Abstract

The invention relates to a process for the preparation of a masterbatch of diene elastomer and reinforcing inorganic filler in accordance with the invention comprises the following successive stages:
bringing into contact and mixing one or more aqueous dispersions (B) of one or more hydrophobized reinforcing inorganic fillers, which coagulate(s) spontaneously with the said latex, and one or more diene elastomer latexes (A) in order to obtain a coagulum, without requiring a coagulating agent, recovery of the coagulum, then drying the recovered coagulum in order to obtain the masterbatch.

First claim

The invention claimed is:

1. Process for the preparation of a masterbatch of diene elastomer and reinforcing inorganic filler comprising the following successive stages: bringing into contact and mixing one or more aqueous dispersions (B) of one or more hydrophobized reinforcing inorganic fillers, which coagulate(s) spontaneously with the said latex, and one or more diene elastomer latexes (A) in order to obtain a coagulum, without requiring a coagulating agent, recovery of the coagulum, then drying the recovered coagulum in order to obtain the masterbatch.

2. Process according to claim 1 , wherein recovery of the coagulum is carried out by a filtering operation.

3. Process according to claim 1 , wherein recovery of the coagulum is carried out by a centrifuging operation.

4. Process according to claim 1 , wherein the diene elastomer latex is a natural rubber latex.

5. Process according to claim 4 , characterized in that the diene elastomer latex is a concentrated natural rubber latex.

6. Process according to claim 1 , wherein the filler is chosen from silica (SiO 2 ), alumina (Al 2 O 3 ), alumina monohydrate (Al 2 O 3 .H 2 O), aluminum hydroxide [Al(OH) 3 ], aluminum carbonate [Al 2 (CO 3 ) 3 ], magnesium hydroxide [Mg(OH) 2 ], magnesium oxide (MgO), magnesium carbonate (MgCO 3 ), talc (3MgO.4SiO.2.H 2 O), attapulgite (5MgO.8SiO 2 . 9H 2 O), titanium dioxide (TiO 2 ), titanium black (TiO 2n-1 ), calcium oxide (CaO), calcium hydroxide [Ca(OH) 2 ], aluminum magnesium oxide (MgO.Al 2 O 3 ), clay (Al2O 3 .2SiO 2 ), kaolin (Al 2 O 3 .2SiO 2 .2H 2 O), pyrophyllite (Al 2 O 3 .4SiO 2 .H 2 O), bentonite (Al 2 O 3 .4SiO 2 .2H 2 O), aluminum silicate (Al 2 SiO 5 .Al4(SiO 4 ) 3 .5H 2 O), magnesium silicate (Mg 2 SiO 4 .MgSiO 3 ), calcium silicate (Ca 2 SiO 4 ), aluminum calcium silicate (Al 2 O 3 .CaO.2SiO 2 ), calcium magnesium silicate (CaMgSiO 4 ), calcium carbonate (CaCO 3 ), zirconium oxide (ZrO 2 ), zirconium hydroxide [ZrO(OH) 2 .nH 2 O], zirconium carbonate [Zr(CO 3 ) 2 ], and crystalline aluminosilicates comprising atoms of hydrogen compensating for the charges, alkali metals or alkaline earth metals, and mixtures thereof.

7. Process according to claim 6 , wherein the filler is silica (SiO 2 ).

8. Process according to claim 1 , wherein the filler is hydrophobized using one or more hydrophobing agents of following formula (I):
E n -F  (Formula I)

in which:
n is an integer equal to 1 or 2,
when n has the value 1, then F is a monovalent group,
when n has the value 2, then F is a divalent group,
E represents a functional group which is capable of bonding physically and/or chemically to the filler and which comprises, in its structure, at least one alkyl or alkylene chain comprising from 1 to 18 carbon atoms which confers hydrophobing properties on the group E,
F represents a group which may or may not bond physically and/or chemically to the diene elastomer.

9. Process according to claim 8 , wherein the hydrophobing agent is of following formula (II):
[G( 3-m )(L-K) m Si-L-] n -F  (II)

with:
when n has the value 1, then F denotes the K group defined below and m varies from 0 to 2, and
when n has the value 2, then F denotes an amino group, a polysulphide (S x ) group or an epoxy group and m varies from 0 to 2,
and for which
the G groups are chosen, independently of one another, from a hydrogen atom, a C 1 -C 18 hydrocarbon group chosen from linear, branched or cyclic alkyl groups, aralkyl groups, alkylaryl groups and aryl groups, an alkoxy (R 1 O)— group, in which R 1 represents a saturated C 1 -C 8 alkyl radical, a halogen atom, and a hydroxyl group,
provided that at least one G group is chosen from an alkoxy group, a chlorine atom or a hydroxyl group,
L denotes a saturated or unsaturated and linear, branched or cyclic C 1 -C 18 alkylene radical, optionally comprising an oxygen atom,
K denotes a hydrogen atom, a halogen atom, or a functional group chosen from an amino group, a polyaminoalkyl group, a mercapto group, an epoxy group, a hydroxyl group, a vinyl group, an acryloyloxy group, a methacryloyloxy group, an —SCN group or an R(CO)S— group with R being a C 1 -C 18 alkyl group.

