Oxidation resistant coatings, processes for coating articles, and their coated articles

Patent metadata

Field	Value
Publication number	US-9611181-B2
Application number	US-201113088599-A
Country	US
Kind code	B2
Filing date	Apr 18, 2011
Priority date	Nov 21, 2006
Publication date	Apr 4, 2017
Grant date	Apr 4, 2017

Abstract

A process for applying an oxidation resistant coating to an article includes the steps of mixing at least about 10% by volume to up to about 99% by volume of a slurry at least one silica based material having a viscosity of about 1×10 2 poise to about 1×10 7 poise at a temperature of about 1,292° F. (700° C.) to about 3,272° F. (1,800° C.) at least about 1% by volume to up to about 90% by volume of the slurry at least one oxygen scavenger, and a liquid medium to form the slurry; coating an article with the slurry to form a slurry coated article; and heat treating under an inert atmosphere the slurry coated article to form an article having at least one oxidation resistant coating layer containing the at least one oxygen scavenger.

First claim

What is claimed is:

1. A process for applying an oxidation resistant coating to an article, comprising:
forming a slurry consisting of at least about 10% by volume to up to about 99% by volume at least one silica based material having a viscosity of about 1×10 2 poise to about 1×10 7 poise at a temperature of about 1,292° F. (700° C.) to about 3,272° F. (1,800° C.), at least about 1% by volume to up to about 90% by volume of at least one oxygen scavenger selected from the group consisting of at least one silicide of molybdenum, chromium, titanium, hafnium, zirconium, yttrium, and mixtures thereof or a boride of at least one of the following: molybdenum, tantalum, chromium, titanium, hafnium, zirconium, yttrium and mixtures thereof, mullite to control viscosity of said slurry during a subsequent heat treatment step, and a liquid medium;
coating an article with said slurry to form a slurry coated article; and
heat treating under an inert atmosphere said slurry coated article to form an article having at least one oxidation resistant coating layer containing said at least one oxygen scavenger.

2. The process of claim 1 , wherein said slurry forming step comprises using a mechanical mixing process comprising at least one of the following: ball mixing, grinding, high energy milling, attrition milling, centrifugal mixing, and combinations thereof.

3. The process of claim 1 , wherein coating comprises at least one of the following processes: thermal spraying, chemical vapor deposition, physical vapor deposition, electrophoretic deposition, electrostatic deposition, preceramic polymer pyrolysis, sol-gel, slurry coating, dipping, air-brushing, sputtering, slurry painting, and combinations thereof.

4. The process of claim 1 , wherein coating comprises a low pressure plasma spraying process or a high velocity oxygen fuel spraying process.

5. The process of claim 1 , wherein heat treating comprises heating said slurry coated substrate at about 1,000° F. (538° C.) to about 2,552° F. (1,400° C.) for a period of time sufficient to form said oxidation resistant coating.

6. The process of claim 1 , wherein said silica based material comprises a particle size range of about 150 mesh to about 325 mesh.

7. The process of claim 1 , wherein said at least one oxygen scavenger comprises a particle diameter size range of about 0.5 microns to about 50 microns.

8. The process of claim 1 , wherein said liquid medium comprises at least one of the following: water, alcohol, terpineol, colloidal silica, inorganic containing solvent, and organic containing solvent.

9. The process of claim 1 , further comprising applying upon said oxidation resistant coating layer a top coat layer comprising at least one of the following: refractory oxide material, refractory carbide material, refractory boride material, refractory silicide material, and mixtures thereof.

10. The process of claim 9 , wherein said refractory oxide material is selected from the group consisting of Ta x O y (where x=1 to 3 and y=1 to 5), Nb x O y (where x=1 to 3 and y=1 to 5), MgO, CaO, SrO, BaO, SiO 2 , HfO 2 , TiO 2 , ZrO 2 , Al 2 O 3 , Y 2 O 3 , La 2 O 3 , rare earth oxides, and mixtures thereof.

11. The process of claim 9 , wherein applying comprises at least one of the following processes: thermal spraying, chemical vapor deposition, physical vapor deposition, electrophoretic deposition, electrostatic deposition, preceramic polymer pyrolysis, sol-gel, slurry coating, dipping, air-brushing, sputtering, slurry painting, high velocity oxygen fuel spraying, and low pressure plasma spraying.

12. The process of claim 1 , wherein forming comprises a manual mixing process.

13. The process of claim 1 , wherein said coating step comprises a painting process.

14. The process of claim 13 , further comprising drying said slurry coated article at about 662° F. (350° C.) for about 30 minutes to about 60 minutes prior to heat treating said slurry coated article.

15. A process for applying an oxidation resistant coating to an article, comprising:
forming a slurry consisting of at least about 10% by volume to up to about 99% of volume of at least one silica based material having a viscosity of about 1×10 2 poise to about 1×10 7 poise at a temperature of about 1,292° F. (700° C.) to about 3,272° F. (1,800° C.), at least about 1% by volume to up to about 90% by volume of at least one oxygen scavenger, wherein said at least one oxygen scavenger is a silicide of any one of the following: molybdenum, chromium, titanium, hafnium, zirconium, yttrium, and mixtures thereof; and a boride of any one of the following: molybdenum, tantalum, chromium, titanium, hafnium, zirconium, yttrium, and mixtures thereof, mullite to control viscosity of said slurry during a subsequent heat treatment step, and a liquid medium;
coating an article with said slurry to form a slurry coated article; and
heat treating under an inert atmosphere said slurry coated article to form an article having at least one oxidation resistant coating layer containing said at least one oxygen scavenger.

16. A process for applying an oxidation resistant coating to an article, comprising:
forming a slurry consisting of at least about 10% by volume to up to about 99% by volume of at least one silica based material having a viscosity of about 1×10 2 poise to about 1×10 7 poise at a temperature of about 1,292° F. (700° C.) to about 3,272° F. (1,800° C.), at least about 1% by volume to up to about 90% by volume of molybdenum silicide,
mullite in an amount sufficient to rheologically control a viscosity of said slurry during a subsequent heat treatment, and water;
said forming step comprising ball mixing said slurry;
thermal spraying an article with said slurry to form a slurry coated article;
heat treating under an inert atmosphere said slurry coated article to form an article having at least one oxidation resistant coating layer; and
applying a top coat formed from Ta x O y where x=1 to 3 and y=1 to 5 upon said at least one oxidation resistant coating layer using a thermal spraying technique.

Assignees

• Tang Xia
• Kashyap Tania Bhatia
• Jarmon David C
• Schmidt Wayde R
• Eaton Jr Harry E
• Smeggil John G
• United Technologies Corp

Inventors

• Tang Xia
• Kashyap Tania Bhatia
• Jarmon David C
• Schmidt Wayde R
• Eaton Jr Harry E
• Smeggil John G

Classifications

• C04B41/89 Primary

  for obtaining at least two superposed coatings having different compositions · CPC title

• C23C26/00

  Coating not provided for in groups C23C2/00 - C23C24/00 · CPC title

• Y10T428/12611

  Oxide-containing component · CPC title

• C04B41/009

  characterised by the material treated · CPC title

• C23C24/10

  with intermediate formation of a liquid phase in the layer · CPC title