Thermally conductive thermoplastic compositions featuring balanced processability

Patent metadata

Field	Value
Publication number	US-9617457-B2
Application number	US-201515125626-A
Country	US
Kind code	B2
Filing date	Mar 11, 2015
Priority date	Mar 14, 2014
Publication date	Apr 11, 2017
Grant date	Apr 11, 2017

Abstract

The invention relates to thermally conductive thermoplastic compositions with balanced processing capacity, i.e. with a balanced proportion of melt volume flow rate to heat distortion resistance, comprising a thermoplastic, an expanded graphite, at least one phosphorus compound, and also ethylene/alkyl (meth)acrylate copolymer.

First claim

The invention claimed is:

1. A composition comprising
A) 20.0 to 80.49 wt % of polycarbonate,
B) 15.0 to 60.0 wt % of expanded graphite, the D(0.5) of the graphite, determined by sieve analysis according to DIN 51938, being <1.2 mm,
C) 4.5 to 10 wt % of at least one phosphorus compound of the general formula (V)

in which
R 1 , R 2 , R 3 and R 4 independently of one another are C 1 - to C 8 -alkyl, optionally halogenated and in each case branched or unbranched, and/or C 5 - to C 6 -cycloalkyl, C 6 - to C 20 -aryl or C 7 - to C 12 -aralkyl, optionally substituted by a branched or unbranched alkyl and/or halogen,
n independently at each occurrence is 0 or 1,
q is an integer from 0 to 30,
X is a monocyclic or polycyclic aromatic radical having 6 to 30 C atoms or is a linear or branched aliphatic radical having 2 to 30 C atoms, optionally substituted or unsubstituted, bridged or unbridged;

D) 0.01 to 5.0 wt % of at least one ethylene/alkyl (meth)acrylate copolymer,
E) optionally at least one further polymer additive, selected from the group consisting of heat stabilizers, flame retardants other than component C, antistatic agents, colorants, pigments, mould release agents, UV absorbers, IR absorbers and fillers, selected from the group of chalk, quartz powder, titanium dioxide, silicates, aluminosilicates, aluminium oxide, silica, magnesium hydroxide and aluminium hydroxide,
with components A) to E) adding up to 100 wt %.

2. The composition according to claim 1 , wherein expanded graphite comprises at least one expanded graphite having a particle size distribution defined by the D(0.5) of ≦1 mm, determined by sieve analysis according to DIN 51938, and also a bulk density of ≧0.1 g/cm 3 , determined according to DIN 51705.

3. The composition according to claim 1 , wherein the composition is free from fluorine-containing anti-dripping agent.

4. The composition according to claim 1 , wherein in the phosphorus compound of the general formula V,
X is one of the following structures:

5. The composition according to claim 1 , wherein phosphorus compound of the general formula V comprises the compound of the formula Va

6. The composition according to claim 1 , wherein the ethylene/alkyl (meth)acrylate copolymer has a melt flow index of at least 2.5 g/10 min, determined according to ASTM D1238 (at 190° C. and 2.16 kg).

7. The composition according to claim 1 , wherein the fraction of component A is 20.0 to 72.0 wt %.

8. The composition according to claim 1 , wherein the fraction of component C is 6.0 to 9.0 wt %.

9. The composition according to claim 1 , wherein the fraction of component C is 5.0 to 7.0 wt %.

10. The composition according to claim 1 , wherein the amount of ethylene/alkyl (meth)acrylate copolymer is 3.0 to 4.0 wt %.

11. The composition according to claim 1 , wherein the composition comprises
A) 52.0 to 72.0 wt % of polycarbonate,
B) 20.0 to 35.0 wt % of expanded graphite, the D(0.5) of the graphite, determined by sieve analysis according to DIN 51938, being <1.2 mm,
C) 5.0 to 10.0 wt % of at least one phosphorus compound of the formula

where q is between 1.0 and 1.2 and is preferably 1.1,

D) 3.0 to 4.0 wt % of at least one ethylene/alkyl (meth)acrylate copolymer,
E) optionally at least one further polymer additive, selected from the group of consisting of heat stabilizers, flame retardants other than component (C), antistatic agents, colorants, pigments, mould release agents, UV absorbers, IR absorbers and fillers, selected from the group consisting of chalk, quartz powder, titanium dioxide, silicates, aluminosilicates, aluminium oxide, silica, magnesium hydroxide and aluminium hydroxide,
with components A) to E) adding up to 100 wt % and where the composition is free from fluorine-containing anti-dripping agent.

12. The composition according to claim 11 , wherein the fraction of component C in the composition is 5.0 to 7.0 wt %.

13. A plastics moulding comprising the composition according to claim 1 .

Assignees

• Covestro Deutschland Ag

Inventors

• Sämisch Birte
• Kuhlmann Timo

Classifications

• C08K7/24

  inorganic · CPC title

• C08L69/00 Primary

  Compositions of polycarbonates; Compositions of derivatives of polycarbonates · CPC title

• C09K5/14 Primary

  Solid materials, e.g. powdery or granular · CPC title

• C08K5/523

  with hydroxyaryl compounds · CPC title

• C08L23/0869

  with unsaturated acids, e.g. [meth]acrylic acid; with unsaturated esters, e.g. [meth]acrylic acid esters · CPC title