Light-weight hybrid glass laminates

Patent metadata

Field	Value
Publication number	US-9616641-B2
Application number	US-201313937707-A
Country	US
Kind code	B2
Filing date	Jul 9, 2013
Priority date	Jun 24, 2011
Publication date	Apr 11, 2017
Grant date	Apr 11, 2017

Abstract

A glass laminate comprises an external glass sheet, an internal glass sheet, and a polymer interlayer formed between the external glass sheet and the internal glass sheet. The external glass sheet can be a thin chemically-strengthened glass sheet or can be a non-chemically strengthened glass sheet, the polymer interlayer can have a thickness of less than 1.6 mm, and the internal glass sheet can be a non-chemically-strengthened glass sheet or a thin chemically strengthened glass sheet.

First claim

What is claimed is:

1. A glass laminate structure comprising:
an interior surface;
a non-chemically strengthened external glass sheet;
a chemically strengthened internal glass sheet; and
a polymer interlayer in direct physical contact with the external and internal glass sheets,
wherein the internal glass sheet has a thickness of 0.7 mm or less,
wherein the external glass sheet has a thickness ranging from about 1.5 mm to about 3.0 mm,

wherein the polymer interlayer has a modulus of elasticity ranging from about 1 MPa to about 75 MPa, and
wherein the internal glass sheet provides the interior surface, and wherein the interior surface constitutes an open surface of the laminate structure.

2. The glass laminate structure of claim 1 , wherein the internal glass sheet includes at least about 6 wt. % aluminum oxide.

3. The glass laminate structure of claim 1 , wherein the internal glass sheet has a thickness of between about 0.5 mm to 0.7 mm.

4. The glass laminate structure of claim 1 , wherein the polymer interlayer comprises a single polymer sheet, a multilayer polymer sheet, or a composite polymer sheet.

5. The glass laminate structure of claim 1 , wherein the polymer interlayer comprises a material selected from the group consisting of poly vinyl butyral (PVB), acoustic PVB, ethylene vinyl acetate (EVA), thermoplastic polyurethane (TPU), ionomer, a thermoplastic material, and combinations thereof.

6. The glass laminate structure of claim 1 , wherein the polymer interlayer has a thickness of between about 0.4 to about 1.2 mm.

7. The glass laminate structure of claim 1 , wherein the external glass sheet comprises a material selected from the group consisting of soda-lime glass and annealed glass.

8. The glass laminate structure of claim 1 , wherein the external glass sheet has a thickness of about 2.1 mm.

9. The glass laminate structure of claim 1 , wherein the glass laminate has an area greater than 1 m 2 .

10. The glass laminate structure of claim 1 , wherein the glass laminate is an automotive windshield, sunroof or cover plate.

11. The glass laminate structure of claim 1 , wherein the internal glass sheet has a surface compressive stress between about 250 MPa and about 900 MPa.

12. The glass laminate structure of claim 1 , wherein the internal glass sheet has a surface compressive stress of between about 250 MPa and about 350 MPa and a DOL of compressive stress greater than about 20 um.

13. The glass laminate structure of claim 1 , wherein a surface of the external glass sheet adjacent the interlayer is acid etched.

14. The glass laminate structure of claim 1 , wherein a surface of the internal glass sheet opposite the interlayer is acid etched.

15. A glass laminate structure comprising:
an interior surface;
a non-chemically strengthened external glass sheet;
a chemically strengthened internal glass sheet; and
a polymer interlayer in direct physical contact with the external and internal glass sheets,
wherein the internal glass sheet has a surface compressive stress between about 250 MPa and about 900 MPa and a thickness of 0.7 mm or less,
wherein the polymer interlayer has a modulus of elasticity ranging from about 1 MPa to about 75 MPa, and
wherein the interior surface constitutes an open surface of the laminate structure, the interior surface provided by the internal glass sheet.

16. The glass laminate structure of claim 15 , wherein the internal glass sheet has a surface compressive stress of between about 250 MPa and about 350 MPa and a DOL of compressive stress greater than about 20 μm.

17. The glass laminate structure of claim 15 , wherein the internal glass sheet has a thickness ranging from about 0.5 mm to 0.7 mm, and wherein the external glass sheet has a thickness ranging from about 1.5 mm to about 3.0 mm.

18. The glass laminate structure of claim 15 , wherein the polymer interlayer comprises a material selected from the group consisting of poly vinyl butyral (PVB), acoustic PVB, ethylene vinyl acetate (EVA), thermoplastic polyurethane (TPU), ionomer, a thermoplastic material, and combinations thereof.

19. The glass laminate structure of claim 15 , wherein the polymer interlayer has a thickness of between about 0.4 to about 1.2 mm.

20. The glass laminate structure of claim 1 , wherein the internal glass sheet includes one or more alkaline earth metal oxides chosen from MgO, CaO, or SrO, and wherein 5 mol. %≦MgO+CaO+SrO≦8 mol. %.

21. The glass laminate structure of claim 1 , wherein the internal glass sheet comprises 60-70 mol. % SiO 2 ; 6-14 mol. % Al 2 O 3 ; 0-15 mol. % B 2 O 3 ; 0-15 mol. % Li 2 O; 0-20 mol. % Na 2 O; 0-10 mol. % K 2 O; 0-8 mol. % MgO; 0-10 mol. % CaO; 0-5 mol % ZrO 2 ; 0-1 mol. % SnO 2 ; 0-1 mol. % CeO 2 ; less than 50 ppm As 2 O 3 , and less than 50 ppm Sb 2 O 3 ; wherein 12 mol. %≦(Li 2 O+Na 2 O+K 2 O)≦20 mol. % and 0 mol. %≦(MgO+CaO)≦10 mol. %.

22. The glass laminate structure of claim 1 , wherein the internal glass sheet comprises 64-68 mol. % SiO 2 ; 8-12 mol. % Al 2 O 3 ; 0-3 mol. % B 2 O 3 ; 0-15 mol. % Li 2 O; 12-16 mol. % Na 2 O; 2-5 mol. % K 2 O; 4-6 mol. % MgO; and 0-5 mol. % CaO; wherein 66 mol. %≦(SiO 2 +B 2 O 3 +CaO)≦69 mol. %, (Na 2 O+K 2 O+B 2 O 3 +MgO+CaO+SrO)>10 mol. %, 5 mol. %≦MgO+CaO+SrO≦8 mol. %, (Na 2 O+B 2 O 3 )—Al 2 O 3 ≦2 mol. %, 2 mol. %≦(Na 2 O—Al 2 O 3 )≦6 mol. %, and 4 mol. %≦(Na 2 O+K 2 O)—Al 2 O 3 ≦10 mol. %.

Assignees

• Corning Inc

Inventors

• Cleary Thomas Michael
• Huten Timothy Scott
• Moore Michael John

Classifications

• B32B17/10761

  containing vinyl acetal · CPC title

• B32B17/10137

  Chemical strengthening · CPC title

• Y10T428/24967

  Absolute thicknesses specified · CPC title

• B32B2605/006

  Transparent parts other than made from inorganic glass, e.g. polycarbonate glazings · CPC title

• B32B17/10119

  having a composition deviating from the basic composition of soda-lime glass, e.g. borosilicate · CPC title