Battery manufacturing method

Patent metadata

Field	Value
Publication number	US-9608258-B2
Application number	US-201013877688-A
Country	US
Kind code	B2
Filing date	Oct 5, 2010
Priority date	Oct 5, 2010
Publication date	Mar 28, 2017
Grant date	Mar 28, 2017

Abstract

The present invention provides a battery manufacturing method including: a step of preparing a thickener aqueous solution by dissolving a thickener in an aqueous solvent (S 10 ); a kneading step of introducing an active material into the prepared thickener aqueous solution and kneading a result (S 20 ); a diluting step of adding an aqueous solvent to a kneaded material resulting from the kneading step such that the kneaded material is diluted, whereby an active material layer forming paste is obtained from the kneaded material (S 30 ); and a step of obtaining an electrode in which an active material layer is formed on a current collector by coating the current collector with the active material layer forming paste and then drying the paste (S 40 ).

First claim

The invention claimed is:

1. A method for manufacturing a battery that includes an electrode having an active material layer which is formed by coating a current collector with an active material layer forming paste containing an active material, a thickener, and an aqueous solvent, and then drying the paste, the method comprising:
preparing a thickener aqueous solution by dissolving the thickener in the aqueous solvent;
a kneading step of introducing the active material into the prepared thickener aqueous solution and kneading a result;
a diluting step of adding an aqueous solvent that is free from the thickener to a kneaded material resulting from the kneading step such that the kneaded material is diluted, whereby the active material layer forming paste is obtained from the diluted kneaded material; and
obtaining the electrode in which the active material layer is formed on the current collector by coating the current collector with the active material layer forming paste and then drying the paste,
wherein the aqueous solvent is introduced in two stages that are the preparing step and the diluting step, and the aqueous solvent introduced in the preparing step occupies between 67% by mass and 76% by mass of a total amount of the aqueous solvent in the active material layer forming paste.

2. The battery manufacturing method according to claim 1 , wherein the thickener aqueous solution is passed through a filter before performing the kneading step.

3. The battery manufacturing method according to claim 1 , wherein a binder is introduced into the active material layer forming paste following the diluting step.

4. The battery manufacturing method according to claim 1 , wherein a viscosity of the active material layer forming paste is between 1000 mPa·s and 10000 mPa·s.

5. The battery manufacturing method according to claim 1 , wherein a solid content of the active material layer forming paste is between 50% by mass and 70% by mass.

6. The battery manufacturing method according to claim 1 , wherein a viscosity of the thickener aqueous solution is between 1000 mPa·s and 10000 mPa·s.

7. The battery manufacturing method according to claim 1 , wherein a cellulose-based polymer is used as the thickener.

8. The battery manufacturing method according to claim 1 , wherein
the electrode is a negative electrode of a lithium secondary battery, and
a carbon-based material is used as the active material.

9. The battery manufacturing method according to claim 8 , wherein foil-form copper or copper alloy is used as the current collector.

Assignees

• Kobayashi Kiwamu
• Toyota Motor Co Ltd

Inventors

• Kobayashi Kiwamu

Classifications

• H01M4/62

  Selection of inactive substances as ingredients for active masses, e.g. binders, fillers · CPC title

• Y02E60/122

  Cross-Sectional Technologies · mapped topic

• H01M4/1393 Primary

  of electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx · CPC title

• H01M4/0411

  by extrusion · CPC title

• Y02P70/54

  Cross-Sectional Technologies · mapped topic