Weather-resistant pearlescent pigments, process for the production and use thereof

Patent metadata

Field	Value
Publication number	US-9631097-B2
Application number	US-201314432838-A
Country	US
Kind code	B2
Filing date	Sep 30, 2013
Priority date	Oct 2, 2012
Publication date	Apr 25, 2017
Grant date	Apr 25, 2017

Abstract

The present invention relates to weather-resistant pearlescent pigment, comprising
a coated or uncoated platelet-shaped substrate which is selected from the group consisting of synthetic mica platelets, glass platelets, SiO 2 platelets, Al 2 O 3 platelets, synthetic boehmite platelets, BiOCl platelets and mixtures thereof, a chromophoric coating with at least one highly refractive metal oxide, and a top layer, wherein the top layer comprises the following layer sequence:

a) a first layer made of tin oxide and/or tin hydroxide and/or hydrated tin oxide, b) a second cerium-containing layer which comprises cerium oxide and/or cerium hydroxide and/or hydrated cerium oxide, c) an organic-chemical coating applied to the cerium-containing layer which contains oligomeric silanes or consists of them, wherein the oligomeric silanes have one or more amino groups and the oligomeric silanes are chemically bonded with the cerium-containing layer. The invention further relates to a process for the production and use of these pearlescent pigments.

First claim

The invention claimed is:

1. A weather-resistant pearlescent pigment, comprising:
a coated or uncoated platelet-shaped substrate which is selected from the group consisting of synthetic mica platelets, glass platelets, SiO 2 platelets, Al 2 O 3 platelets, synthetic boehmite platelets, BiOCl platelets and mixtures thereof,
a chromophoric coating comprising at least one highly refractive metal oxide, and
a top layer,
wherein the top layer comprises the following layer sequence:
a) a first layer comprising tin oxide and/or tin hydroxide and/or hydrated tin oxide,
b) a second cerium-containing layer consisting of cerium oxide and/or cerium hydroxide and/or hydrated cerium oxide,
c) an organic-chemical coating applied to the cerium-containing layer which comprises one or more oligomeric silane(s), wherein the oligomeric silane(s) have one or more amino groups and the oligomeric silane(s) are chemically bonded with the cerium-containing layer.

2. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the substrate is selected from the group consisting of synthetic mica platelets, glass platelets and mixtures thereof.

3. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the proportion of tin oxide, tin hydroxide and/or hydrated tin oxide, calculated as SnO 2 , in the top layer lies in a range of from 0.4 to 4.0 wt.-%, relative to the total weight of the pearlescent pigment.

4. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the weight ratio of tin oxide, tin hydroxide and/or hydrated tin oxide, calculated as SnO 2 , to Ce, calculated as elemental Ce, in the top layer lies in a range of from 2 to 10.

5. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the proportion by weight of Ce, calculated as elemental Ce, in the top layer lies in a range of from 0.05 to 1.5 wt %, relative to the total weight of the pearlescent pigment.

6. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the proportion by weight of C (carbon proportion), lies in a range of from 0.03 to 0.5 wt.-%, relative to the total weight of the pearlescent pigment.

7. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the top layer consists of layers a), b) and c).

8. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the reaction products of the oligomeric silanes independently of one another have one or more alkyl groups of from 1 to 18 C atoms.

9. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the proportion of the top layer on all of the pearlescent pigment lies in a range of from 1.0 to 5.0 wt.-%, relative to the total weight of the pearlescent pigment.

10. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the coating of the pearlescent pigment with all of the top layer takes place in aqueous environment.

11. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the substrate is coated with one or more chromophoric, highly refractive metal oxide layer(s) which is selected from the group consisting of TiO 2 , Fe 2 O 3 , TiFe 2 O 5 , Fe 2 Ti 3 O 9 , FeTiO 3 and mixtures thereof.

12. The weather-resistant pearlescent pigment according to claim 11 , wherein,
the chromophoric, highly refractive coating comprises TiO 2 in the rutile structure.

13. The weather-resistant pearlescent pigment according to claim 12 , wherein,
the proportion of TiO 2 in the rutile structure lies in a range of from 30 to 80 wt.-%, relative to the total weight of the pearlescent pigment.

