Polymeric coating mixture, process for application of this coating mixture to a metallic substrate for protection of an edge or an area, covering, substrate coated in this manner and use thereof

Patent metadata

Field	Value
Publication number	US-9598530-B2
Application number	US-86727207-A
Country	US
Kind code	B2
Filing date	Oct 4, 2007
Priority date	Dec 5, 2001
Publication date	Mar 21, 2017
Grant date	Mar 21, 2017

Abstract

The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets or shaped parts.

First claim

The invention claimed is:

1. A composition comprising:
45 wt. % of a urethane acrylate with a molecular weight of 2,000 to 20,000;
7.5 wt. % 1-Hydroxy-cyclo-hexyl phenyl ketone;
29.4 wt. % isobornyl acrylate monofunctional monomer;
10 wt. % phosphoric acid ester;
0.1 wt. % polyether-modified polydimethylsiloxane;
5 wt. % silicate pigment modified with calcium ions; and
3 wt. % hydrophobic silica.

2. The composition of claim 1 , having a viscosity in the range of from 4,500-5,000 mPa·s at room temperature.

3. A coating mixture comprising:
from 20-60% by weight of a radically polymerizable binder containing double bonds, wherein the binder comprises at least one member selected from the group consisting of a urethane acrylate, an epoxyacrylate and a polyester acrylate;
about 6.7% by weight of a corrosion prevention pigment comprising a silicate modified with calcium ions;
about 13.3% by weight of an adhesion promoting phosphoric acid ester;
a photoinitiator; and
water, and

wherein the coating mixture has a pH, has a dry weight and contains a sufficient amount of phosphoric acid ester to pickle a metallic substrate to which it is applied, and wherein the coating mixture has one or more of the following features:
the radically polymerizable binder comprises at least two urethane acrylates, wherein one of the two urethane acrylates has a molecular weight in the range of about 2000 to about 20,000, and/or the other urethane acrylate has a molecular weight in the range of about 100 to about 2,500, and
the photoinitiator comprises two photoinitiator compounds, where one of the two photoinitiator compounds is 1-hydroxy cyclohexyl phenyl ketone, and the other photoinitiator compound is bis(2,6-dimethoxy-benzoyl)-2,4,4-trimethylpentyl-phosphine oxide;
wherein:
the urethane acrylate having a molecular weight in the range of about 2000 to about 20,000 is in an amount of about 39.9% by weight, and the urethane acrylate having a molecular weight in the range of about 100 to about 2,500 is in an amount of about 20% by weight; and
the 1-hydroxy-cyclohexyl phenyl ketone is in an amount of about 6.7% by weight, and the bis(2,6-dimethoxy-benzoyl)-2,4,4-trimethylpentylphosphine oxide is in an amount of about 3.3% by weight.

4. A coated metallic sheet comprising a metallic sheet which comprises at least one of aluminum, steel, an alloy comprising aluminum, iron, magnesium, titanium or zinc and a coating in a cut edge region proximate a cut edge of the metallic sheet formed by applying the coating mixture of claim 3 , wherein the coating mixture is applied in the region of the cut edge of the metallic sheet.

5. A metallic substrate with a largely or completely cured polymeric covering formed from the mixture of claim 3 , wherein the mixture has a water content of 1 to 4.5%.

6. A method for protecting a cut edge of a metallic substrate comprising the steps of:
coating a substrate having said cut edge with the coating mixture of claim 3 , whereby the cut edge is coated with a polymeric covering formed by the coating mixture.

7. The method as in claim 6 wherein the cut edge comprises burrs, and wherein said burrs are covered with a polymeric covering.

8. The coating mixture of claim 3 , further comprising at least one post-crosslinking compound.

9. A coated metallic sheet comprising a metallic sheet which comprises at least one of aluminum, steel, an alloy comprising aluminum, iron, magnesium, titanium or zinc and a coating in a cut edge region proximate a cut edge of the metallic sheet formed by applying the coating mixture of claim 8 , wherein the coating mixture is applied in the region of the cut edge of the metallic sheet.

10. A metallic substrate with a largely or completely cured polymeric covering formed from the mixture of claim 8 , wherein the mixture has a water content of 1 to 4.5%.

11. A method for protecting a cut edge of a metallic substrate comprising the steps of:
coating a substrate having said cut edge with the coating mixture of claim 8 , whereby the cut edge is coated with a polymeric covering formed by the coating mixture.

12. The method as in claim 11 wherein the cut edge comprises burrs, and wherein said burrs are covered with the polymeric covering.

13. A composition comprising:
35 wt. % of a urethane acrylate with a molecular weight of 2,000 to 20,000;
8.5 wt. % of a urethane acrylate with a molecular weight of 100 to 2500;
7.5 wt. % 1-Hydroxy-cyclo-hexyl phenyl ketone;
30.9 wt. % isobornyl acrylate monofunctional monomer;
10 wt. % phosphoric acid ester;
0.1 wt. % polyether-modified polydimethylsiloxane;
5 wt. % silicate pigment modified with calcium ions; and
3 wt. % hydrophobic silica.

Assignees

• Gros Georg
• Maurus Norbert
• Stellnberger Karl-Heinz
• Schinzel Marcus
• Chemetall Gmbh

Inventors

• Gros Georg
• Maurus Norbert
• Stellnberger Karl-Heinz
• Schinzel Marcus

Classifications

• C08G18/792 Primary

  formed by oligomerisation of aliphatic and/or cycloaliphatic isocyanates or isothiocyanates · CPC title

• C08G2150/90

  Compositions for anticorrosive coatings · CPC title

• C08K3/36

  Silica · CPC title

• Y10T428/25

  Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles · CPC title

• C08K5/0025

  Crosslinking or vulcanising agents; including accelerators · CPC title