Laminated ceramic capacitor

Patent metadata

Field	Value
Publication number	US-9613756-B2
Application number	US-201514985662-A
Country	US
Kind code	B2
Filing date	Dec 31, 2015
Priority date	Jan 21, 2011
Publication date	Apr 4, 2017
Grant date	Apr 4, 2017

Abstract

As a dielectric ceramic constituting dielectric layers of a laminated ceramic capacitor, a dielectric ceramic is used which contains, as its main constituent, a perovskite-type compound containing Ca and Zr and optionally containing Sr, Ba, and Ti, and further contains Si, Mn, and Al, and when the total content of Zr and Ti is regarded as 100 parts by mol, the total content (100×m) of Ca, Sr, and Ba meets 1.002≦m≦1.100 in terms of parts by mol, the Si content n meets 0.5≦n≦10 in terms of parts by mol, the Mn content u meets 0.5≦u≦10 in terms of parts by mol, and the Al content w meets 0.02≦w≦4 in terms of parts by mol, m and n satisfying −0.4≦100(m−1)−n≦3.9.

First claim

The invention claimed is:

1. A laminated ceramic capacitor comprising:
a laminated body including a plurality of stacked dielectric layers, and a plurality of internal electrodes along interfaces between the stacked dielectric layers, wherein the internal electrodes contain Ni or a Ni alloy as a main constituent; and
a plurality of external electrodes on an outer surface of the laminated body, each of the plurality of external electrodes electrically connected to different sets of electrodes of the plurality of internal electrodes,
wherein the laminated body has a composition containing, as a main constituent thereof, a perovskite-type compound containing Ca and Zr, and further containing Si, Mn, and Al, and
when a total content of Zr is 100 parts by mol,
a total content (100×m) of Ca meets 1.002≦m≦1.100 in terms of parts by mol,
the Si content n meets 0.5≦n≦10 in terms of parts by mol,
the Mn content u meets 0.5≦u≦10 in terms of parts by mol, and
the Al content w meets 0.02≦w≦4 in terms of parts by mol,
m and n satisfying −0.4≦100(m−1)−n≦3.9.

2. The laminated ceramic capacitor according to claim 1 , wherein the perovskite-type compound further contains at least one selected from the group consisting of Sr, Ba, and Ti, and
when the total content of Zr and Ti is regarded as 100 parts by mol,
the total content (100×m) of Ca, Sr, and Ba meets 1.002≦m≦1.100 in terms of parts by mol,
a molar ratio s of Ti/(Zr+Ti) is 0≦s≦0.50,
a molar ratio y of Sr/(Ca+Sr+Ba) is 0≦y≦0.29, and
a molar ratio z of Ba/(Ca+Sr+Ba) is 0≦z≦0.29, y and z satisfying 0≦y+z≦0.29.

3. The laminated ceramic capacitor according to claim 2 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

4. The laminated ceramic capacitor according to claim 1 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

5. A laminated ceramic capacitor comprising:
a laminated body including a plurality of stacked dielectric layers, and a plurality of internal electrodes along interfaces between the stacked dielectric layers, wherein the internal electrodes contain Ni or a Ni alloy as a main constituent; and
a plurality of external electrodes on an outer surface of the laminated body, each of the plurality of external electrodes electrically connected to different sets of electrodes of the plurality of internal electrodes,
wherein the laminated body has a composition containing, as a main constituent thereof, a perovskite-type compound containing Ca and Zr, and further containing Si, Mn, and Al, and
when the laminated body is dissolved in a solvent,
when the total content of Zr is regarded as 100 parts by mol,
a total content (100×m) of Ca meets 1.002≦m≦1.100 in terms of parts by mol,
the Si content n meets 0.5≦n≦10 in terms of parts by mol,
the Mn content u meets 0.5≦u≦10 in terms of parts by mol, and the Al content w meets 0.02≦w≦4 in terms of parts by mol,
m and n satisfying −0.4≦100(m−1)−n≦3.9.

6. The laminated ceramic capacitor according to claim 5 , wherein the perovskite-type compound further contains at least one selected from the group consisting of Sr, Ba, and Ti, and
when the total content of Zr and Ti is regarded as 100 parts by mol,
the total content (100×m) of Ca, Sr, and Ba meets 1.002≦m≦1.100 in terms of parts by mol,
a molar ratio s of Ti/(Zr+Ti) is 0≦s≦0.50,
a molar ratio y of Sr/(Ca+Sr+Ba) is 0≦y≦0.29, and
a molar ratio z of Ba/(Ca+Sr+Ba) is 0≦z≦0.29, y and z satisfying 0≦y+z≦0.29.

7. The laminated ceramic capacitor according to claim 6 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

8. The laminated ceramic capacitor according to claim 5 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

9. A laminated ceramic capacitor comprising:
a laminated body including a plurality of stacked dielectric layers stacked, and a plurality of internal electrodes along interfaces between the stacked dielectric layers, wherein the internal electrodes contain Ni or a Ni alloy as a main constituent,
wherein the dielectric layers have a composition containing, as a main constituent thereof, a perovskite-type compound containing Ca and Zr, and further containing Si, Mn, and Al, and
when the total content of Zr is regarded as 100 parts by mol,
the total content (100×m) of Ca meets 1.002≦m≦1.100 in terms of parts by mol,
the Si content n meets 0.5≦n≦10 in terms of parts by mol,
the Mn content u meets 0.5≦u≦10 in terms of parts by mol, and
the Al content w meets 0.02≦w≦4 in terms of parts by mol,
m and n satisfying −0.4≦100(m−1)−n≦3.9.

10. The laminated ceramic capacitor according to claim 9 , wherein the perovskite-type compound further contains at least one selected from the group consisting of Sr, Ba, and Ti, and
when the total content of Zr and Ti is regarded as 100 parts by mol,
the total content (100×m) of Ca, Sr, and Ba meets 1.002≦m≦1.100 in terms of parts by mol,
a molar ratio s of Ti/(Zr+Ti) is 0≦s≦0.50,
a molar ratio y of Sr/(Ca+Sr+Ba) is 0≦y≦0.29, and
a molar ratio z of Ba/(Ca+Sr+Ba) is 0≦z≦0.29, y and z satisfying 0≦y+z≦0.29.

11. The laminated ceramic capacitor according to claim 10 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

12. The laminated ceramic capacitor according to claim 9 , wherein a relationship of 0≦100(m−1)−n≦2.0 is satisfied.

Assignees

• Murata Manufacturing Co

Inventors

• Nishimura Hitoshi
• Naito Masahiro

Classifications

• H01G4/30 Primary

  Stacked capacitors (H01G4/33 takes precedence) · CPC title

• C04B2235/6562

  Heating rate · CPC title

• C04B35/49

  containing also titanium oxides or titanates · CPC title

• C01G23/003

  Titanates (C01G23/001 takes precedence) · CPC title

• C04B2235/3262

  Manganese oxides, manganates, rhenium oxides or oxide-forming salts thereof, e.g. MnO · CPC title