Back-plate composition, back plate, brake pad, and caliper device

Patent metadata

Field	Value
Publication number	US-9618065-B2
Application number	US-201314437607-A
Country	US
Kind code	B2
Filing date	Oct 24, 2013
Priority date	Oct 26, 2012
Publication date	Apr 11, 2017
Grant date	Apr 11, 2017

Abstract

A back-plate composition of the present invention is a composition for forming a back plate of a brake pad, the brake pad having a friction material and the back plate bonded to the friction material. The back-plate composition includes a resin, a plurality of first fibers and a plurality of second fibers having an average length shorter than an average length of the first fibers. In the case where the average length of the first fibers is “L1” [μm] and the average length of the second fibers is “L2” [μm], “L2”/“L1” is in the range of 0.001 to 0.5. This makes it possible to provide a back-plate composition having excellent moldability, as well as a back plate formed of the back-plate composition, a brake pad including the back-plate and a caliper device provided with the brake pad.

First claim

What is claimed is:

1. A back-plate composition for forming a back plate of a brake pad, the brake pad having a friction material and the back plate bonded to the friction material, an entirety of the back-plate composition being a mixture comprising:
a resin;
a plurality of first fibers including organic fibers or inorganic fibers other than metal fibers; and
a plurality of second fibers having an average length shorter than an average length of the first fibers and including organic fibers or inorganic fibers other than metal fibers,
wherein “L2”/“L1” is in the range of 0.001 to 0.5, where the average length of the first fibers is “L1” [μm], and the average length of the second fibers is “L2” [μm], and
wherein “X2”/“X1” is in the range of 0.006 to 0.294, where an amount of the first fibers contained in the back-plate composition is “X1” [mass %], and an amount of the second fibers contained therein is “X2” [mass %].

2. The back-plate composition as claimed in claim 1 , wherein the average length “L1” of the first fibers is in the range of 5 to 50 mm.

3. The back-plate composition as claimed in claim 1 , wherein the average length “L2” of the second fibers is in the range of 50 μm to 10 mm.

4. The back-plate composition as claimed in claim 1 , wherein a total amount of the first fibers and the second fibers contained in the back-plate composition is in the range of 20 to 80 mass %.

5. The back-plate composition as claimed in claim 1 , wherein the first fibers and the second fibers are formed of the same material or the same type of material.

6. The back-plate composition as claimed in claim 1 , wherein the first fibers and/or the second fibers are glass fibers.

7. The back-plate composition as claimed in claim 1 , wherein the first fibers and/or the second fibers are subjected to a surface treatment.

8. The back-plate composition as claimed in claim 1 , wherein the resin comprises at least one type selected from the group consisting of phenol resin, epoxy resin, bismaleimide resin, benzoxazine resin, and unsaturated polyester resin.

9. The back plate formed of the back-plate composition defined by claim 1 .

10. The back plate as claimed in claim 9 , wherein at least the first fibers orient along a surface direction of the back plate.

11. The back plate as claimed in claim 10 , wherein at least the first fibers orient along an advancing direction of a disc that is braked by the brake pad.

12. The brake pad comprising:
the friction material; and
the back plate defined by claim 9 , the back plate bonded to the friction material.

13. A caliper device comprising:
the brake pad defined by claim 12 ;
a piston that presses the brake pad toward a disc; and
a caliper in which the piston is put so as to be movable.

14. The back-plate composition as claimed in claim 1 , wherein each of the first and second fibers is coated with the resin by a dry method using fluidized-bed technology.

15. The back-plate composition as claimed in claim 1 , wherein the average length “L1” of the first fibers is in the range of 12 to 50 mm.

Assignees

• Sumitomo Bakelite Co

Inventors

• Inokuchi Hideaki
• Yazawa Hidemi

Classifications

• F16D2250/0076

  Welding, brazing · CPC title

• F16D69/0408

  specially adapted for plane linings · CPC title

• F16D65/092 Primary

  for axially-engaging brakes, e.g. disc brakes · CPC title

• F16D2069/0458

  metallurgic, e.g. welding, brazing, sintering · CPC title

• F16D55/225

  the braking members being brake pads · CPC title