Method for the production and stabilization of impact-modified polycarbonate compositions using diluted solutions of acidic compounds

Patent metadata

Field	Value
Publication number	US-9637632-B2
Application number	US-201214353827-A
Country	US
Kind code	B2
Filing date	Oct 23, 2012
Priority date	Oct 26, 2011
Publication date	May 2, 2017
Grant date	May 2, 2017

Abstract

The present invention relates to a process for the preparation of stabilized impact-modified polycarbonate compositions using dilute aqueous acidic solutions, and to the compositions so prepared themselves.

First claim

The invention claimed is:

1. A process for preparing an impact-modified polymer composition comprising
A) from 10 to 98 parts by weight, based on the sum of components A+B+C+D+E, of at least one polymer selected from the group consisting of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters, as well as mixtures thereof,
B) from 0.5 to 50.0 parts by weight, based on the sum of components A+B+C+D+E, of at least one pulverulent rubber-modified vinyl (co)polymer,
C) from 0 to 80 parts by weight, based on the sum of components A+B+C+D+E, of at least one component selected from the group consisting of rubber-modified vinyl (co)polymers in granulate form and rubber-free vinyl (co)polymers,
D) from 0.002 to 0.200 part by weight, based on the sum of components A+B+C+D+E, of at least one Brönsted acid,
E) from 0.1 to 40.0 parts by weight, based on the sum of components A+B+C+D+E, of one or more additives, with the exception of the Brönsted acid according to component D,
wherein the sum of the parts by weight of components A+B+C+D+E in the impact-modified polymer composition is 100,

the process comprising:
(i) preparing a solution comprising the at least one Brönsted acid of component D with a concentration of from 0.3 to 30 wt. % in a solvent,
(ii) physically blending the solution comprising the at least one Brönsted acid from (i) with the total amount or a partial amount of the at least one pulverulent rubber-modified vinyl (co)polymer of component B to form a mixture, wherein the solution comprising the at least one Brönsted acid is present in the mixture in an amount, based on the sum of components B and D in the mixture, of not more than 30 parts by weight, and
(iii) melting, mixing and dispersing in one another the mixture from (ii) with the further and/or residual components A-E of the impact-modified polymer composition, which have optionally been premixed, in a compounding unit to produce the impact-modified polymer composition in the form of a polymer melt,
wherein the solvent that has been added to the impact-modified polymer composition by the solution comprising the at least one Brönsted acid is removed in a degassing zone of the compounding unit by application of an absolute pressure of not more than 800 mbar, and
wherein the polymer melt solidified by cooling and then granulated.

2. The process according to claim 1 , wherein in (ii), in addition to the solution comprising the at least one Brönsted acid, one or more additives of component E are also mixed with component B, wherein the one or more additives mixed with component B comprise one or more stabilizers.

3. The process according to claim 1 , wherein in (ii), component B and the solution comprising the at least one Brönsted acid are first mixed, before one or more further pulverulent components are added.

4. The process according to claim 1 , wherein the amount of component B physically blended in (ii) is not more than 10 parts by weight, based on the total composition.

5. The process according to claim 1 , wherein the amount of component B physically blended in (ii) is from 1.5 to 5.0 parts by weight, based on the total composition.

6. The process according to claim 1 , wherein the solution comprising the at least one Brönsted acid is used in the mixture prepared in (ii) in an amount, based on the sum of components B and D therein, of not more than 20 parts by weight.

7. The process according to claim 1 , wherein the solvent in (i) is an inorganic solvent.

8. The process according to claim 1 , wherein the solvent in (i) is water.

9. The process according to claim 1 , wherein the impact-modified polymer composition comprises
from 55 to 65 parts by weight of said component A,
from 1.5 to 5.0 parts by weight of said component B,
from 20 to 40 parts by weight of said component C,
from 0.007 to 0.020 part by weight of said component D,
from 0.5 to 3.0 parts by weight of one or more additives, with the exception of said acid that is added in component D, of component E, and
wherein the sum of the parts by weight of components A+B+C+D+E in the composition is 100.

10. The process according to claim 1 , wherein in (i) the solution comprising the at least one Brönsted acid is prepared with a concentration of from 1 to 6 wt. % in the solvent.

11. The process according to claim 1 , wherein the at least one Brönsted acid is selected from the group consisting of Brönsted-acidic phosphorus compounds in which the phosphorus has oxidation state +3 or +5.

12. The process according to claim 1 , wherein the at least one Brönsted acid comprises is ortho-phosphoric acid.

Assignees

• Covestro Deutschland Ag

Inventors

• Seidel Andreas
• Thiem Hans-Juergen

Classifications

• C08J2433/20

  Homopolymers or copolymers of acrylonitrile (C08J2455/02 takes precedence) · CPC title

• C08J2409/00

  Characterised by the use of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08L25/12

  with unsaturated nitriles · CPC title

• C08L67/02

  Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence) · CPC title

• C08L55/02

  ABS [Acrylonitrile-Butadiene-Styrene] polymers · CPC title