Three-way catalyst systems including Nb—Zr—Al-mixed oxide supports, Ba—Pd, and Rh—Fe material compositions

Patent metadata

Field	Value
Publication number	US-9604175-B2
Application number	US-201514732499-A
Country	US
Kind code	B2
Filing date	Jun 5, 2015
Priority date	Jun 6, 2014
Publication date	Mar 28, 2017
Grant date	Mar 28, 2017

Abstract

The present disclosure describes zoned three way catalyst (TWC) systems including Rhodium-iron overcoat layers and Nb—Zr—Al Oxide overcoat layers. Disclosed herein are TWC sample systems that are configured to include a substrate and one or more of a washcoat layer, an impregnation layer, and/or an overcoat layer. In catalyst systems disclosed herein, closed-coupled catalysts include a first catalyst zone with an overcoat layer formed using a slurry that includes an oxide mixture and an Oxygen Storage Material (OSM). In catalyst systems disclosed herein, oxide mixtures include niobium oxide (Nb 2 O 5 ), zirconia, and alumina. Further, catalyst systems disclosed herein include a second catalyst zone with an overcoat layer formed to include a rhodium-iron catalyst. Yet further, catalyst systems disclosed herein include impregnation layers that include one or more of Palladium, Barium, Cerium, Neodymium, and Rhodium.

First claim

What is claimed is:

1. A close-coupled converter system, comprising:
a first catalyst zone; and
a second catalyst zone;
wherein the first catalyst zone is configured to receive exhaust gases, process the received exhaust gases into first treated gases, and expel the first treated gases into the second catalyst zone;
wherein the second catalyst zone is configured to receive the first treated gases from the first catalyst zone, process the received first treated gases into second treated gases, and expel the second treated gases;
wherein the first catalyst zone comprises:
a first catalyst zone substrate;
a first catalyst zone washcoat deposited on the first catalyst zone substrate;
at least one first catalyst zone impregnation layer; and
a first catalyst zone overcoat;

wherein the first catalyst zone washcoat comprises a first catalyst zone first oxygen storage material including Cerium, Zirconium-Hafnium, Neodymium, and Yttrium, and a first catalyst zone support oxide;
wherein the at least one first catalyst zone impregnation layer comprises Pd, Ba, Ce, and Nd;
wherein the first catalyst zone overcoat comprises a first catalyst zone second oxygen storage material comprising Cerium, Zirconium-Hafnium, Neodymium, and Yttrium, and a first catalyst zone oxide mixture comprising Niobium, Zirconium-Hafnium, Alumina and Rhodium;
wherein the second catalyst zone comprises:
a second catalyst zone substrate;
a second catalyst zone washcoat deposited on the second catalyst zone substrate;
at least one second catalyst zone impregnation layer; and
a second catalyst zone overcoat;

wherein at the second catalyst zone overcoat comprises rhodium and iron.

2. The close-coupled converter system of claim 1 , wherein the second catalyst zone overcoat comprises a second catalyst zone oxygen storage material, Fe, and Rh.

3. The close-coupled converter system of claim 1 , wherein the at least one second catalyst zone impregnation layer comprises Pd, Ba, Ce, and Nd.

4. The close-coupled converter system of claim 1 , wherein a first layer of the at least one first catalyst zone impregnation layer comprises about 22 g/ft 3 to about 90 g/ft 3 of palladium and about 115 g/ft 3 to about 690 g/ft 3 of barium.

5. The close-coupled converter system of claim 4 , wherein a first layer of the at least one second catalyst zone impregnation layer comprises 25 g/ft 3 of loaded palladium; about 115 g/ft 3 of loaded barium; about 105 g/ft 3 of loaded cerium; and about 12 g/ft 3 of loaded neodymium.

6. The close-coupled converter system of claim 1 , wherein the first layer of the at least one first catalyst zone impregnation layer further comprises about 105 g/ft 3 of loaded cerium and about 12 g/ft 3 of loaded neodymium.

7. The close-coupled converter system of claim 1 , wherein a second layer of the at least one first catalyst zone impregnation layer includes 0 g/ft 3 to about 147 g/ft 3 of loaded palladium.

8. The close-coupled converter system of claim 7 , wherein a second layer of the at least one first catalyst zone impregnation layer includes 70 g/ft 3 to about 147 g/ft 3 of loaded palladium.

9. The close-coupled converter system of claim 7 , wherein a first layer of the at least one second catalyst zone impregnation layer comprises 25 g/ft 3 of loaded palladium; about 115 g/ft 3 of loaded barium; about 105 g/ft 3 of loaded cerium; and about 12 g/ft 3 of loaded neodymium.

10. The close-coupled converter system of claim 1 , wherein a first layer of the at least one second catalyst zone impregnation layer comprises 25 g/ft 3 of loaded palladium; about 115 g/ft 3 of loaded barium; about 105.8 g/ft 3 of loaded cerium; and about 12 g/ft 3 of loaded neodymium.

11. The close-coupled converter system of claim 1 , wherein the first catalyst zone oxide mixture comprises about 10 wt % niobium oxide and about 20 wt % zirconia.

12. The close-coupled converter system of claim 1 , wherein the first catalyst zone overcoat is loaded with about 3 g/ft 3 to about 3 g/ft 3 rhodium.

13. The close-coupled converter system of claim 1 , wherein the first catalyst zone overcoat is loaded with about 15.1 g/ft 3 to about 24 g/ft 3 rhodium.

14. The close-coupled converter system of claim 1 , wherein the second catalyst zone overcoat is loaded with about 3 g/ft 3 to about 3 g/ft 3 rhodium.

15. The close-coupled converter system of claim 1 , wherein the second catalyst zone overcoat is loaded with about 210 g/ft 3 iron.

16. The close-coupled converter system of claim 1 , wherein the second catalyst zone second oxygen storage material comprises 31 wt % Cerium, about 58 wt % Zirconium-Hafnium, about 5 wt % Neodymium, and about 5 wt % Yttrium Oxide.

17. The close-coupled converter system of claim 1 , wherein the first catalyst zone first oxygen storage material comprises 31 wt % Cerium, about 58 wt % Zirconium-Hafnium, about 5 wt % Neodymium, and about 5 wt % Yttrium Oxide.

18. The close-coupled converter system of claim 1 , wherein the first catalyst zone washcoat comprises about 40 wt % of the first catalyst zone first oxygen storage material and about 60 wt % of the first catalyst zone support oxide and wherein the first catalyst zone support oxide is doped alumina.

19. The close-coupled converter system of claim 1 , wherein, excluding the Rhodium, the first catalyst zone overcoat comprises about 40 wt % of the first catalyst zone second oxygen storage material and about 60 wt % of the catalyst zone oxide mixture.

20. The close-coupled converter system of claim 1 , wherein the second catalyst zone washcoat comprises about 40 wt % of a second catalyst zone first oxygen storage material and about 60 wt % of a doped alumina.

Assignees

• Clean Diesel Tech Inc

Inventors

• Hatfield Randal L
• Nazarpoor Zahra
• Ngo Johnny T
• Lee Edward J
• Golden Stephen J

Classifications

• B01J23/10 Primary

  of rare earths · CPC title

• B01J35/56

  Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional [3D] monoliths · CPC title

• B01J35/0006

  Operations & Transport · mapped topic

• B01D2255/2066

  Praseodymium · CPC title

• B01D53/9454

  characterised by a specific device · CPC title