The product according to claim 1 , wherein the processing agent is aluminum sulfate or its hydrate.

11. The product according to claim 1 , wherein the processing agent is aluminum sulfate hexadecahydrate.

12. The product according to claim 11 , wherein the aluminum sulfate is added up to 5 wt. % based on the weight of the dry slurry.

13. The product according to claim 11 , which is in the form of a slurry.

14. The product according to claim 11 , which is dried.

15. The product according to claim 1 , wherein the surface modified calcium carbonate has a median grain diameter of from 4 μm to about 100 μm.

16. The product according to claim 1 , wherein the surface modified calcium carbonate has a median grain diameter of from 10 μm to 50 μm.

17. The product according to claim 1 , wherein the surface modified calcium carbonate has a median grain diameter of from 15 μm to 30 μm.

18. The product according to claim 1 , wherein the surface modified calcium carbonate has a BET specific surface area of more than 15 m 2 /g.

19. The product according to claim 1 , wherein the surface modified calcium carbonate has a BET specific surface area of 20 m 2 /g to 200 m 2 /g.

20. The product according to claim 1 , wherein the surface modified calcium carbonate has a BET specific surface area of 30 m 2 /g to 150 m 2 /g.

21. The product according to claim 1 , wherein the surface modified calcium carbonate has a BET specific surface area of 40 m 2 /g to 100 m 2 /g.

22. The product according to claim 1 , wherein the surface modified calcium carbonate has a BET specific surface area of 30 m 2 /g to about 90 m 2 /g and a median grain diameter from 10 μm to 50 μm.

23. The product according to claim 1 , wherein the surface modified calcium carbonate has a particle size distribution d 98 /d 50 smaller than 3.

24. The product according to claim 1 , wherein the surface modified calcium carbonate has a particle size distribution d 98 /d 50 smaller than 2.5.

25. The product according to claim 1 , wherein the surface modified calcium carbonate has a particle size distribution d 98 /d 50 from 1.4 to 2.9.

26. Paint or coating comprising the product of claim 1 in slurry or dried form.

27. The paint or coating according to claim 26 , wherein the surface modified calcium carbonate in slurry or dried form is used as a matting agent in paints and coatings.

28. The paint or coating according to claim 27 , wherein the matting agent is present in an amount of 1 to 10 wt. %, based on the wet paint.

29. The paint or coating according to claim 27 , wherein the dried paint or coating has a gloss at 85° in the range of below 10, when measured according to DIN 67 530.

30. Paper, tissue paper, digital photo paper, a paint, a coating, an adhesive, a plastic, or waste water treating agent comprising or made with the product according to claim 1 in slurry or dried form.

Assignees

• Omya Int Ag

Inventors

• Gerard Daniel Edward
• Schoelkopf Joachim
• Gane Patrick Arthur Charles
• Lehner Fritz
• Werner Dennis

Classifications

• C01P2006/22

  Rheological behaviour as dispersion, e.g. viscosity, sedimentation stability · CPC title

• D21H15/02

  characterised by configuration · CPC title

• C01P2004/51

  Particles with a specific particle size distribution · CPC title

• D21H17/00

  Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution · CPC title

• C01P2004/32

  Spheres · CPC title