14. The weather-resistant pearlescent pigment according to claim 12 , wherein,
the chromophoric, highly refractive coating with TiO 2 in the rutile structure has an average thickness which lies in a range of from 80 to 280 nm.

15. The weather-resistant pearlescent pigment according to claim 1 , wherein,
the weather-resistant pearlescent pigment has a cumulative frequency distribution based on a volume-averaged size distribution function with the values D 10 , D 50 , D 90 , with a span ΔD of from 0.7-1.4, wherein the span ΔD is calculated according to Formula (I):
Δ D =( D 90 −D 10 )/ D 50   (I).

16. The weather-resistant pearlescent pigment according to claim 15 , wherein,
the pearlescent pigment has a span ΔD in a range of from 0.75-1.3.

17. A process for the production of weather-resistant pearlescent pigment according to claim 1 , wherein,
the process comprises the following steps:
a) optionally classifying coated or uncoated platelet-shaped substrates, obtaining substrates which preferably have the values D 10 , D 50 , D 90 from a cumulative frequency distribution of a volume-averaged size distribution function with a span ΔD in a range of from 0.7-1.4,
b) suspending coated or uncoated platelet-shaped substrates, optionally from step a), in aqueous solution, and coating the coated or uncoated platelet-shaped substrates with one or more highly refractive metal oxide(s), obtaining pearlescent pigments which are optionally calcined,
c) coating the pearlescent pigments coated in step b) in aqueous solution with tin oxide, tin hydroxide and/or hydrated tin oxide by hydrolysis of a tin salt or of a hydrolyzable tin metalorganic compound in a pH range of from 1.5 to 3.0,
d) coating the pearlescent pigments coated in step c) in aqueous solution with cerium oxide, cerium hydroxide and/or hydrated cerium oxide by hydrolysis of a cerium salt or of a hydrolyzable cerium metalorganic compound,
e) coating the pearlescent pigments coated in step d) in aqueous solution with one or more oligomeric silane(s),
f) separating off the pearlescent pigments coated in step e), optionally washing with demineralized water, and
g) optionally drying the pearlescent pigments of step f).

18. The process of using the weather-resistant pearlescent pigment of claim 1 for the pigmentation of coatings, printing inks, plastics and cosmetics.

19. The weather-resistant pearlescent pigment according to claim 1 , wherein the organic-chemical coating consists of one or more oligomeric silane(s), wherein the oligomeric silane(s) have one or more amino groups and the oligomeric silane(s) are chemically bonded with the cerium-containing layer.

20. The weather-resistant pearlescent pigment according to claim 11 , wherein, the chromophoric, highly refractive coating consists of TiO 2 in the rutile structure.

21. The process according to claim 17 , wherein the pearlescent pigments of step f) are optionally dried at a temperature from 80° C. to 160° C.

22. A weather-resistant pearlescent pigment, comprising:
a coated or uncoated platelet-shaped substrate which is selected from the group consisting of synthetic mica platelets, glass platelets, SiO 2 platelets, Al 2 O 3 platelets, synthetic boehmite platelets, BiOCl platelets and mixtures thereof,
a chromophoric coating comprising at least one highly refractive metal oxide, and
a top layer,
wherein the top layer comprises the following layer sequence:
a) a first layer comprising tin oxide and/or tin hydroxide and/or hydrated tin oxide,
b) a second cerium-containing layer consisting of cerium oxide and/or cerium hydroxide and/or hydrated cerium oxide,
c) an organic-chemical coating applied to the cerium-containing layer which comprises one or more oligomeric silane(s), wherein the oligomeric silane(s) have one or more amino groups and the oligomeri

Assignees

• Eckart Gmbh

Inventors

• Grüner Michael
• Kaupp Günter
• Schneider Thomas

Classifications

• C09C1/0015 Primary

  Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings · CPC title

• C09C2200/102

  the core consisting of glass or silicate material like mica or clays, e.g. kaolin · CPC title

• C09C2200/1087

  the core consisting of bismuth oxychloride, magnesium fluoride, nitrides, carbides, borides, lead carbonate, barium or calcium sulfate, zinc sulphide, molybdenum disulphide or graphite · CPC title

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title

• C09D5/36

  Pearl essence, e.g. coatings containing platelet-like pigments for pearl lustre · CPC title