10. Process according to claim 9 , wherein m=0.

11. Process according to claim 10 , wherein the hydrophobing agent is of following formula (III):
G 3 Si-L-K  (III)

12. Process according to claim 10 , wherein the hydrophobing agent is of following formula (IV):
[G3Si-L-]2-F  (IV).

13. Process according to claim 8 , wherein the hydrophobing agent is chosen from chlorotrimethylsilane, chlorotriethylsilane, chlorotripropylsilane, bromotrimethylsilane, bromotriethylsilane, bromotripropylsilane, fluorotrimethylsilane, methoxytrimethylsilane, methoxytriethylsilane, methoxytripropylsilane, chlorotrimethylsilane, dichlorodimethylsilane, trichloromethylsilane, bromotrimethylsilane, dibromodimethylsilane, tribromomethylsilane, methoxytrimethylsilane, dimethoxydimethylsilane, trimethoxymethylsilane, tetramethoxysilane, trimethoxypropylsilane, trimethoxyoctylsilane, trimethoxyhexadecylsilane, dimethoxydipropylsilane, triethoxymethylsilane, triethoxypropylsilane, triethoxyoctylsilane, diethoxydimethylsilane, octenyldimethylchlorosilane, octadecyltrichlorosilane, (γ-aminopropyl)trimethoxysilane, (γ-aminopropyl)triethoxysilane, (γ-hydroxypropyl)tripropoxysilane, (γ-mercaptopropyl)triethoxysilane, (γ-aminopropyl)dimethylethoxysilane, (γ-aminopropyl)dihydroxymethoxysilane, (glycidylpropyl)trimethoxysilane, [γ-(N-aminoethyl)aminopropyl]triethoxysilane, (γ-methacryloyloxypropyl)triethoxysilane, (γ-methacryloyloxypropyl)trimethoxysilane, (β-mercaptoethyl)triethoxysilane, [γ-(N-aminoethyl)aminopropyl]trimethoxysilane, (N-methylaminopropyl)trimethoxysilane, (γ-thiocyanatopropyl)triethoxysilane, bis-(3-triethoxythiopropyl)silane tetrasulphide, vinyltriethoxysilane, vinylphenylmethylsilane, vinyldimethylmethoxysilane, divinyldimethoxysilane, divinylethyldimethoxysilane, dimethylvinylchlorosilane, bis(3-triethoxysilylpropyl)tetrasulphide and mixtures thereof.

14. Process according to claim 8 , wherein the hydrophobing agent, once attached to the filler, comprises at most 30 carbon atoms.

15. Process according to claim 8 , wherein the hydrophobing agent is selected from octenyldimethylchlorosilane, bis(3-triethoxysilylpropyl)tetrasulphide and mixtures thereof.

16. Process according to claim 8 , wherein the hydrophobized filler has a degree of hydrophobation of greater than or equal to 0.29 carbon atom carried by the hydrophobing agent, once attached to the filler, per nm2 of filler surface area.

17. Process according to claim 1 , wherein the process does not use a coagulating agent.

18. Process according to claim 9 , wherein aryl groups are chosen from a phenyl and a benzyl group.

19. Process according to claim 9 , wherein cyclic alkyl groups are chosen from a cvclopentyl and a cyclohexvl group.

20. Process according to claim 9 , wherein the C 1 -C 8 alkyl radical is chosen from methyl, ethyl and isopropyl groups.

21. Process according to claim 9 , wherein the C 1 -C 8 alkyl radical is chosen from at least one methyl and ethyl group.

22. Process according to claim 9 , wherein the halogen atom is chosen from fluorine, chlorine, bromine and iodine.

23. Process according to claim 9 , wherein C 1 -C 18 alkylene radical is of 1 to 8 carbon atoms.

24. Process according to claim 9 , wherein C 1 -C 18 alkylene radical is chosen from the methylene, ethylene, isoprop

Assignees

• Bibette Jérôme
• Martinez Pedrero Fernando
• De Gaudemaris Benoît
• Berriot Julien
• Michelin & Cie
• Michelin Rech Tech

Inventors

• Bibette Jérôme
• Martinez Pedrero Fernando
• De Gaudemaris Benoît
• Berriot Julien

Classifications

• B60C1/0016

  Compositions of the tread · CPC title

• C08J2307/02

  Latex · CPC title

• C08L21/00

  Compositions of unspecified rubbers · CPC title

• C08K3/013

  Fillers, pigments or reinforcing additives · CPC title

• C08J3/215

  at least one additive being also premixed with a liquid phase · CPC title